A technology of functional nanoparticles and fiber surface, applied in fiber processing, textiles and papermaking, etc., can solve the problems of unsuitable down fiber, reduced fluffiness of down, unfavorable for down application, etc., to improve production value, low cost and high efficiency The effect of using

Inactive Publication Date: 2014-02-05
WUHAN TEXTILE UNIV
View PDF7 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is suitable for polyester fibers and polyamide fibers, but not for down fibers, because this method will destroy the bimolecular film on the surface of down fibers, affect its surface stru

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] According to the above steps: take 1g of duck down fiber after washing and drying, prepare 100g of sodium polystyrene sulfonate aqueous solution with a mass fraction of 1%, the relative molecular weight of sodium polystyrene sulfonate is 3000, put duck down fiber into polystyrene Soak in the sodium sulfonate aqueous solution for 72h, soak temperature is 25 ℃, adjust pH to be 3, obtain duck down fiber / sodium polystyrene sulfonate dispersion solution. Weigh 0.5g of sodium p-styrene sulfonate and add it to 100mL deionized water, add 1g of ferric oxide after mechanical stirring for 1h, the particle size of ferric oxide is 100nm, and obtain ferric oxide solution after ultrasonic treatment for 1h, ultrasonic The processing temperature is 25 °C. Mix the above-mentioned duck down fiber / sodium polystyrene sulfonate dispersion solution and the iron ferric oxide solution at a volume ratio of 1:1, and after the mixed solution is ultrasonically treated for 1 hour, take out the duck ...

Embodiment 2

[0032]According to the above steps: take 1g of goose down fiber after washing and drying, prepare 500g of sodium polystyrene sulfonate aqueous solution with a mass fraction of 5%, the relative molecular weight of sodium polystyrene sulfonate is 12000, put the goose down fiber into polystyrene Soak in the sodium sulfonate aqueous solution for 168h, the soaking temperature is 50 DEG C, adjust the pH to be 5, obtain the goose down fiber / sodium polystyrene sulfonate dispersion solution. Weigh 1g of sodium dodecylbenzenesulfonate and add it to 100mL deionized water, add 5g of carbon nanotubes after mechanical stirring for 1h, the particle size of the carbon nanotubes is 20nm, and obtain a carbon nanotube solution after ultrasonic treatment for 5h, and the ultrasonic treatment temperature at 50°C. The above-mentioned goose down fiber / sodium polystyrene sulfonate dispersion solution and the carbon nanotube solution were mixed according to the volume ratio of 1:2, and after the mixed ...

Embodiment 3

[0034] According to the above steps: take 1g of duck down fiber after washing and drying, prepare 300g of sodium polystyrene sulfonate aqueous solution with a mass fraction of 3%, the relative molecular weight of sodium polystyrene sulfonate is 8000, put duck down fiber into polystyrene Soak 120h in the sodium sulfonate aqueous solution, soak temperature is 40 ℃, adjust pH to be 4, obtain duck down fiber / sodium polystyrene sulfonate dispersion solution. Weigh 0.8g of sodium dodecylsulfonate and add it to 100mL of deionized water, add 3g of silver particles after mechanical stirring for 1h, the particle size of the silver particles is 30nm, and obtain a silver particle solution after ultrasonic treatment for 3h, and the ultrasonic treatment temperature is 40 ° c. Mix the above-mentioned duck down fiber / sodium polystyrene sulfonate dispersion solution and the silver particle solution according to the volume ratio of 1:1.5, and after the mixed solution is ultrasonically treated f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a method for compounding functional nano particles on the surfaces of down feather fibers and belongs to the technical field of textile materials. According to the method provided by the invention, the functional nano particles are compounded on the surfaces of the down feather fibers by preparing a down feather fiber/sodium polystyrenesulfonate dispersed solution, preparing a functional nano particle solution and compounding the surfaces of the down feather fibers. The dispersed functional nano particles are firmly compounded on the surfaces of the down feather fibers by the effects of molecules layer upon layer through sodium polystyrenesulfonate, a sulfo group dispersing agent and the functional nano particles, so that the down feather fibers have various functions. The method for compounding the functional nano particles on the surfaces of the down feather fibers effectively utilizes a lot of waste down feather fibers, improves the additional value of the down feather fibers and explores applications of the down feather fibers in the other fields; furthermore, the whole process equipment is simple, the cost is low, pollution to the ecological environment is not caused and the application prospect is very great.

Description

technical field [0001] The invention relates to a method for compounding functional nanoparticles on the surface of down fibers, belonging to the technical field of textile materials. Background technique [0002] Down comes from the feathers of poultry. It is a natural protein material and is very rich in resources. Our country's annual output reaches more than 600,000 tons, accounting for 60% of the world's total output. It has a wide range of sources and low economic costs. Down is in the shape of a flower, with 60-150 down filaments, which are distributed radially outward with a node as the core, forming a three-dimensional spatial structure that is sparse on the outside and dense on the inside. The down silk has the characteristics of natural curl and softness, and the closer the distribution of the down silk to the core, the greater the density of the down silk. Therefore, the velvet filaments between the velvet and velvet are not cohesive, and are in a fluffy state. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M19/00D06M15/233D06M11/49D06M11/74D06M11/83D06M11/46
Inventor 刘欣郭蕾程远佳吴勇敏陈凤翔徐卫林
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap