Highly wear resistant rubber and preparation method thereof

A rubber and natural rubber technology, applied in the rubber field of shoes, can solve the problems of poor flexibility, heavy soles, poor wear resistance, etc.

Inactive Publication Date: 2013-12-18
XTEPCHINA
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous improvement of people's living standards and sports competition, light and comfortable shoes have become the mainstream. The density of ordinary shoe-making rubber is 1.2G / CM3, and the wear resistance is 110mm3. The sole is relatively heavy, poor wear resistance, and less soft. good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention is described in detail below in conjunction with embodiment:

[0017] High wear-resistant rubber, characterized in that: the rubber is composed of the following parts by mass: 40-50 parts of natural rubber; 55-62 parts of butadiene rubber; 8-12 parts of styrene-butadiene rubber; 28-50 parts of white carbon black 32 parts; 5 parts of processing oil; 5 parts of anti-wear agent; 5 parts of zinc oxide powder; 3 parts of H550 active agent; 2 parts of PEG active agent; 2 parts of H600 thickener, 2.5 parts of H606 antioxidant; ; 2.5 parts of HA2 accelerator; 0.15 parts of TS / 80 accelerator; 2.5 parts of S80 sulfur.

[0018] Specifically, the rubber is composed of the following parts by mass: 45 parts of natural rubber; 60 parts of butadiene rubber; 10 parts of styrene-butadiene rubber; 30 parts of white carbon black; 5 parts of processing oil; 5 parts of anti-slip agent; 5 parts of zinc oxide powder; 3 parts of H550 active agent; 2 parts of PEG active ag...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

Highly wear resistant rubber comprises, by mass, 40-50 parts of natural rubber, 55-62 parts of butadiene rubber, 8-12 parts of styrene butadiene rubber, 28-32 parts of white carbon black, 5 parts of processing oil, 5 parts of a wear resistance agent, 5 parts of zinc oxide powder, 3 parts of an H550 activator, 2 parts of a PEG activator, 2 parts of an H600 tackifier, 2.5 parts of an H606 antioxidant, 0.5 parts of stearic acid, 2.5 parts of an HA2 accelerant, 0.15 parts of a TS / 80 accelerant, and 2.5 parts of S80 sulfur. The highly wear resistant rubber comprises a plurality of high-molecular polymers and chemical engineering raw materials according to a certain ratio, and is prepared through banburying, roller and flat platform vulcanization and the like. The highly wear resistant rubber has the advantages of light weight, good elasticity, good flexibility and the like when the highly wear resistant rubber is used on sports soles.

Description

Technical field: [0001] The invention relates to a shoe rubber, in particular to a high wear-resistant rubber used in sports shoe soles and a manufacturing method thereof. Background technique: [0002] With the continuous improvement of people's living standards and sports competition, light and comfortable shoes have become the mainstream. The density of ordinary shoe-making rubber is 1.2G / CM3, and the wear resistance is 110mm3. The sole is relatively heavy, poor wear resistance, and less soft. good. Invention content: [0003] The purpose of the present invention is to overcome the above-mentioned shortcomings, and provide a kind of high wear-resistant rubber and its manufacturing method. A high wear-resistant rubber outsole made by vulcanization and other operations. This rubber outsole is applied to the sole of sports shoes and has the advantages of light weight, good elasticity and good softness. [0004] To achieve the above object, the present invention adopts th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/00C08L7/00C08L9/06C08K13/02C08K3/36C08K3/22C08K5/09C08K3/06B29C43/02B29B7/00A43B13/04
Inventor 丁水波
Owner XTEPCHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com