A five-stand cold tandem rolling and emulsion technology, which is applied in the field of metallurgical cold rolling, can solve the problems of instable rolling speed of the unit, poor surface quality of strip steel, and low rolling speed.

Inactive Publication Date: 2016-03-02
唐山扬邦钢铁技术研究院有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

That is to say, the change of the emulsion concentration can affect the occurrence probability of slipping, thermal slipping, vibration and other defects during the rolling process, as well as the exit shape of the last stand and the pressing width of the work roll, thus finally affecting the rolling speed
If the concentration of the emulsion is set unreasonably, it may cause the rolling speed of the unit to increase and affect the rolling efficiency
In the past, the setting of the emulsion concentration on site basically relied on the experience of the operator. The same concentration was used for all specifications of strip steel, resulting in low rolling speed or low Poor surface quality brings great economic loss to the unit

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Setting method of emulsion concentration in ultra-thin strip rolling of five-stand cold tandem mill
  • Setting method of emulsion concentration in ultra-thin strip rolling of five-stand cold tandem mill
  • Setting method of emulsion concentration in ultra-thin strip rolling of five-stand cold tandem mill

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] exist figure 1 In the overall calculation flow chart of the method for setting the emulsion concentration in the ultra-thin strip rolling of the five-stand cold tandem mill as shown, first, in step 1, collect the main equipment and parameters of the five-stand cold tandem mill Process parameters, 1-5 stand rolling mill allowable maximum rolling pressure setting value P imax =(1800t, 1800t, 1800t, 1800t, 1800t) i=1, 2,...5, 1-5 stand rolling mill allowable maximum rolling power setting value F imax =(2680kw, 4000kw, 4000kw, 4000kw, 4000kw), 1-5# frame middle roller allowable maximum displacement δ imax =80mm, 1-5# frame work roll maximum positive roll bending force Maximum negative bending force of working rolls in 1-5# frame The maximum positive bending force of the middle roll of 1-5# frame The maximum negative bending force of the middle roll of 1-5# frame The maximum pressing length allowed by the end frame The maximum plate shape value allowed at the outl...

Embodiment 2

[0062] First, in step 1, collect the main equipment and process parameters of the five-stand cold tandem rolling mill, the allowable maximum rolling pressure setting value P of the 1-5 stand rolling mill imax =(1800t, 1800t, 1800t, 1800t, 1800t) i=1, 2,...5, 1-5 stand rolling mill allowable maximum rolling power setting value F imax =(2680kw, 4000kw, 4000kw, 4000kw, 4000kw), 1-5# frame middle roller allowable maximum displacement δ imax =80mm, 1-5# frame work roll maximum positive roll bending force Maximum negative bending force of working rolls in 1-5# frame The maximum positive bending force of the middle roll of 1-5# frame The maximum negative bending force of the middle roll of 1-5# frame The maximum pressing length allowed by the end frame The maximum plate shape value allowed at the outlet of the last frame 1-5# work roll diameter D iw ={476.84,480.86,463.06,399.33,406.86}mm, 4-5# frame middle roller diameter D im ={533.26,529.82,513.45,510.46,508.92}mm, 1-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

A method for setting the concentration of the emulsion in the ultra-thin strip rolling of a five-stand cold tandem rolling unit, comprising the following steps executed by a computer: 1. Collecting the main equipment of the unit, the characteristics of the strip to be rolled, the main rolling process and Process lubrication system parameters; 2. Define relevant process parameters; 3. Calculate roll bending force and roll shifting amount; 4. Assign values ​​to relevant search process parameters; 5. Calculate concentration process parameters; 6. Calculate search process speed of maximum rolling speed; 7. Calculate the friction coefficient of each stand under the current conditions; 8. Calculate the rolling force, rolling power, slip factor, thermal slip index and vibration coefficient of each stand under the current conditions; 9. Calculate the working roll of each stand Thermal convexity; 10. Calculate the outlet plate shape and pressing width; 11. Obtain and output the optimal ratio concentration. The invention can increase the rolling speed, ensure the rolling efficiency, avoid slipping, thermal slipping and vibration, and ensure the minimum shape of the end stand exit and the pressing width of the work roll end.

Description

technical field [0001] The invention relates to the field of metallurgical cold rolling, and is particularly suitable for a method for setting the concentration of emulsion in ultra-thin strip rolling of a five-stand cold tandem rolling mill. Background technique [0002] With the intensification of market competition, users have increasingly strong demand for strip thickness reduction, requiring manufacturers to provide 0.17mm or even thinner products. However, according to the actual experience in the field, as the strip thickness decreases, related defects such as vibration, slipping, and thermal slipping are easily generated during the production process, especially the impact on the vibration of the rolling mill is particularly obvious, and the vibration of the rolling mill will be in the strip. Alternating light and dark stripes perpendicular to the rolling direction are formed on the surface of the material or the thickness deviation at the exit is too large, which af...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): G06F17/50
CPCB21B1/28B21B37/007B21B45/0242B21B2001/221B21B2261/20B21B2265/12B21B2265/20
Inventor 白振华陈浩孔令昆王凯陈双玉常金梁
Owner 唐山扬邦钢铁技术研究院有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products