A method for preparing Y-modified CoalNI coating on Ni-based superalloy by adopting embedding infiltration process

A high-temperature alloy and embedding infiltration technology, which is applied in the direction of coating, metal material coating process, solid-state diffusion coating, etc., can solve the problems of reducing the oxidation resistance and thermal corrosion resistance of high-temperature alloys

Inactive Publication Date: 2014-10-15
BEIHANG UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the elements added to improve the high temperature strength of the alloy usually reduce the oxidation resistance and hot corrosion resistance of the superalloy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing Y-modified CoalNI coating on Ni-based superalloy by adopting embedding infiltration process
  • A method for preparing Y-modified CoalNI coating on Ni-based superalloy by adopting embedding infiltration process
  • A method for preparing Y-modified CoalNI coating on Ni-based superalloy by adopting embedding infiltration process

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The present invention relates to a method for preparing a Y-modified CoAlNi coating on a Ni-based superalloy by adopting an embedding and infiltration process. The coating preparation method has the following steps:

[0030] The first step: pretreatment of the substrate

[0031] (A) The surface of the Ni-based superalloy was polished with 800# SiC water abrasive paper to obtain the first sample;

[0032] The surface roughness of the first sample is Ra=1.6;

[0033] (B) After putting the first sample into absolute ethanol for 10-15 minutes of ultrasonic cleaning, the second sample was obtained;

[0034] The second step: preparation of embedding seepage material

[0035] Prepare 100g of embedding material by 6-8g of Al powder with a particle size of 100 mesh, 15-25g of Co powder with a particle size of 100 mesh, and 1-3g of Y with a particle size of 100 mesh 2 o 3 Powder, 3~5g NH with a particle size of 100 mesh 4 Cl powder, 3-5g NH with a particle size of 100 mesh ...

Embodiment 1

[0046] The substrate is Ni-6.2Co-8.9Cr-7.0W-6.1Al-3.8Ta-2.0Mo-1.5Hf-1.0Ti (brand DZ125).

[0047] The first step: pretreatment of the substrate

[0048] (A) The surface of the Ni-based superalloy is polished with 800# SiC water-grinding paper to prepare the first sample;

[0049] The surface roughness of the first sample is Ra=1.6;

[0050] (B) After placing the first sample in absolute ethanol for ultrasonic cleaning for 10 to 15 minutes, the second sample is obtained;

[0051] The second step: making the embedding material

[0052] 100g of embedded infiltration material is prepared from 7.6g of Al powder with a particle size of 100 mesh, 20g of Co powder with a particle size of 100 mesh, and 2g of Y with a particle size of 100 mesh. 2 O 3 Powder, 4g particle size is 100 mesh NH 4 Cl powder, 4g NH with particle size of 100 mesh 4 I powder and balance particle size are 100 mesh Al 2 O 3 powder composition;

[0053] In the present invention, the added Al 2 O 3 The powd...

Embodiment 2

[0067] The matrix is ​​selected from Ni-10Co-9Cr-12W-5Al-1.5Hf-2Ti (brand DZ22).

[0068] The first step: pretreatment of the substrate

[0069] (A) The surface of the Ni-based superalloy is polished with 800# SiC water-grinding paper to prepare the first sample;

[0070] The surface roughness of the first sample is Ra=1.6;

[0071] (B) After placing the first sample in absolute ethanol for ultrasonic cleaning for 10 to 15 minutes, the second sample is obtained;

[0072] The second step: making the embedding material

[0073] 100g of embedded seepage material is prepared from 6g of Al powder with a particle size of 100 mesh, 15g of Co powder with a particle size of 100 mesh, and 3g of Y with a particle size of 100 mesh. 2 O 3 Powder, 5g particle size is 100 mesh NH 4 Cl powder, 5g particle size of 100 mesh NH 4 I powder and balance particle size are 100 mesh Al 2 O 3 powder composition;

[0074] In the present invention, the added Al 2 O 3 The powder does not partic...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a Y modified CoAlNi coating on an Ni-based high temperature alloy by an embedding infiltration process. The thickness of the CoAlNiY coating is between 10 and 30 mu m. The CoAlNiY coating only comprises an Al0.9 Ni1.1 phase, wherein partial Ni atoms are replaced by Co atoms, and Y atoms exist in the Al0.9 Ni1.1 phase in the form of placeholder solid solution. Continuous and dense Al2O3 oxide layers can be formed on the prepared CoAlNiY coating C when the CoAlNiY coating is subjected to high-temperature cycle oxidation at the temperature of 1,050 DEG, so that the coating and a substrate can be prevented from being further oxidized, and the high-temperature cycle oxidation resistance of the substrate is improved. The CoAlNiY coating has higher thermal corrosion resistance at the high temperature of between 850 and 950 DEG C.

Description

technical field [0001] The invention relates to a high-temperature coating, more particularly to a method for preparing a Y-modified CoAlNi coating on a Ni-based superalloy by adopting an embedding infiltration process. Background technique [0002] Nickel-based superalloys usually have high mechanical strength and creep resistance at high temperatures, which makes them widely used in aviation jet engines, various industrial gas turbines and other hot-end components, such as engine blades. However, the elements added to improve the high temperature strength of the alloy usually reduce the oxidation resistance and hot corrosion resistance of the superalloy. An effective measure to solve this problem is to prepare a high-temperature protective coating on the surface of the alloy. Many researchers have done a lot of research, such as aluminizing the surface of the alloy, aluminizing silicon, chromizing silicon, aluminizing hafnium, etc. The research results show that these The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C10/52
Inventor 周春根乔敏李海霞
Owner BEIHANG UNIV