Highly abrasion resistant brake pad and preparation method thereof

A brake pad, high wear-resistant technology, applied in the field of brake pads, can solve problems such as increased brake load, achieve the effect of increasing friction torque, improving cushioning and wear resistance, and simple process

Inactive Publication Date: 2014-03-19
NINGGUO FEIYING AUTO SPARE PARTS
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] As we all know, there are high mountains and steep roads in Yunnan, Guizhou, Sichuan, and cars are still overloaded when driving, which increases the load on the brakes. There are also great restrictions on the price of brake pads in China. If the price is too high, they cannot be sold. How to prepare a wear-resistant Good performance, stable friction coefficient at high temperature, simple preparation method, low cost, and cheap brake pads have become technical problems that need to be solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high wear-resistant brake pad, its raw materials include: 13.6% modified phenolic resin, 32.5% fiber material, 47.9% filler material, 6% Xinjiang white vermiculite, wherein the fiber material is composed of mineral fiber, glass Fiber and paper fiber composition;

[0019] In this embodiment, the preparation method of the above-mentioned high wear-resistant brake pad includes the following steps:

[0020] S1, take modified phenolic resin, fiber material, filler material and Xinjiang white vermiculite by weight percentage;

[0021] S2. Mix the modified phenolic resin, filler material and Xinjiang white vermiculite in S1 evenly, then add the fiber material in S1 and fully mix evenly in a plow mixer;

[0022] S3. Send the material obtained in S2 and the rubberized brake pad back plate to a hydraulic press for pressing, wherein the pressing temperature is 145° C. to obtain a high wear-resistant brake pad.

Embodiment 2

[0024] A high wear-resistant brake pad, its raw materials include by weight percentage: 15.3% modified phenolic resin, 31.4% fiber material, 48.6% filler material, 4.7% Xinjiang white vermiculite, wherein the fiber material is mineral fiber;

[0025] In this embodiment, the preparation method of the above-mentioned high wear-resistant brake pad includes the following steps:

[0026] S1, take modified phenolic resin, fiber material, filler material and Xinjiang white vermiculite by weight percentage;

[0027] S2. Mix the modified phenolic resin, filler material and Xinjiang white vermiculite in S1 evenly, then add the fiber material in S1 and fully mix evenly in a plow mixer;

[0028] S3. Send the material obtained in S2 and the rubberized brake pad back plate to a hydraulic press for pressing, wherein the pressing temperature is 149° C. to obtain a high wear-resistant brake pad.

Embodiment 3

[0030] A high wear-resistant brake pad, its raw materials include: 15.7% modified phenolic resin, 29.5% fiber material, 50.8% filler material, 4% Xinjiang white vermiculite, wherein the fiber material is composed of mineral fiber, glass Fiber and paper fiber composition;

[0031] In this embodiment, the preparation method of the above-mentioned high wear-resistant brake pad includes the following steps:

[0032] S1, take modified phenolic resin, fiber material, filler material and Xinjiang white vermiculite by weight percentage;

[0033] S2. Mix the modified phenolic resin, filler material and Xinjiang white vermiculite in S1 evenly, then add the fiber material in S1 and fully mix evenly in a plow mixer;

[0034] S3. Send the materials obtained in S2 and the glue-coated brake pad back plate to a hydraulic press for pressing, wherein the pressing temperature is 153° C. to obtain a high wear-resistant brake pad.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a highly abrasion resistant brake pad which comprises, by weight, 13-16% of modified phenolic resin, 28-33% of fiber materials, 45-55% of filling materials and 3-6% of Sinkiang white vermiculite, wherein the fiber materials are composed of one or more of mineral fibers, glass fibers and paper fibers. The invention further discloses a preparation method of the highly abrasion resistant brake pad. The highly abrasion resistant brake pad is stable in high-temperature friction coefficient and good in abrasion resistance, and the preparation method is simple, low in cost and suitable for Yunan, Guizhou and Sichuan regions and other regions with high mountains, steep roads and large brake loads.

Description

technical field [0001] The invention relates to the technical field of brake pads, in particular to a high wear-resistant brake pad and a preparation method thereof. Background technique [0002] Brake pads are also called brake pads or brake pads. In the braking system of a car, brake pads are the most critical safety parts and play a decisive role in the braking effect. Brake pads are generally made of steel plates, adhesive insulation layers and friction block composition. The friction block is composed of friction material and adhesive. When braking, the friction block is squeezed on the brake disc or brake drum to generate friction with it, so as to achieve the purpose of decelerating and braking the vehicle. It can be seen that the friction block determines the braking performance of the brake pad at high speed and high temperature. The friction material is an important part of the brake pad in the manufacturing process and use process. [0003] The working principle...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): F16D69/02C09K3/14
Inventor 孙奇春张逢
Owner NINGGUO FEIYING AUTO SPARE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com