Production method of anti-cracking leather

A production method and anti-cracking technology, which is applied in the directions of leather drying, leather surface treatment, leather flattening/rolling, etc., can solve the problems of leather surface cracking, leather cracking resistance, weak leather cracking resistance, etc. Achieve the effect of optimizing the production process and excellent crack resistance

Active Publication Date: 2014-01-01
漳州香洲皮革有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the continuous development of leather technology, its resistance has been greatly improved, but because the leather is exposed to the external environment for a long time, it is easily oxidized and cracked by the environment, and the existing leather is weak in tensile cracking ability. Leather is pron

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The invention provides a kind of production method of anti-cracking leather, it comprises:

[0032] To prepare the leather, it is required to have a uniform thickness of 1.4-1.6mm, the leather body is filled and full, and the fur is average.

[0033] Primer coating process: Take 100 parts by mass of water, heat to 10-25 degrees Celsius, add 55-65 parts by mass of cationic wax, stir for 1-2 minutes, then add 35-45 parts by mass of acrylic resin, stir for 1-2 minutes, Make it fully dissolve; spread the leather on the conveyor belt of the spraying machine, the transmission speed of the conveyor belt is 0.8-1.2 meters per second, the amount of paint is 13-15g / square foot, the length of the coating is 20 meters, and the transmission speed is 0.08- 0.15 meters per second, bake in an oven with a baking temperature of 80-100 degrees Celsius, and repeat the above spraying 2-3 times.

[0034] Rolling process: place the sprayed leather in the primer process at room temperature of...

Embodiment 2

[0041] The invention provides a kind of production method of anti-cracking leather, it comprises:

[0042] To prepare the leather, it is required to shave it to an even thickness of 1.4 mm, and the leather body is full and full of fur.

[0043] Primer coating process: Take 100 parts by mass of water, heat it to 10~25 degrees Celsius, add 55 parts by mass of cationic wax, stir for 2 minutes, then add 45 parts by mass of acrylic resin, stir for 2 minutes to fully dissolve it; Lay flat on the conveyor belt of the spraying machine. The conveying speed of the conveying belt is 0.8 meters per second, and the coating dosage is 13g / square foot. , the above spraying was repeated 2 times.

[0044] Rolling process: place the sprayed leather in the primer process at room temperature of 10-30 degrees Celsius for 3 hours, heat the roller to 100 degrees Celsius, and adjust the pressure of the roller of the roller to 7 kg per square centimeter. The speed of the tumbler conveyor belt is set ...

Embodiment 3

[0051] The invention provides a kind of production method of anti-cracking leather, it comprises:

[0052] To prepare the leather, it is required to shave it to an even thickness of 1.6mm, and the leather body is well filled, and the fur is like grass.

[0053] Primer coating process: Take 100 parts by mass of water, heat it to 10~25 degrees Celsius, add 60 parts by mass of cationic wax, stir for 2 minutes, then add 40 parts by mass of acrylic resin, stir for 2 minutes to fully dissolve it; Lay flat on the conveyor belt of the spraying machine, the transmission speed of the conveyor belt is 0.9 meters per second, the amount of paint is 15g / square foot, after coating, the length is 20 meters, the transmission speed is 0.1 meters per second, and the baking temperature is 90 degrees Celsius. , the above spraying was repeated 3 times.

[0054] Rolling process: place the sprayed leather in the primer process at room temperature of 10-30 degrees Celsius for 10 hours, heat the rolli...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of leather production and specifically relates to a production method of anti-cracking leather. The production method comprises the following step of sequentially performing primary coating, tumbling, floating coating, tumbling, scratching, color correction and drum falling treatment on a leather material with a plump leather body and general fur, wherein in the primary coating step, a cationic wax agent and acrylic resin are used for being dissolved in water for spray-coating treatment; in the tumbling step, a tumbling machine is used for tumbling; in the floating coating step, a leather hand feeling agent and waterborne color-changing wax are used for being dissolved in the water for spray-coating treatment; in the top coating step, a hand feeling agent is used for being dissolved in the water for spray-coating treatment. By adopting the method provided by the invention, an obtained leather finished product has the advantages of strong anti-cracking capability and no need of frequent washing, the service life of the leather is prolonged, the original luster of the leather is kept to the greatest extent, strong compressive capacity is achieved, and the leather is less prone to damages during a using process.

Description

technical field [0001] The invention relates to the technical field of leather production, in particular to a production method of anti-cracking leather. Background technique [0002] Leather is a material commonly used in daily life. It is used in various aspects such as dressing and hats, furniture making and so on. [0003] With the continuous development of leather technology, its resistance has been greatly improved, but because the leather is exposed to the external environment for a long time, it is easily oxidized and cracked by the environment, and the existing leather is weak in tensile cracking ability. Leather is prone to cracks during repeated use. On the one hand, the cracks will affect the aesthetics of leather products, and on the other hand, the cracks produced during long-term use will easily crack the leather surface. In addition, the current anti-cracking ability of leather cannot meet the requirements of some specific occasions. Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C14C11/00C14B1/58C14B1/30C14B1/54
CPCC14B1/30C14B1/54C14B1/58C14B2700/07C14B2700/12C14B2700/14C14C11/00
Inventor 许维奇
Owner 漳州香洲皮革有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap