Nanometer magnesium hydroxide flame retarding silicon rubber composite material and preparation method thereof

A technology of nano-magnesium hydroxide and composite materials, which is applied in the field of flame-retardant silicone rubber composite materials modified by nano-magnesium hydroxide and its preparation, can solve the problems of deteriorating mechanical properties of materials, and achieve easy operation, excellent flame-retardant performance, The effect of simple preparation method

Inactive Publication Date: 2013-03-13
高润宝
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, adding flame retardants is an effective and simple method to improve the flame retardant properties of silicone rubber, but adding fille

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] 100 parts of phenyl silicone rubber; 8 parts of diphenyldimethoxysilane; 10 parts of nano-magnesium hydroxide; 5 parts of fumed silica; 2 parts of cyclotrisilazane; 3 parts of montmorillonite; 0.3 part of chloroform; 3 parts of cetyltrimethylammonium bromide; 1 part of vulcanizing agent.

Embodiment 2

[0020] 120 parts of phenyl silicone rubber; 10 parts of diphenyldimethoxysilane; 20 parts of nano-magnesium hydroxide; 30 parts of fumed silica; 4 parts of cyclotrisilazane; 6 parts of montmorillonite; 0.6 part of chloroform; 6 parts of tributyl phosphate; 1 part of vulcanizing agent.

Embodiment 3

[0022] 110 parts of phenyl silicone rubber; 9 parts of diphenyldimethoxysilane; 15 parts of nano-magnesium hydroxide; 20 parts of fumed silica; 3 parts of cyclotrisilazane; 5 parts of montmorillonite; 0.5 part of chloroform; 3 parts of cetyltrimethylammonium bromide; 3 parts of tributyl phosphate; 1 part of vulcanizing agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tear strengthaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a nanometer magnesium hydroxide flame retarding silicon rubber composite material and a preparation method thereof. The composite material comprises the following components in parts by weight: 100-120 parts of phenyl silicon rubber, 8-10 parts of diphenyldimethoxysilane, 10-20 parts of nanometer magnesium hydroxide, 5-30 parts of fumed silica, 2-4 parts of cyclotrisilazane, 3-6 parts of montmorillonite, 0.3-0.6 part of chloroform, 3-8 parts of surfactant and 1 part of vulcanizing agent. The composite material provided by the invention has excellent flame retarding property and the mechanical property of the composite material is not reduced at the same time; and the preparation method is simple and easy to operate.

Description

technical field [0001] The invention relates to a flame-retardant silicone rubber, in particular to a flame-retardant silicone rubber composite material modified by nano-magnesium hydroxide and a preparation method thereof. Background technique [0002] The oxygen index of silicone rubber is higher than that of rubber with carbon as the main chain. When burning, the heat release rate is low, the flame propagation speed is slow, and there is no dripping. Moreover, pure silicone rubber hardly generates toxic gases when burning, and it will burn on the surface after burning. The formation of a ceramic carbon silicon layer can prevent the exchange of heat and oxygen and the outward diffusion of internal combustibles to contact with heat and oxygen. Due to the special properties of silicone rubber in terms of flame retardancy and high and low temperature resistance, it has been widely used in aerospace, electronic and electrical, power transmission and mechanical parts an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L83/04C08K13/06C08K9/06C08K3/34C08K3/22C08K3/36C08K5/549
Inventor 高润宝
Owner 高润宝
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap