Method for smelting high-grade pipe line steel with RH single-link process
A high-grade, pipeline steel technology, applied in the field of steelmaking, can solve the problems of lower temperature, high cost, and long cycle in the refining process, and achieve the effects of simplifying the smelting process, making up for heat loss, and reducing production costs
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0030] Example 1
[0031] During the converter tapping process, before the tapping volume reaches 1 / 3 stage, add aluminum and iron to the molten steel, and control the mass percentage of aluminum in the molten steel to 0.13% after the deoxidation is completed (see Table 1); the tapping volume reaches 1 In the / 3 to 2 / 3 stage, add lime 8kg / t steel to the molten steel. After tapping, use a top gun to blow argon into the molten steel for strong stirring. The argon blowing intensity is controlled to 5NL / min / t steel, and the argon blowing time is 8 minutes. After the molten steel is blown with argon, perform the RH vacuum treatment. After vacuuming for 3.5 minutes and the vacuum degree is 984 Pa, add the desulfurizing agent to the molten steel through the vacuum silo. After adding the desulfurizing agent, keep the vacuum degree at 992 Pa, continue RH vacuum cycle treatment of molten steel for 3 minutes (see Table 2), further deep desulfurization of molten steel. Among them, the amou...
Example Embodiment
[0032] Example 2
[0033] During the converter tapping process, before the tapping volume reaches 1 / 3 stage, add aluminum and iron to the molten steel, and control the mass percentage of aluminum in the molten steel to 0.12% after the deoxidation is completed (see Table 1); the tapping volume reaches 1 / 3 to 2 / 3 stage, add lime 9kg / t steel to the molten steel. After tapping, the top gun is used to blow argon into the molten steel for strong stirring, the argon blowing intensity is controlled to 7NL / min / t steel, and the argon blowing time is 5 minutes. After the molten steel is blown with argon, the RH vacuum treatment is carried out. After the vacuum is drawn for 4.5 minutes and the vacuum degree is 923 Pa, the desulfurization agent is added to the molten steel through the vacuum silo. After the desulfurization agent is added, the vacuum degree is maintained at 984 Pa, continue RH vacuum cycle treatment of molten steel for 3 minutes (see Table 2), further deep desulfurization of...
Example Embodiment
[0034] Example 3
[0035] During the converter tapping process, before the tapping volume reaches 1 / 3 stage, add aluminum and iron to the molten steel to control the mass percentage of aluminum in the molten steel to 0.15% after deoxidation (see Table 1); the tapping volume reaches 1 / 3 to 2 / 3 stage, add lime 10kg / t steel to the molten steel. After tapping, use a top gun to blow argon into the molten steel for strong stirring. The argon blowing intensity is controlled to 6NL / min / t steel, and the argon blowing time is 7 minutes. After the molten steel is blown with argon, the RH vacuum treatment is carried out. After the vacuum is drawn for 4.5 minutes and the vacuum degree is 977Pa, the desulfurization agent is added to the molten steel through the vacuum silo. After the desulfurization agent is added, the vacuum degree is maintained at 992Pa. RH vacuum cycle treatment of molten steel for 3 minutes (see Table 2), further deep desulfurization of molten steel. Among them, the amo...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap