Heat-proof magnetic conveyor belt cover rubber and preparation method thereof

A technology for covering rubber and conveyor belts, applied in the field of conveyor belts, can solve the problems of easy slippage, disadvantage, and shortened service life of parts, and achieve the effect of reducing the rate of thermal aging damage, improving work efficiency, and improving service life.

Active Publication Date: 2013-09-18
江苏凯嘉橡胶科技股份有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the heat-resistant conveyor belt used to transport high-temperature parts on the iron and steel smelting and casting production line in China has poor heat resistance and short service life, and when the conveyor belt is transferring high-temperature parts, the parts are prone to slip on the conveyor belt. Messy and disorderly, it is easy to cause the danger of scalding, which is not conducive to the production of the next process
The main reason is that during use, the heat of the high-temperature material is easily and quickly transferred to the inside of the belt, which causes the cover rubber of the belt to age and crack, and the rubber layer and the core layer of the belt are separated, resulting in a shortened service life of the belt.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] Prescription ratio is by weight, and the ratio of used material is:

[0019] 100 parts of EPDM rubber, 2 parts of anti-aging agent, 6 parts of zinc oxide, 2 parts of magnesium oxide, 1 part of stearic acid, 40 parts of carbon black, 4 parts of dicumyl peroxide, 35 parts of asbestos fiber, 200 parts of magnetic powder parts, 10 parts of paraffin oil.

[0020] The preparation method of the cover glue on the heat-resistant magnetic conveyor belt, the specific steps are as follows:

[0021] (1) Add 100 parts of EPDM rubber into the internal mixer for pre-compression mixing for 50 seconds, then add 2 parts of anti-aging agent RD, 6 parts of zinc oxide, 2 parts of magnesium oxide, and 1 part of stearic acid, and mix for 50 seconds. second, then add 45 parts of carbon black, 35 parts of asbestos fiber, 200 parts of magnetic powder, and 10 parts of paraffin oil, and carry out mixing for 60 seconds. When the temperature of the mixed material reaches 125 ° C, the glue is dischar...

Embodiment 2

[0025] Prescription ratio is by weight, and the ratio of used material is:

[0026] 100 parts of EPDM rubber, 3 parts of anti-aging agent RD, 7 parts of zinc oxide, 3 parts of magnesium oxide, 2 parts of stearic acid, 40 parts of carbon black, 4.5 parts of dicumyl peroxide, 30 parts of asbestos fiber, 180 parts of magnetic powder parts, 8 parts of paraffin oil.

[0027] The preparation method of the cover glue on the heat-resistant magnetic conveyor belt, the specific steps are as follows:

[0028] (1) Add 100 parts of EPDM rubber into the internal mixer for pre-compression mixing for 45 seconds, then add 3 parts of anti-aging agent RD, 7 parts of zinc oxide, 3 parts of magnesium oxide, and 2 parts of stearic acid, and mix for 70 second, then add 40 parts of carbon black, 30 parts of asbestos fiber, 180 parts of magnetic powder, and 8 parts of paraffin oil, and mix for 30 seconds. When the temperature of the mixed material reaches 130 ° C, the glue is discharged to obtain a m...

Embodiment 3

[0032] Prescription ratio is by weight, and the ratio of used material is:

[0033] 100 parts of EPDM rubber, 3 parts of anti-aging agent RD, 5 parts of zinc oxide, 8 parts of magnesium oxide, 2 parts of stearic acid, 50 parts of carbon black, 5 parts of dicumyl peroxide, 50 parts of asbestos fiber, 250 parts of magnetic powder parts, 15 parts of paraffin oil.

[0034] The preparation method of the cover glue on the heat-resistant magnetic conveyor belt, the specific steps are as follows:

[0035] (1) Add 100 parts of EPDM rubber into the internal mixer for pre-compression mixing for 60 seconds, then add 1 part of accelerator, 3 parts of anti-aging agent RD, 5 parts of zinc oxide, 8 parts of magnesium oxide, and 2 parts of stearic acid , mixed for 30 seconds, then added 50 parts of carbon black, 50 parts of asbestos fiber, 250 parts of magnetic powder, and 15 parts of paraffin oil, and mixed for 70 seconds. rubber compound.

[0036] (2) Cool the mixed rubber in step (1) for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention provides heat-proof magnetic conveyor belt cover rubber. The cover rubber comprises the following components in parts by weight: 100 parts of ethylene propylene diene monomer rubber, 2-5 parts of anti-aging agent, 5-10 parts of zinc oxide, 2-8 parts of magnesium oxide, 1-3 parts of stearic acid, 25-50 parts of carbon black, 4-6 parts of dicumyl peroxide, 30-50 parts of asbestos fiber, 150-300 parts of magnetic powder, and 5-20 parts of paraffin oil. In addition, the invention further provides a preparation method of the heat-proof magnetic conveyor belt cover rubber. The heat-proof magnetic conveyor belt cover rubber meets the heat-proof property of high-temperature parts conveyed on an iron making and steel making production line, the heated aging damage rate of the conveyor belt can be reduced, and the service life of the conveyor belt can be prolonged; furthermore, metal parts falling on the conveyor belt can be effectively adsorbed, the slippage of the metal parts can be prevented, unnecessary damage can be reduced, the production of next procedure can be favorably carried out, and the working efficiency can be improved.

Description

technical field [0001] The invention relates to the field of conveyor belts, in particular to a covering glue on a heat-resistant magnetic conveyor belt and a preparation method thereof. Background technique [0002] At present, the heat-resistant conveyor belt used to transport high-temperature parts on the iron and steel smelting and casting production line in China has poor heat resistance and short service life, and when the conveyor belt is transferring high-temperature parts, the parts are prone to slip on the conveyor belt. Messy and disorderly, it is easy to cause the danger of scalding, which is not conducive to the production of the next process. The main reason is that during use, the heat of the high-temperature material is easily and quickly transferred to the inside of the belt, which causes the cover rubber of the belt to age and crack, and the rubber layer and the core layer of the belt are separated, resulting in a shortened service life of the belt. [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08K13/04C08K3/22C08K5/09C08K3/04C08K5/14C08K7/12C08K3/00B65G15/32B29B7/00B29B7/52
Inventor 沈王平沈玉海何承霞顾宇飞夏茂华
Owner 江苏凯嘉橡胶科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com