Nano macromolecular insulating and heat-isolation environment-friendly paint

A nano-polymer and environmentally friendly coating technology, applied in anti-corrosion coatings, anti-fouling/underwater coatings, coatings, etc., can solve the problems of easy corrosion of coatings, danger of acrylate, poor antibacterial effect, etc., to prevent breeding and The effect of reproduction, excellent tear resistance and good market prospect

Inactive Publication Date: 2017-09-19
李壮
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, most anti-corrosion coatings contain acrylate oligomers and monomers, but acrylates are dangerous and toxic, especially strong irritants to eyes and skin
General coatings are easily corroded, easily peeled off, moldy, etc., have a short service life, and have poor antibacterial effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A nano-polymer insulating heat-insulating environmental protection coating, prepared from the following components by weight: 40-80 parts of phenolic resin, 120-160 parts of butyrolactone, 20-30 parts of zinc borate, 20-40 parts of aluminum hydroxide 12-24 parts of triester phosphate, 12-18 parts of antimony trioxide, 4-12 parts of asbestos fiber, 4-8 parts of isopropyl acrylate, 8-12 parts of butyl acetate, 15-25 parts of acetate, 50-60 parts of benzene-free epoxy resin, 20-26 parts of conductive diacetone alcohol, 2-5 parts of titanium dioxide, 8-12 parts of conductive additive, 2-8 parts of conductive zinc oxide, 5-10 parts of nano-antibacterial titanium dioxide , 25-27 parts of heavy calcium carbonate, 8-10 parts of filler, 0.6-0.8 part of dispersant, 0.3-0.8 part of defoamer, 0.1-0.5 part of thickener, 3-5 parts of nano carbon powder, 5 parts of glass fiber -8 servings.

[0016] The acetate is adipate, the filler is superfine talcum powder, and 3-6 parts by weight...

Embodiment 2

[0018] A nano-polymer insulating and heat-insulating environmental protection coating, which is prepared from the following components in parts by weight: 40 parts of phenolic resin, 120 parts of butyrolactone, 20 parts of zinc borate, 20 parts of aluminum hydroxide, and 12 parts of phosphoric acid triester 12 parts of antimony trioxide, 4 parts of asbestos fiber, 4 parts of isopropyl acrylate, 8 parts of butyl acetate, 15 parts of acetate, 50 parts of benzene-free epoxy resin, 20 parts of conductive diacetone alcohol, 2 parts of titanium dioxide Parts, 8 parts of conductive additive, 2 parts of conductive zinc oxide, 5 parts of nano antibacterial titanium dioxide, 25 parts of heavy calcium carbonate, 8 parts of filler, 0.6 part of dispersant, 0.3 part of defoamer, 0.1 part of thickener, nano 3 parts of carbon powder, 8 parts of glass fiber.

[0019] The acetate is adipate, the filler is superfine talcum powder, and 6 parts by weight of an anti-humidity agent is also provided....

Embodiment 3

[0021] A nano-polymer insulating and heat-insulating environmental protection coating, which is prepared from the following components by weight: 80 parts of phenolic resin, 160 parts of butyrolactone, 30 parts of zinc borate, 40 parts of aluminum hydroxide, 24 parts of phosphate triester, 18 parts of antimony trioxide, 12 parts of asbestos fiber, 8 parts of isopropyl acrylate, 12 parts of butyl acetate, 25 parts of acetate, 60 parts of benzene-free epoxy resin, 26 parts of conductive diacetone alcohol, 5 parts of titanium dioxide, 12 parts of conductive additive, 8 parts of conductive zinc oxide, 10 parts of nano antibacterial titanium dioxide, 27 parts of heavy calcium carbonate, 10 parts of filler, 0.8 part of dispersant, 0.8 part of defoamer, 0.5 part of thickener, nano carbon powder 5 parts, glass fiber 8 parts.

[0022] The acetate is adipate, the filler is superfine talcum powder, and 3 parts by weight of an anti-humidity agent is also provided.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a nano-polymer insulating and heat-insulating environmental protection paint, which belongs to the technical field of building materials. It is prepared from the following components by weight: 40-80 parts of phenolic resin, 120-160 parts of butyrolactone, 20-30 parts of zinc borate, 20-40 parts of aluminum hydroxide, 12-24 parts of phosphate triester, 12-18 parts of antimony trioxide, 4-12 parts of asbestos fiber, 4-8 parts of isopropyl acrylate, 8-12 parts of butyl acetate, 15-25 parts of acetate, 50-60 parts of benzene-free epoxy resin, 20-26 parts of conductive diacetone alcohol, 2-5 parts of titanium dioxide, 8-12 parts of conductive additive, 2-8 parts of conductive zinc oxide, etc. The invention has stable quality, good use effect, non-toxic raw materials for production, environmental protection, good insulation and heat insulation properties, good acid resistance and alkali resistance, and strong adhesion, and low production cost. , has a good market prospect.

Description

technical field [0001] The invention relates to a paint component, in particular to a nano-polymer insulating, heat-insulating and environment-friendly paint, which belongs to the technical field of building materials. Background technique [0002] Paint is coated on the surface of the object to be protected or decorated, and can form a continuous film firmly attached to the object to be coated, usually based on resin, or oil, or emulsion, with or without adding pigments, fillers, and adding corresponding Additives, viscous liquids prepared with organic solvents or water. Currently, most anti-corrosion coatings contain acrylate oligomers and monomers, but acrylates are dangerous and toxic, especially strong irritants to eyes and skin. General paint is easy to be corroded, easy to peel, fall off, moldy, etc., has a short service life, and has poor antibacterial effect. Contents of the invention [0003] The purpose of the present invention is to provide a nano-polymer ins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/06C09D4/02C09D7/12C09D7/06C09D5/25C09D5/08C09D5/14
CPCC09D4/06C09D5/08C09D5/14
Inventor 李壮
Owner 李壮
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com