Method for manufacturing flocking stainless steel spraying decoration plate

A manufacturing method and technology of stainless steel, applied in chemical instruments and methods, building structure, layered products, etc., can solve the problems of flocked stainless steel sheets failing to achieve the effect of light diffuse reflection, monotonous color, and weak velvet feeling. , to achieve the effect of bright and dazzling colors, soft hand feeling and strong velvet feeling

Inactive Publication Date: 2014-01-15
WUXI XINDAZHONG STEEL SHEET
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the flocking stainless steel plate has weak velvet feeling and monotonous color, especially with the expansion of the surface area of ​​the suede surface, the flocking stainless steel plate cannot achieve excellent light diffuse reflection effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The manufacture method of a kind of flocking stainless steel spray plate of the present invention comprises the following steps:

[0018] (1) Material selection: The material is a stainless steel plate with a thickness of 0.65mm and a width of 1100mm;

[0019] (2), board surface pretreatment: clean the board surface, unoiled stainless steel plate with a thickness of 0.65 mm and a width of 1100 mm enters the surface treatment machine for pretreatment of the board surface coating agent. The coated board surface treatment agent is FD90 passivator produced by Nippon Paint Co., Ltd. The single-side coating speed of the board surface treatment agent is: 10m / min, and the single-side coating amount of the board surface treatment agent is: 0.9g / m 2 , the temperature of the surface treatment agent when coating is 15°C;

[0020] (3) Drying treatment: the stainless steel plate coated with the surface treatment agent enters the oven for drying treatment. The temperature of the oven...

Embodiment 2

[0028] The manufacture method of a kind of flocking stainless steel spray plate of the present invention comprises the following steps:

[0029] (1) Material selection: the material is a stainless steel plate with a thickness of 0.8mm and a width of 1100mm;

[0030] (2), board surface pretreatment: clean the board surface, unoiled stainless steel plate with a thickness of 0.8 mm and a width of 1100 mm enters the surface treatment machine for pretreatment of the board surface coated with the board surface treatment agent. The coated board surface treatment agent is FD90 passivator produced by Nippon Paint. The single-side coating speed of the board surface treatment agent is: 25m / min, and the single-side coating amount of the board surface treatment agent is: 0.8g / m 2 , the temperature of the surface treatment agent is 22°C when coating;

[0031] (3) Drying treatment: the stainless steel plate coated with the surface treatment agent enters the oven for drying treatment. The te...

Embodiment 3

[0039] The manufacture method of a kind of flocking stainless steel spray plate of the present invention comprises the following steps:

[0040] (1) Material selection: The material selection is a stainless steel plate with a thickness of 0.9mm and a width of 1100mm;

[0041] (2), board surface pretreatment: clean the board surface, unoiled stainless steel plate with a thickness of 0.9 mm and a width of 1100 mm enters the surface treatment machine for pretreatment of the board surface coated with the board surface treatment agent. The coated board surface treatment agent is FD90 passivator produced by Nippon Paint. The single-side coating speed of the board surface treatment agent is: 30m / min, and the single-side coating amount of the board surface treatment agent is: 0.4g / m 2 , the temperature of the surface treatment agent when coating is 25°C;

[0042](3), drying treatment: the stainless steel plate coated with the surface treatment agent enters the oven for drying treatme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing a building plate which has corrosion resistance and weather resistance, prevents dew from dropping and has certain heat insulation performance, in particular to a method for manufacturing a flocking stainless steel spraying decoration plate. The manufacturing method comprises the following steps of material selecting, plate surface pretreatment, drying treatment, tackiness agent coating, electrostatic flocking, pattern spraying, process drying, checking, and putting in storage. The method for manufacturing the flocking stainless steel spraying decoration plate is characterized in that the flocking of electrostatic flocking is polypropylene fiber flocking. A plate surface treatment agent is FD90 passivant. A product obtained through the method has good fireproof performance, and passes China building material fireproofing grade B-1 certification after detection, complete environmental protection is achieved, pollution is avoided, environmental certification is passed, the product can be directly used indoors, and the effects that the upright flocking sense is strong, colors are bright and attractive, hand feeling is soft, sound absorption and light absorption performance is good, and light diffusion reflection is excellent are achieved.

Description

technical field [0001] The invention relates to a manufacturing method of a building panel with corrosion resistance, weather resistance, dew condensation prevention, and certain thermal insulation performance, especially a manufacturing method of a flocked stainless steel spray-painted panel. Background technique [0002] In modern decoration, stainless steel plates are used in many cases, such as square stainless steel gussets for integrated ceilings, and large-area stainless steel baking varnish plates for wall decoration. The flocked stainless steel sheet can provide more luxurious decorative effects than existing products. The fleece layer itself has a certain water absorption capacity. When the ambient humidity is too high, it can keep the condensation water on the surface of the sheet and prevent water droplets from dripping. However, the flocking stainless steel plate has weak velvet feeling and monotonous color, especially with the expansion of the surface area of ​...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04F13/075B32B15/09B32B15/16
Inventor 周明华
Owner WUXI XINDAZHONG STEEL SHEET
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com