Colorful heat insulation coating mortar as well as manufacturing method and application thereof

A technology of heat insulation and manufacturing methods, which is applied to building construction, covering/lining, construction, etc., can solve the problems of long cycle time, increased construction cost, on-site material loss, etc., and achieve the goal of overcoming construction troubles and reducing overall labor costs Effect

Active Publication Date: 2014-11-05
南通苏宝建筑节能科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The construction period is long, and it will virtually increase the construction cost and the loss of on-site materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colorful heat insulation coating mortar as well as manufacturing method and application thereof
  • Colorful heat insulation coating mortar as well as manufacturing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1) Preparation of colored aggregates: Mix 13.5 parts by weight of pure acrylic emulsion, 1.0 parts of thickener, and 1.5 parts of plasticizer and stir for 4 minutes until uniform, then it will become a colored aggregate and set aside;

[0018] 2) Surface coating treatment of floating beads and micro-beads: use weather-resistant pigment epoxy-modified silicone resin coating, put 2.5 parts by weight of floating beads and 2.5 parts of ceramic micro-beads on a stainless steel with a diameter of 50 cm Fully stir in the container. After about 3 minutes, the speed of the mixer is 10 rpm, and then pour it into a container with an electric sieve on the top to keep the epoxy-modified silicone resin coating. The electric sieve continues to work to prevent the paint from agglomerating. , and then dried by an air-drying instrument at room temperature, so that the surface is colored, that is, modified colored microbeads;

[0019] 3) Take 6.5 parts by weight of the modified colored be...

Embodiment 2

[0026] 1) Preparation of colored aggregates: Mix 15.1 parts by weight of pure acrylic emulsion, 1.4 parts of thickener, and 2 parts of plasticizer and stir for 8 minutes until uniform, then it will become a colored aggregate and set aside;

[0027] 2) Surface coating treatment of floating beads and micro-beads: use epoxy-modified silicone resin coating with weather-resistant pigments, put 3 parts by weight of floating beads and 3.5 parts of ceramic micro-beads on a stainless steel surface with a diameter of 50 cm Fully stir in the container. After about 5 minutes, the speed of the mixer is 20 rpm, and then pour it into a container with an electric sieve on the top to keep the epoxy-modified silicone resin coating. The electric sieve continues to work to prevent the paint from agglomerating. , and then dried by an air-drying instrument at room temperature, so that the surface is colored, that is, modified colored microbeads;

[0028] 3) Take 7.5 parts by weight of the modified ...

Embodiment 3

[0033] 1) Preparation of colored aggregates: Mix 14 parts by weight of pure acrylic emulsion, 1.2 parts of thickener, and 1.8 parts of plasticizer and stir for 6 minutes until uniform, then it will become a colored aggregate and set aside;

[0034] 2) Surface coating treatment of floating beads and micro-beads: use weather-resistant pigment epoxy-modified silicone resin coating, put 2.8 parts by weight of floating beads and 3 parts of ceramic micro-beads on a stainless steel surface with a diameter of 50 cm Fully stir in the container. After about 4 minutes, the speed of the mixer is 15 rpm, and then pour it into a container with an electric sieve on the top to keep the epoxy-modified silicone resin coating. The electric sieve continues to work to prevent the paint from agglomerating. , and then dried by an air-drying instrument at room temperature, so that the surface is colored, that is, modified colored microbeads;

[0035] 3) Take 7 parts by weight of the modified colored ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses colorful heat insulation coating mortar as well as a manufacturing method and application thereof. The manufacturing method comprises the following steps of: 1) preparing color aggregate; (2) performing surface coating treatment on floating beads and micro-beads; and 3) mixing. The colorful heat insulation coating mortar disclosed by the invention is manufactured by combining a heat reflection principle with heat insulation and energy saving technologies including thermal obstruction and the like, and compared with the prior art, the defects of construction cost and material wastes and the like caused by long construction period during construction of an existing heat insulation system are overcome, and the effects of energy conservation, low carbon and environmental protection are really achieved.

Description

technical field [0001] The invention relates to a method for manufacturing a paint for building exterior walls, in particular to a heat-insulating paint for exterior walls with thermal insulation properties and various colors, a manufacturing method and its application. Background technique [0002] At present, the external wall insulation system widely used in industrial and civil buildings is composed of insulation layer, interface layer, anti-crack (plastering) layer and finishing layer. Generally, alkali-resistant mesh cloth is pressed and pasted on the insulation layer before anti-cracking (plastering layer). The anti-cracking layer needs to be cured for at least 7 days and nights. If the weather is good and the average daily temperature is around 20°, after 3 days of curing , The strength of the mortar can reach 50%, and the strength of the mortar can reach 80% after 7 days. After waiting for the maintenance, the finishing layer putty and paint or pasting bricks and ot...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline