Production method of homogeneous carbonized wood using masson pine wood as raw material

A technology of homogeneous carbonized wood and production methods, which is applied in wood treatment, wood processing equipment, wood treatment details, etc., can solve the problems of insufficient economic value, less application, damage to precious tree species or wild wood, etc., to improve the application Value, economic benefits, and the effect of expanding the application field

Inactive Publication Date: 2016-02-17
重庆家和琴森木业有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although deep carbonized wood can achieve anti-corrosion and moisture-proof effects, its internal and external colors are different, which seriously affects the quality of further processed products. Therefore, the applicant's research team has summarized a set of homogeneous carbonized wood after long-term research and practice. Advanced processing and production methods, not only anti-corrosion and moisture-proof, but also beautiful, uniform and durable
[0006] At present, the main species of carbonized wood are Pinus sylvestris sylvestris, hemlock, oak, etc. At present, there is no use of masson pine raw materials, mainly because the resin pipe diameter of masson pine is developed, the content of turpentine is high, and the wood deformation is large. When it is dry, it warps seriously, and it is not resistant to corrosion. When the temperature is high, it even overflows and pollutes the surface of the material, resulting in poor paint and bonding performance. Therefore, it is less used in furniture. At present, it is mainly used for building templates, mine pillars, boards, and packaging. Boxes, matchsticks, plywood, etc., or as raw materials for man-made fiberboards; however, masson pine, as a fast-growing economic forest, is widely planted in most mountainous areas of my country, and its due economic value is not sufficient due to its limitations in application fields. Play; indirectly cause damage to other precious tree species or wild wood

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Production method of homogeneous carbonized wood using masson pine wood as raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Cut and saw 10m3 masson pine wood into a wood with a length of 100cm and a thickness of 2cm; then immerse in a 20% lime solution and boil continuously for 5 hours, then put it into clean water and rinse it, and then immerse in a concentration of 1‰ hydrogen peroxide solution Boil continuously for 5 hours, then rinse in clean water; then adjust the temperature in the conventional steam drying kiln to 72°C, and spray water vapor into the conventional steam drying kiln to make it saturated, and then degrease the masson pine Put the wood in a conventional steam drying kiln to fully absorb water. After 25 hours, the masson pine wood absorbs water to reach saturation, then stop spraying water vapor, adjust the temperature in the conventional steam drying kiln to 65°C, and keep the kiln for 12 hours, then open the vent hole to Exhaust outside, and gradually increase the temperature in the conventional steam drying kiln to 82°C, and dehydrate for 3 hours; repeat this twice, then...

Embodiment 2

[0031] Cut and saw 10m3 early wood of masson pine wood into a wood with a length of 200cm and a thickness of 5cm; then immerse in a 20% lime solution and boil continuously for 5 hours, then put it into clean water and rinse it, and then immerse in a concentration of 1‰ Boil continuously in hydrogen peroxide solution for 5 hours, then rinse in clean water; then adjust the temperature in the conventional steam drying kiln to 72°C, and spray water vapor into the conventional steam drying kiln to make it saturated, and then degrease the Put the masson pine wood into the conventional steam drying kiln to fully absorb water. After 25 hours, the masson pine wood absorbs water to reach saturation, then stop spraying water vapor, adjust the temperature in the conventional steam drying kiln to 65°C, and keep the kiln for 12 hours, then turn on the exhaust The hole is exhausted outward, and the temperature in the conventional steam drying kiln is gradually raised to 82°C, and the dehydrat...

Embodiment 3

[0034] Cut and saw 10m3 early wood of masson pine wood into a wood with a length of 200cm and a thickness of 5cm; then immerse in a 20% lime solution and boil continuously for 5 hours, then put it into clean water and rinse it, and then immerse in a concentration of 1‰ Boil continuously in hydrogen peroxide solution for 5 hours, then rinse in clean water; then adjust the temperature in the conventional steam drying kiln to 73°C, and spray water vapor into the conventional steam drying kiln to make it saturated, and then degrease the Put the masson pine wood in a conventional steam drying kiln to fully absorb water. After 26 hours, the masson pine wood absorbs water to a saturated state, then stop spraying water vapor, adjust the temperature in the conventional steam drying kiln at 66°C, and keep the kiln for 12.5 hours, then turn on the exhaust The hole is exhausted outward, and the temperature in the conventional steam drying kiln is gradually raised to 83°C, and the dehydrati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The production method of homogeneous carbonized wood using masson pine wood as raw material belongs to the field of forestry product processing technology, and is completed by degreasing and carbonization. Excessive carbonization of the outer layer at high temperature due to excessive grease overflow causes uneven carbonization inside and outside, laying a solid foundation for achieving homogeneous carbonization; different heating and cooling methods are adopted according to different materials and color targets of masson pine raw materials Speed, carbonization temperature and carbonization time, so that the masson pine wood can be carbonized to the same degree from the outside to the inside, so that the hygroscopicity, dimensional stability, mechanical properties, corrosion resistance, hardness and compression resistance of each part, The properties of gluing and surface finishing, especially the color, all show the same good characteristics and achieve a true homogeneous carbonization effect, which greatly expands the application field of masson pine wood and improves the application value and economic benefits.

Description

technical field [0001] The invention belongs to the technical field of forestry product processing, in particular to a production method of homogeneous carbonized wood using masson pine wood as a raw material. Background technique [0002] Carbonized wood is to carbonize wood under high temperature without any chemical agent, so that its nutrients are destroyed, so it has better anti-corrosion and insect-proof functions. Because its water-absorbing functional group hemicellulose is reorganized, the product has better physical properties. [0003] Carbonized wood is a real green and environmentally friendly product. Although the product has anti-corrosion and insect-proof properties, it does not contain any harmful substances. Animals and the environment have any negative impact; the surface of the charred wood has a dark brown aesthetic effect, and has the effect of anti-corrosion and anti-biological attack. It has low moisture content, is not easy to absorb water, stable m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B27M1/06B27K5/00
Inventor 杨琴
Owner 重庆家和琴森木业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products