Surface treating agent for copper and copper alloys

A surface treatment agent and copper alloy technology, applied in the field of metal surface treatment agents, can solve the problems of weak rust removal ability and poor oil stain removal performance, and achieve the effect of strong rust removal ability and good oil stain removal performance

Active Publication Date: 2014-03-26
江苏鑫美特金属科技有限公司
View PDF2 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] This application aims to provide a copper and copper alloy surface treatment agent for the technical problems of poor oil removal performance and weak rust removal ability of existing metal surface treatment agents.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A copper and copper alloy surface treatment agent, its composition expressed in parts by mass: 100 parts of sodium hydroxide; 0.2 parts of pickling corrosion inhibitor; 1 part of ethanol; 15 parts of sodium phosphate; fatty alcohol polyoxyethylene ether 8 parts; 10 parts of sodium carbonate; 1 part of butyl cellosolve; 5 parts of surfactant; 4 parts of triethanolamine; 10 parts of sodium tripolyphosphate; 5 parts of sodium hexametaphosphate; 20 parts of turpentine; 10 parts of water.

[0018] The product has good oil stain removal performance and strong rust removal ability. It can be treated for 4 hours at room temperature and 15 minutes when the temperature is 80°C.

[0019]

Embodiment 2

[0021] A copper and copper alloy surface treatment agent, its composition expressed in parts by mass: 100 parts of sodium hydroxide; 0.5 parts of pickling corrosion inhibitor; 3 parts of ethanol; 35 parts of sodium phosphate; fatty alcohol polyoxyethylene ether 10 parts; 40 parts of sodium carbonate; 5 parts of butyl cellosolve; 10 parts of surfactant; 5 parts of triethanolamine; 15 parts of sodium tripolyphosphate; 10 parts of sodium hexametaphosphate; 25 parts of turpentine; 20 parts of water.

[0022] The product has good oil stain removal performance and strong rust removal ability. It can be treated for 2 hours at room temperature and 10 minutes when the temperature is 70°C.

[0023]

Embodiment 3

[0025] A copper and copper alloy surface treatment agent, characterized in that: its composition expressed in parts by mass is: 100 parts of sodium hydroxide; 0.35 parts of pickling corrosion inhibitor; 2 parts of ethanol; 25 parts of sodium phosphate; fatty alcohol 9 parts of polyoxyethylene ether; 25 parts of sodium carbonate; 3 parts of butyl cellosolve; 7.5 parts of surfactant; 4.5 parts of triethanolamine; 12.5 parts of sodium tripolyphosphate; 7.5 parts of sodium hexametaphosphate; 22.5 parts of turpentine; 15 servings.

[0026] The product has good oil stain removal performance and strong rust removal ability. It can be treated for 1 hour at room temperature and 5 minutes when the temperature is 60°C.

[0027] All components in the above examples are commercially available.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A surface treating agent for copper and copper alloys comprises the components in parts by mass as follows: 100 parts of sodium hydroxide, 0.2-0.5 part of a pickling inhibitor, 1-3 parts of ethanol, 15-35 parts of sodium phosphate, 8-10 parts of an emulsifier, 10-40 parts of sodium carbonate, 1-5 parts of a butyl cellosolve, 5-10 parts of a surfactant, 4-5 parts of triethanolamine, 10-15 parts of sodium tripolyphosphate, 5-10 parts of sodium hexametaphosphate, 20-25 parts of turpentine and 10-20 parts of water. The surface treating agent is good in oil stain removing performance and high in derusting capacity, takes 1-4 h for treatment at the room temperature and 5-15 min for treatment at the temperature of 60-80 DEG C, can be widely produced and can continuously replace existing materials.

Description

[0001] technical field [0002] The application belongs to the field of metal surface treatment agents, in particular to a copper and copper alloy surface treatment agent. [0003] Background technique [0004] Metal surface treatment agent refers to the general term for various chemical agents for metal surface treatment. Metal surface treatment includes degreasing, rust removal, phosphating, antirust and other substrate pretreatments, which are prepared for metal coating technology and metal protection technology. The quality of substrate pretreatment has a great influence on subsequent coating preparation and metal use. big impact. [0005] The alkaline cleaning agents mainly include sodium hydroxide, sodium carbonate, sodium silicate, sodium phosphate, etc., which dissolve in water to become alkaline cleaning agents. The principle of their action is that they can saponify with the fatty acid glycerides in the oil to form nascent soap, making the oil water-soluble and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/20C23G1/16
Inventor 王惠张松岩钱忆张陈新燕
Owner 江苏鑫美特金属科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap