Granulation tower insulating oil

A technology of thermal insulation oil and prilling tower, which is applied in the direction of heat exchange materials, chemical instruments and methods, can solve the problems of easy production accidents, low safety level, unstable chemical properties of thermal insulation oil, etc., and achieves good thermal insulation effect. Effect

Inactive Publication Date: 2013-09-25
JIANGSU HAIAN PETROCHEM PLANT
View PDF1 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Thermal insulation oil is widely used in chemical companies. Many chemical products need to be stored under certain temperature conditions after production. However, many thermal insulation oils are not safe due to their unstable chemical properties, which may easily cause production accidents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0008] A granulation tower insulation oil, which is prepared by mixing dimethyl acetic acid, polyethylene oxide, octadecyl tetrahydroxyglyceride, polyacrylamide, glycerin, tallow alkyl propanolamine and cationic water. Wherein the parts by weight of each component are: dimethyl acetic acid: 10 parts; polyethylene oxide: 10 parts; octadecyl tetrahydroxyglyceride: 10 parts; polyacrylamide: 0.8 parts; glycerin: 10 parts; tallow Alkyl propanolamine: 0.5 parts; cationic water: 30 parts.

[0009] The preparation method of the above slimming warm-up oil: firstly mix 10 parts of dimethyl acetic acid, 10 parts of polyethylene oxide and 10 parts of stearyl tetrahydroxyglyceride and heat it to 55°C, then add 0.8 parts of polyacrylamide, glycerin 10 parts, 0.5 parts of tallow alkyl propanolamine, wait until it is completely mixed evenly, let it condense, after the condensation is completed, add 30 parts of cationic water and stir evenly.

Embodiment 2

[0011] A granulation tower insulation oil, which is prepared by mixing dimethyl acetic acid, polyethylene oxide, octadecyl tetrahydroxyglyceride, polyacrylamide, glycerin, tallow alkyl propanolamine and cationic water. Wherein the parts by weight of each component are: dimethyl acetic acid: 20 parts; polyethylene oxide: 20 parts; octadecyl tetrahydroxyglyceride: 20 parts; polyacrylamide: 1 part; glycerin: 15 parts; tallow Alkyl propanolamine: 1.5 parts; cationic water: 40 parts.

[0012] The preparation method of the above slimming warm-up oil: firstly mix 20 parts of dimethyl acetic acid, 20 parts of polyethylene oxide and 20 parts of stearyl tetrahydroxyglyceride and heat to 55°C, then add 1 part of polyacrylamide, glycerin 15 parts, 1.5 parts of tallow alkyl propanolamine, wait until it is completely mixed evenly, let it condense, after the condensation is completed, add 40 parts of cationic water and stir evenly.

Embodiment 3

[0014] A granulation tower insulation oil, which is prepared by mixing dimethyl acetic acid, polyethylene oxide, octadecyl tetrahydroxyglyceride, polyacrylamide, glycerin, tallow alkyl propanolamine and cationic water. Wherein the parts by weight of each component are: dimethyl acetic acid: 15 parts; polyethylene oxide: 15 parts; octadecyl tetrahydroxyglyceride: 15 parts; polyacrylamide: 0.9 parts; glycerin: 12.5 parts; tallow Alkyl propanolamine: 1 part; cationic water: 35 parts.

[0015] The preparation method of the above slimming warm-up oil: firstly mix 15 parts of dimethyl acetic acid, 15 parts of polyethylene oxide and 15 parts of stearyl tetrahydroxyglyceride and heat it to 55°C, then add 0.9 parts of polyacrylamide, glycerin 12.5 parts, 1 part of tallow alkyl propanolamine, wait until it is completely mixed evenly, let it condense, after the condensation is completed, add 35 parts of cationic water and stir evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses granulation tower insulating oil which is prepared by mixing the following components in parts by weight: 10-20 parts of dimethyl acetic acid, 10-20 parts of polyoxyethylene, 10-20 parts of octadecyl tetrahydroxy glyceride, 0.8-1 part of polyacrylamide, 10-15 parts of glycerol, 0.5-1.5 parts of alkyl butter propanolamine and 30-40 parts of cationic water. The granulation tower insulating oil is safe and non-flammable and has a good heat insulation effect.

Description

technical field [0001] The invention relates to a chemical product, in particular to a granulation tower insulation oil. Background technique [0002] Thermal insulation oil is widely used in chemical companies. Many chemical products need to be stored at a certain temperature after production. However, many thermal insulation oils are not safe due to their unstable chemical properties, which may easily cause production accidents. Contents of the invention [0003] Purpose of the invention: In order to solve the deficiencies of the prior art, the present invention provides a prilling tower insulation oil. [0004] Technical solution: A granulated tower insulation oil, which is prepared by mixing dimethyl acetic acid, polyethylene oxide, octadecyl tetrahydroxyglyceride, polyacrylamide, glycerin, tallow alkyl propanolamine and cationic water Formed, the parts by weight of each component are: dimethyl acetic acid: 10-20 parts; polyethylene oxide: 10-20 parts; octadecyl tetra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/10
Inventor 王加国
Owner JIANGSU HAIAN PETROCHEM PLANT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap