Non-asbestos brake block containing animal fibers and manufacturing method thereof

An animal fiber, asbestos-free technology, applied in the field of brake pads, can solve the problems of inability to transfer, the blank is easy to fall apart, etc., and achieve the effects of not easy to fall apart, good dispersion and adsorption performance, and improved wear resistance.

Inactive Publication Date: 2014-03-19
NINGGUO FEIYING AUTO SPARE PARTS
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the prohibition of asbestos, more and more asbestos-free formulas have been developed, because the friction materials of brake pads generally have to go through two processes of cold pressing preforming and hot pressing forming, and asbestos substitute materials do not have good dispersion and Absorptivity, resulting in cold-pressed preformed blanks that are easy to fall apart after being released from the mold, and cannot be transported. Therefore, how to prepare a non-asbestos formula with good high temperature resistance and good wear resistance when cold-pressed preformed Strength, so as to achieve the purpose of transshipment asbestos-free brake pads become a technical problem to be solved at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A non-asbestos brake pad containing animal fiber, its raw materials include: 14.4% modified phenolic resin, 25% fiber material, 53% filling material, 7.6% sheep wool; wherein the fiber material is made of mineral fiber , glass fiber and paper fiber.

[0021] In the present embodiment, the preparation method of the above-mentioned non-asbestos brake pad containing animal fibers comprises the following steps:

[0022] S1. Weigh modified phenolic resin, fiber materials, filling materials and sheep wool by weight percentage;

[0023] S2. Mix the modified phenolic resin and the filler material in S1 evenly, then add the fiber material and sheep wool described in S1 and mix evenly in a plow mixer;

[0024] S3. Send the material obtained in S2 and the glued brake pad back plate into the hydraulic press for cold press preforming, and the control pressure is 21MPa;

[0025] S4. The product obtained in S3 is subjected to hot-press molding at a pressing temperature of 148° C. to...

Embodiment 2

[0027] A non-asbestos brake pad containing animal fibers, its raw materials include: 15% modified phenolic resin, 23.7% fiber materials, 55.1% filling materials, 6.2% animal fibers, wherein the animal fibers are composed of sheep wool, rabbit Composed of wool, camel hair and goat hair, the fiber material is mineral fiber;

[0028] In the present embodiment, the preparation method of the above-mentioned non-asbestos brake pad containing animal fibers comprises the following steps:

[0029] S1. Weigh modified phenolic resin, fiber materials, filling materials and animal fibers by weight percentage;

[0030] S2. Mix the modified phenolic resin and the filler material in S1 evenly, then add the fiber material and animal fiber described in S1 and mix evenly in a plow mixer;

[0031] S3. Send the materials obtained in S2 and the glue-coated brake pad back plate into the hydraulic press for cold-press preforming, and the control pressure is 24MPa;

[0032] S4. The product obtained ...

Embodiment 3

[0034] A non-asbestos brake pad containing animal fibers, its raw materials include: 15.3% modified phenolic resin, 23% fiber materials, 56% filling materials, 5.7% animal fibers, wherein the animal fibers are made of mohair, yak hair , silk and goat hair, fiber materials are composed of mineral fibers, glass fibers and paper fibers;

[0035] In the present embodiment, the preparation method of the above-mentioned non-asbestos brake pad containing animal fibers comprises the following steps:

[0036] S1. Weigh modified phenolic resin, fiber materials, filling materials and animal fibers by weight percentage;

[0037] S2. Mix the modified phenolic resin and the filler material in S1 evenly, then add the fiber material and animal fiber described in S1 and mix evenly in a plow mixer;

[0038] S3. Send the materials obtained in S2 and the glue-coated brake pad back plate into the hydraulic press for cold-press preforming, and the control pressure is 25MPa;

[0039] S4. The produ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a non-asbestos brake block containing animal fibers. The non-asbestos brake block comprises, by weight, 14-16% of modified phenolic resin, 20-28% of fiber material, 53-61% of filling material and 5-8% of the animal fibers. The animal fibers are composed of one or more of sheep wool, cony hair, camel hair, goat hair, mohair, yakwool and silk, and the fiber material is composed of one or more of mineral fibers, glass fibers and paper fibers. The invention further discloses a manufacturing method for the non-asbestos brake block containing the animal fibers. The non-asbestos brake block containing the animal fibers is good in high-temperature resistance and abrasive resistance, the non-asbestos formula can have good strength in the cold-pressing performing process so that the purpose of transferring can be achieved, and the non-asbestos brake block containing the animal fibers is simple in manufacturing method and low in cost.

Description

technical field [0001] The invention relates to the technical field of brake pads, in particular to an asbestos-free brake pad containing animal fibers and a preparation method thereof. Background technique [0002] Brake pads are also called brake pads or brake pads. In the braking system of a car, brake pads are the most critical safety parts and play a decisive role in the braking effect. Brake pads are generally made of steel plates, adhesive insulation layers and friction block composition. The friction block is composed of friction material and adhesive. When braking, the friction block is squeezed on the brake disc or brake drum to generate friction with it, so as to achieve the purpose of decelerating and braking the vehicle. It can be seen that the friction block determines the braking performance of the brake pad at high speed and high temperature. The friction material is an important part of the brake pad in the manufacturing process and use process. [0003] T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): F16D69/02C09K3/14
Inventor 孙奇春张逢
Owner NINGGUO FEIYING AUTO SPARE PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com