Mesoporous C3N4 photocatalytic material prepared by using molten salt method and application thereof in photocatalysis field

A photocatalytic material, C3N4 technology, applied in the direction of physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve problems such as not easy to promote industrialization, not environmentally friendly, cumbersome process, etc., to achieve easy large-scale The effect of industrialized production and large specific surface area
CN102992282AInactive Publication Date: 2013-03-27NANJING UNIV
2 Cites 44 Cited by

Patent Information

Authority / Receiving Office
CN · China
Patent Type
Applications(China)
Current Assignee / Owner
NANJING UNIV
Publication Date
2013-03-27
Estimated Expiration
Not applicable · inactive patent

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
  • Figure 3
    Figure 3
Patent Text Reader

Abstract

The invention discloses a mesoporous C3N4 photocatalytic material prepared by using a molten salt method and a preparing method thereof. The method comprises the following steps that water-soluble low-melting-point molten salt is fully mixed with melamine, small molten salt drops are used as a blocked layer under the melting temperature of the molten salt, C3N4 grows in a way of being coated with the small drops, and the molten salt is recycled by water washing after reaction, so as to obtain the C3N4 photocatalytic material. The C3N4 photocatalytic material is in a wormlike mesoporous structure, the mesoporous size is within 3.8+ / -1nm, and the forming mechanism of the mesoporous C3N4 photocatalytic material is that the small molten salt drops are used as the growth blocked layer. When the material is prepared, water-soluble low-melting-point chloride salt is used as the molten salt and is fully mixed with melamine to obtain a mixture, the mixture is subjected to the heat treatment in a muffle furnace for 1-5h under the temperature being 400-680 DEG C to obtain samples, and the samples after the heat treatment are washed by water to recycle the molten salt, so as to obtain the mesoporous C3N4 photocatalytic material. In the whole process, a template is not introduced, and the operation is easy and feasible, so that the large-scale industrial production can be realized easily.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention relates to a mesoporous photocatalytic material and its preparation method and application, in particular to a mesoporous C material prepared by using molten salt droplets as a barrier agent. 3 N 4 Methods and applications of photocatalytic materials. Background technique

[0002] In recent years, C 3 N 4 As an emerging important photocatalytic material of organic polymers, it has attracted much attention. It has been experimentally confirmed that C 3 N 4 In the degradation of organic pollutants, water splitting and photocatalytic CO 2 It has a good effect in reduction and has a good application prospect in the field of photocatalysis.

[0003] A large number of experimental facts have proved that mesoporous materials usually have high specific surface area and more reactive sites, so they have better photocatalytic activity. However, currently mesoporous C 3 N 4 The preparation of photocatalytic materials mostly uses mesoporous...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More