Acrylate adhesive, protective film tape employing same and preparation method of acrylate adhesive

An acrylate and acrylate-based technology, applied in the field of protective film tape and its preparation, can solve problems such as unfavorable resource protection and environmental protection, failure to realize self-rewinding, violation of environmental protection development requirements, etc., to reduce user processes, Facilitate industrial production and save natural resources

Active Publication Date: 2013-04-17
NINGBO SOKEN CHEM
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be seen that these existing protective film adhesive tapes still have deficiencies: one is that a large amount of release film or release paper will be used, which will directly lead to an increase in the cost of the protective film; the other is that it is not conducive to resource protection and environmental protection. It violates the development requirements of environmental protection; the third is that the silica gel of the release agent will pollute the quilt; the fourth is that it needs to be matured at high temperature for a long time, which can neither realize self-winding from the back, but also consumes a lot of heat energy, and the production cycle is long. Need to occupy a lot of production space, low efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylate adhesive, protective film tape employing same and preparation method of acrylate adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] The acrylic pressure-sensitive adhesive is coated on one side of the base polyester film, as follows:

[0030] 1. Prepare the adhesive mixture, take 100 parts by mass of acrylic ester adhesive SK-1499M (produced by Soken Chemical Co., Ltd.), 3 parts by mass of isocyanate-based hardener HMDI, and 0.1 parts by mass of metal catalyst dilauric acid N-Butyltin, stir well after mixing, take a certain amount for coating, the coating thickness is 10μm, and dry after coating.

[0031] 2. The first section of the oven is set to 70°C for the removal of adhesive solvents, the second section is set to 120°C, and the third section is set to 130°C. These two sections are the curing stage.

[0032] 3. The drying time of the oven is 5min.

[0033] 4. After drying, cool to room temperature, then rewind and slit from the back to prepare protective film tape.

Embodiment 2

[0035] The acrylic pressure-sensitive adhesive is coated on one side of the base polyester film, as follows:

[0036] 1. Prepare the adhesive mixture, take 100 parts by mass of acrylic ester adhesive SK-1499M (Japan Soken Chemical Co., Ltd.), 1 part by mass of isocyanate-based hardener HMDI, and 0.01 parts by mass of metal catalyst tetraacetyl zirconium acetonate , Stir fully after mixing, take a certain amount for coating, the coating thickness is 7μm, and dry after coating.

[0037] 2. The first section of the oven is set to 70°C, which is used to drive the adhesive solvent, the second section is set to 100°C, and the third section is set to 120°C, these two sections are the curing stage.

[0038] 3. The drying time of the oven is 2min.

[0039] 4. After drying, cool to room temperature, then rewind and slit from the back to prepare protective film tape.

Embodiment 3

[0041] The acrylic pressure-sensitive adhesive is coated on one side of the base polyester film, as follows:

[0042] 1. Prepare the adhesive mixture, take 100 parts by mass of acrylic ester adhesive SK-1499M (Japan Soken Chemical Co., Ltd.), 5 parts of isocyanate hardener TDI, and 0.03 parts of metal catalyst dioctyl dineodecanoyl Oxygen tin, fully stir after mixing, take a certain amount for coating, the coating thickness is 10μm, and dry after coating.

[0043] 2. The first section of the oven is set to 80°C for the removal of adhesive solvents, the second section is set to 120°C, and the third section is set to 130°C. These two sections are the curing stage.

[0044] 3. The drying time of the oven is 5min.

[0045] 4. After drying, cool to room temperature, then rewind and slit from the back to prepare protective film tape.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses an acrylate adhesive, a protective film tape employing the acrylate adhesive, and a preparation method of the acrylate adhesive. The acrylate adhesive comprises the following components in parts by weight: 100 parts of acrylate adhesive, 1.0-5.0 parts of isocyanate hardener and 0.01-0.5 part of metal catalyst, wherein the acrylate adhesive is an acrylate polymer, which is a polymer formed by taking a monomer at least containing an acrylate group in a molecule as a main composition monomer; the weight-average molecular weight (a) of the acrylate polymer is 5,000-500,000; the protective film tape comprises a basic material and an adhesive layer coated on one surface of the basic material; and no release layers are formed on the two surfaces of the basic material. The adhesive is high in hardening speed; the tape prepared with the adhesive can be directly wound from the rear surface without being coated with a layer of release film or release paper; the rear surface of the tape does not need to be coated with a release coating, the release film or the release paper; the problem that the conventional protective film needs to use the release film or the release paper is effectively solved; and the adhesive is convenient to use, environment-friendly and simple in production process, lowers the production cost and the resource consumption of the protective film tape, and is convenient for industrial production.

Description

Technical field [0001] The invention relates to the technical field of adhesive materials, in particular to an acrylate adhesive, a protective film tape applied with the adhesive, and a preparation method thereof. Background technique [0002] Protective film tape is currently widely used in the production process of electronic products, especially in FPD, computers, mobile phones and other industries, widely used for process, engineering protection or shipment protection. [0003] At present, the performance requirements of the tape protective film, one of the important ones is: in terms of appearance, it is required that there are no secondary points and impurities in the appearance (the number of secondary points or impurities below 2mm in diameter is within 10 per square, and there is no diameter above 2mm. The secondary points or impurities), and the glue surface has no lack of glue, no bubbles, no glue marks. [0004] At present, the protective film tapes on the market all com...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/04C09J11/06C09J175/04C09J7/02
Inventor 徐苗森柳彬彬金子昌元小林晃司
Owner NINGBO SOKEN CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap