Preparation method of calcium boride

A technology of calcium boride and calcium oxide, which is applied in the field of metallurgy, can solve the problems of large carbon dioxide emissions and high impurity content, and achieve the effects of low emissions, high product purity, and low environmental pollution

Inactive Publication Date: 2013-12-18
SUZHOU KEYU ELECTRONICS TECH SERVICE
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Calcium boride is an additive in metal smelting. At present, there are few domestic manufacturers. Most of the raw materials are boron gangue, petroleum coke and calcium carbonate, and they are prepared by high-temperature sintering. also higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A kind of preparation method of calcium boride provided by the invention, the method comprises the following steps:

[0013] A, 84g powdery boron carbide and 56g calcium oxide are uniformly mixed;

[0014] B. The mixture was sintered in air at a temperature of 1700° C. for 2 hours to obtain 106 g of calcium boride particles.

Embodiment 2

[0016] A kind of preparation method of calcium boride provided by the invention, the method comprises the following steps:

[0017] A, 84g powdery boron carbide and 56g calcium oxide are uniformly mixed;

[0018] B. The mixture was sintered in air at a temperature of 1800° C. for 1 hour to obtain 106 g of calcium boride particles.

[0019] The calcium boride preparation method disclosed by the invention has the advantages of low carbon dioxide emission in the production process, little environmental pollution, high purity of the produced product and few impurities. At the same time, the method is simple to operate and utilizes large-scale production of enterprises.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of calcium boride, the preparation method comprises the following steps: A, mixing powdery boron carbide and calcium oxide according to a molar ratio of 3:2; B, sintering a mixture of step A in air at 1700-1800 DEG C for 1-2 hours to obtain the calcium boride. In the production process of the preparation method, the carbon dioxide emission load is low, the pollution to the environment is less, and a produced product is high in purity and few in impurity.

Description

technical field [0001] The invention belongs to the technical field of metallurgy, in particular to a preparation method of calcium boride. Background technique [0002] Calcium boride is an additive in metal smelting. At present, there are few domestic manufacturers. The raw materials are mostly boron gangue, petroleum coke and calcium carbonate, which are prepared by high-temperature sintering. Also higher. Contents of the invention [0003] In order to solve the problems in the above-mentioned background technology, the object of the present invention is to provide a method for preparing calcium boride with low carbon dioxide emissions and high product purity. [0004] In order to achieve the above object, the technical scheme adopted in the present invention is: [0005] 1, a preparation method of calcium boride, is characterized in that, the method comprises the following steps: [0006] A, powdery boron carbide and calcium oxide are mixed according to the molar ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B35/04
Inventor 不公告发明人
Owner SUZHOU KEYU ELECTRONICS TECH SERVICE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com