Sealant used for aqueous acrylic acid ester emulsion coating and application method

A technology of acrylate and sealing agent, which is applied in the field of coatings, can solve the problems of reducing the anti-corrosion performance of coatings, and achieve the effects of improving anti-corrosion performance, good interface compatibility, and environmental friendliness

Inactive Publication Date: 2015-01-07
SICHUAN UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the curing process of acrylate resin, micropores will inevitably be formed in the coating, which will become the channel for water, oxygen or other chemical substances to corrode the substrate, reduce the anti-corrosion performance of the coating, and limit the water-based acrylate emulsion coating. Application in some industries or products that require high coating anti-corrosion performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] The formula of the water-based sealing agent is (component is mass):

[0013] Diethylene glycol: 20

[0014] Triethylene glycol: 100

[0015] span-20:2

[0016] tx-10;6

[0017] Water: 500

[0018] The specific operation is: according to the above formula, mix the raw materials evenly to obtain the water-based sealing agent;

[0019] The method of using the water-based sealing agent is: use the spraying method to evenly coat the water-based sealing agent on the surface of the acrylate wet film, and then perform curing treatment at 100°C for 2 hours to obtain a good sealing effect. Acrylic coating.

Embodiment 2

[0021] The formula of the water-based sealing agent is (component is mass):

[0022] Triethylene glycol: 150

[0023] span-20:2

[0024] tx-10;6

[0025] Water: 500

[0026] The specific operation is: according to the above formula, mix the raw materials evenly to obtain the water-based sealing agent;

[0027] The method of using the water-based sealing agent is as follows: apply the water-based sealing agent evenly on the surface of the acrylate wet film by dip coating, and then cure it at 120°C for 2 hours to obtain the sealing effect. Good acrylic coating.

Embodiment 3

[0029] The formula of the water-based sealing agent is (component is mass):

[0030] Diethylene glycol: 20

[0031] Triethylene glycol: 100

[0032] tx-10;6

[0033] Water: 400

[0034] The specific operation is: according to the above formula, mix the raw materials evenly to obtain the water-based sealing agent;

[0035] The method of using the water-based sealing agent is: use the spraying method to evenly coat the water-based sealing agent on the surface of the acrylate wet film, and then perform curing treatment for 4 hours at a temperature of 80°C to obtain a good sealing effect. Acrylic coating.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a sealant used for aqueous acrylic acid ester emulsion coating and an application method, the sealant is used for sealing the micropore of an acrylic acid ester film, and the anticorrosion performance of the coating can be enhanced. The aqueous sealant comprises an organic active component, a surfactant and water, the mass ratio of organic active component to surfactant to water is (10-40): (1-3): 100. The organic active component is diglycol (diglycol) or triglycol (triethylene glycol) or a mixture, and the surfactant is polyol ester or polyether or a mixture. A usage method is characterized in that the sealant is prepared by the above ratio, a spraying method or a dipping method is employed for uniformly coating the sealant on an acrylic acid ester moisture membrane surface, and fully filtered in a film aperture. The treated film is solidified for 1-5 hours at the temperature of 80-150 DEG C to obtain the acrylic acid ester coating with good sealing effect.

Description

technical field [0001] The invention belongs to the field of coatings, and relates to a water-based sealing agent, in particular to a sealing agent for water-based acrylate emulsion coatings and an application method thereof. Background technique [0002] Water-based acrylic emulsion coating refers to a type of water-based coating that uses acrylate resin as a film-forming substance. It has the outstanding advantages of high environmental protection, weather resistance, corrosion resistance, gloss retention, color retention, and convenient construction. It is widely used in construction, furniture, and home appliances. , automotive industry, etc. have a wide range of applications. However, during the curing process of acrylate resin, micropores will inevitably be formed in the coating, which will become the channel for water, oxygen or other chemical substances to corrode the substrate, reduce the anti-corrosion performance of the coating, and limit the water-based acrylate ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C25D11/00C09D5/08C09D133/04
Inventor 廖立谢克难黎明
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap