Polyurea waterproofing paint

A waterproof coating, polyurea technology, applied in polyester coatings, polyether coatings, polyurea/polyurethane coatings, etc., can solve the problems of opacity, unfavorable waterproof coatings and water seepage, and achieve good water seepage performance.

Active Publication Date: 2013-12-25
山东正大防水材料股份有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the waterproof coatings currently on the market are simply mixed with emulsion and water. After the waterproof coating is applied to the substrate, the formed film is not transparent, and the film is very thin, which is not conducive to the waterproof coating to prevent water seepage.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A polyurea waterproof coating, which consists of the following components in parts by weight: 40 parts of polyether, 40 parts of polyester, 2 parts of bactericide, 2 parts of defoamer, 10 parts of filler, 5 parts of plasticizer, and 6 parts of curing agent 80 parts and 80 parts of water are mixed and stirred.

[0019] In this embodiment, the polyether is polyethylene glycol ether 3000, the polyester is polyethylene terephthalate, and the defoamer is polysiloxane, polyacrylic acid polymer or their mixture, the filler is calcium fluoride, the plasticizer is dioctyl phthalate or dibutyl phthalate, and the curing agent is 4-hydroxybenzenesulfonic acid.

[0020] The preparation method of the above-mentioned polyurea waterproof coating is as follows: mixing and stirring the required amount of each component material, stirring for 2 hours, and the stirring speed is 500r / min to obtain the desired product.

Embodiment 2

[0022] A polyurea waterproof coating, which consists of the following components in parts by weight: 60 parts of polyether, 60 parts of polyester, 1 part of bactericide, 1 part of defoamer, 8 parts of filler, 2 parts of plasticizer, and 3 parts of curing agent 60 parts and 60 parts of water are mixed and stirred.

[0023] In this embodiment, the polyether is polyethylene glycol ether 3000, the polyester is polyethylene terephthalate, and the defoamer is polysiloxane, polyacrylic acid polymer or their mixture, the filler is calcium fluoride, the plasticizer is dioctyl phthalate or dibutyl phthalate, and the curing agent is 4-hydroxybenzenesulfonic acid.

[0024] The preparation method of the above-mentioned polyurea waterproof coating is as follows: mixing and stirring the required amount of each component material, stirring for 1 hour, and the stirring speed is 800r / min to obtain the desired product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a polyurea waterproofing paint. The paint is prepared by mixing and stirring the following components in parts by weight: 40-60 parts of polyether, 40-60 parts of polyester, 1-2 parts of bactericide, 1-2 parts of defoaming agent, 8-10 parts of filler, 2-5 parts of plasticizer, 3-6 parts of curing agent, and 60-80 parts of water. The polyurea waterproofing paint is transparent after being coated on the surface of a base material to form a film, so that the color of the base material is not changed after the film is formed. Furthermore, the paint is solvent-free and pollution-free, is of a high reaction type, and is good in water seepage resistance.

Description

technical field [0001] The invention relates to a polyurea waterproof coating, which belongs to the field of new materials. Background technique [0002] Polyurea waterproof coatings are mainly used to prevent water seepage. Most of the waterproof coatings currently on the market are simply mixed with emulsion and water. After the waterproof coating is applied to the substrate, the formed film is not transparent, and the film is very thin, which is not conducive to the waterproof coating to prevent water seepage. Therefore, the development of a solvent-free, pollution-free, high-response polyurea waterproof coating is necessary. Contents of the invention [0003] Purpose of the invention: The technical problem to be solved by the present invention is to provide a solvent-free, pollution-free, high-response polyurea waterproof coating. [0004] In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is: ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D175/02C09D171/00C09D167/00C09D7/12
Inventor 朱静
Owner 山东正大防水材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products