Polyamide composite material with high glowing filament temperature and preparation method and application thereof

A flame retardant polyamide and high glow wire technology, applied in the field of modified polymer new materials, can solve the problems of large specific gravity and low tracking index of halogen-based flame retardant polyamide composite materials, and achieve easy industrial production, specific gravity Light, light color effect

Inactive Publication Date: 2013-06-05
上海耐特复合材料制品有限公司
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to overcome the defects of the existing halogen-based flame-retardant polyamide composite materials, which have a large specificity and a low tracking index compared with them, and provide a high-glow-wire-temperature flame-retardant polyamide composite material, and Its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Source of raw materials:

[0022] PA6 was purchased from Taiwan Jisheng, the model is TP-4208, and the relative viscosity is 2.4.

[0023] EBS was purchased from Jinyi Chemical Technology, model EBA-60.

[0024] 2. Raw material formula:

[0025] PA6 59.1%, Melamine Cyanurate 15%, EBS 0.3%, Antioxidant 1098 0.3%, Antioxidant 168 0.3%, and Talc 25%.

[0026] 3. Preparation method:

[0027] Add melamine cyanurate, EBS and antioxidant into a high-speed mixer and mix evenly, then take out the mixture. Add PA6 from the main feeding port of the twin-screw extruder, add the mixture at the first side feeding port, and then add talc powder at the second side feeding port, so that all materials are mixed evenly in the twin-screw extruder , extruded, cooled, and pelletized to obtain a high glow wire temperature flame-retardant polyamide composite material; the extrusion temperature from the feed section to the machine head is: 210°C, 230°C, 250°C, 250°C, 240°C, 235°C ℃, 230...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
comparative tracking indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyamide composite material with high glowing filament temperature. A raw material formula of the polyamide composite material comprises, by weight, polyamide 40%-70%, halogen-free flame retardant 5%-15%, lubricating agent 0.1%-3%, antioxidant 0.1%-1% and reinforced modifying agent 10%-30%. The halogen-free flame retardant is cyanuric acid melamine. The invention further discloses a preparation method and application of the polyamide composite material with the high glowing filament temperature. The polyamide composite material with the high glowing filament temperature is light in color, light in specific gravity and wide in application range, can be dyed with various colors and has comparative tracking index larger than 500V, and the glowing filament combustion index is 960 DEG C. The polyamide composite material with the high glowing filament temperature can be prepared by means of a conventional device and a conventional method, a manufacture device is not required to be modified, and industrial production is easily performed.

Description

technical field [0001] The invention relates to the field of modified polymer new materials, in particular to a high glow wire temperature flame-retardant polyamide composite material and its preparation method and application. Background technique [0002] Polyamide, commonly known as nylon (PA), is a general term for a class of thermoplastic resins containing repeated amide groups (-NHCO-) ​​in the main molecular chain. Unmodified polyamides have poor flame retardancy and can easily cause fires during use. Therefore, flame retardant modification of polyamide is required in the fields of electronic appliances and other applications. The types of flame retardants that can be used for flame-retardant modification of polyamide mainly include halogen-based, phosphorus-based, nitrogen-based, etc. At present, halogen-based flame-retardant polyamides are the most widely used. The proportion of halogenated flame retardants is large, and halogenated flame retardants usually need t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/02C08K13/04C08K7/14C08K3/34C08K3/26C08K5/3492
Inventor 陈勋森
Owner 上海耐特复合材料制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap