Iron-based electrode material with pure copper transition layer and surface pure metal molybdenum or tungsten coating and preparation method for electrode material

An electrode material and transition layer technology, applied in metal material coating process, metal layered products, chemical instruments and methods, etc., can solve the problems of increased power consumption, large power consumption, poor conductivity, etc. Keep constant, power consumption is stable, and the effect of improving specific energy

Inactive Publication Date: 2013-04-10
GUILIN UNIV OF ELECTRONIC TECH
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The initial electrode material is graphite, but it is being phased out because of its low strength, high production cost, easy loss, easy to fall off, and short working life; metal-based electrode materials (such as carbon steel), although they have good strength , plasticity, machinability, and low cost, but it is not corrosion-resistant in use, and consumes a lot of power and has a short life; now stainless steel and metal titanium are commonly used as electrode materials, although they have the advantages of corrosion resistance and high strength, but Oxygen is generated at the anode, and a dense oxide film (such as: TiO 2 Film or Cr 2 o 3 film), the conductivity of this type of oxide film is extremely poor, as time goes on, the thickness of the film increases, the conductivity deteriorates, and the power consumption increases sharply

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The base material of the sample is 4Cr13 martensitic stainless steel, with a size of 50mm×20mm×3mm (length×width×thickness). Up to Ra = 0.8μm.

[0019] First, the surface is brush-plated with pure copper, and the model of the brush-plating power supply is GSD-200A. Connect the polished and cleaned sample to the negative electrode, and the plating pen to the anode, and brush the plating solution, No. 1 activation solution, No. 2 activation solution and alkali copper on the surface of the workpiece respectively. The plating speed is 60 times per minute, and the brush plating time is 60s; the voltage of brush plating No. 1 activation solution is 10V, the brush plating speed is 65 times per minute, and the brush plating time is 60s; the voltage of brush plating No. 2 activation solution is 11V , The brush plating speed is 70 times per minute, and the brush plating time is 70s; the voltage of brush plating alkali copper is 8V, the brush plating speed is 60 times per minute,...

Embodiment 2

[0022] The metal tungsten coating with dense surface can be obtained by arc ion plating pure metal tungsten coating on TSU-650 ultra-high vacuum magnetron sputtering and ion plating deposition equipment, and the rest is the same as that of embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an iron-based electrode material with a pure copper transition layer and a surface pure metal molybdenum or tungsten coating and a preparation method for the electrode material. The preparation method comprises the following steps: coating pure copper with certain thickness on the surface of an iron-based material to serve as a transition layer by electric brush plating or chemical plating and sputter plating technologies; and depositing metal molybdenum or tungsten by a sputter plating technology to form the novel iron-based electrode material with the pure copper transition layer and the surface pure metal molybdenum or tungsten coating. The iron-based material serves as the electrode material, so the electrode material has high processability, high conductivity, high strength and low cost. One layer of copper is plated on the electrode material, so the conductivity is enhanced; and the copper layer serves as the transition layer, so the film substrate bonding strength of the surface pure metal molybdenum (or tungsten) layer is enhanced; and the surface pure metal molybdenum (or tungsten) has the advantages of corrosion resistance, high strength and hardness and low electrical resistivity, so the specific energy and the specific power of the electrode can be greatly increased, the contact resistance maintains constant and the electric energy consumption is stable and low.

Description

technical field [0001] The invention relates to surface engineering, in particular to an electrode material and a preparation method of an iron base, a pure copper transition layer and a pure metal molybdenum (or metal tungsten) coating on the surface. Background technique [0002] In industrial production, the electrode material is used as a positive electrode for electrolysis, and its basic requirements are: good electrical conductivity, electrochemical corrosion resistance, certain mechanical strength and easy processing and manufacturing performance. The initial electrode material is graphite, but it is being phased out because of its low strength, high production cost, easy loss, easy to fall off, and short working life; metal-based electrode materials (such as carbon steel), although they have good strength , plasticity, machinability, and low cost, but it is not corrosion-resistant in use, and consumes a lot of power and has a short life; now stainless steel and metal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B32B15/01C23C28/02C25B11/04
Inventor 高原吴炜钦马志康王成磊张焱徐晋勇蔡航伟陆小会韦文竹张光耀
Owner GUILIN UNIV OF ELECTRONIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap