Method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate

A technology for carbon-coated lithium iron phosphate and lithium iron phosphate is applied in the field of preparation of lithium iron phosphate and basic lithium iron phosphate to prepare carbon-coated lithium iron phosphate, which can solve problems such as undisclosed specific methods and achieve stable product performance. , The process is simple and the controllability is good.

Inactive Publication Date: 2013-08-28
HANGZHOU DIANZI UNIV
View PDF7 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the patent "A Preparation Method of Basic Lithium Iron Phosphate" (ZL200710156063.6), LiFePO is mentioned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate
  • Method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate
  • Method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0058] Example 1

[0059] 1mol iron phosphate FePO 4 , 1mol lithium hydroxide LiOH and 4L deionized water were put into a ball mill and ball milled for 1 hour to obtain a mixture; then the mixture was added to the reaction kettle and reacted at 120°C for 32 hours, filtered and dried to obtain the chemical formula LiFePO 4 (OH) basic lithium iron phosphate.

Example Embodiment

[0060] Example 2

[0061] 1mol iron phosphate FePO 4 , 1.02mol lithium hydroxide LiOH and 4.5L deionized water were put into a ball mill and ball milled for 2 hours to obtain a mixture; then the mixture was added to the reaction kettle, reacted at 200°C for 20 hours, filtered and dried to obtain the chemical formula: LiFePO 4 (OH) basic lithium iron phosphate.

Example Embodiment

[0062] Example 3

[0063] 1mol iron phosphate FePO 4 , 1.05mol lithium hydroxide LiOH and 5L deionized water were put into a ball mill and ball milled for 3 hours to obtain a mixture; then the mixture was added to the reaction kettle, reacted at 250°C for 6 hours, filtered and dried to obtain the chemical formula LiFePO 4 (OH) basic lithium iron phosphate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate. In conventional preparation processes for lithium iron phosphate, P, Fe and Li are originated from different raw materials, and in the process of mixing, inadequate batch mixing easily happens, which results in incomplete generation of lithium iron phosphate. The method provided by the invention comprises the following steps: mixing basic lithium iron phosphate, a carbon source and a catalyst and then carrying out sintering so as to obtain the carbon-coated lithium iron phosphate, wherein a mass ratio of the carbon source to basic lithium iron phosphate is 4-8: 100, and a mol ratio of metal ions in the catalyst to iron ions in basic lithium iron phosphate LiFePO4(OH) is 1-3: 100. According to the invention, P, Fe and Li are originated from the same raw material basic lithium iron phosphate, so the problem in homogeneity of batch mixing is overcome; the carbon source is decomposed at a high temperature to produce a gaseous organic matter which can reduce positive trivalent Fe in basic lithium iron phosphate into positive bivalent Fe and enables carbon to be deposited on the surface of lithium iron phosphate to form coating carbon. The method provided by the invention has the advantages of simple process, good controllability and stable product performance.

Description

technical field [0001] The invention belongs to the technical field of chemical industry and relates to a preparation method of lithium iron phosphate, in particular to a method for preparing carbon-coated lithium iron phosphate from basic lithium iron phosphate. Background technique [0002] Lithium-ion battery is a battery system widely used in contemporary times, which has the advantages of light weight, long life and no pollution. Lithium iron phosphate can be used as a cathode material for lithium-ion batteries. Batteries using lithium iron phosphate as the positive material are generally called lithium iron phosphate batteries. Compared with other types of lithium-ion batteries, lithium iron phosphate batteries have the characteristics of high safety, long life, and rich sources of raw materials, and are suitable for power batteries. Lithium iron phosphate batteries are widely used in electric vehicles in my country. [0003] In the existing technical solutions, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01B25/45C01B31/02H01M4/58C01B32/05
CPCY02E60/10
Inventor 倪华良赵淑敏席俊华季振国
Owner HANGZHOU DIANZI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap