Fibrous curly hair fixing adhesion agent, preparation method and periwig prepared with adhesion agent

An adhesive and fiber technology, applied in wigs, fiber processing, applications, etc., can solve the problems of scattered pieces, stiff hand, cumbersome and other problems, and achieve the effects of easy deposition, uniform appearance and low surface tension

Active Publication Date: 2014-04-16
HENAN REBECCA HAIR PRODS TNC
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the soaked special hair products have a good setting and bonding effect, they feel stiff, and the formed film is a one-time dura mater, which can no longer stick together after being combed. It will be scattered after wearing for a period of time or after washing. It is very cumbersome to go to a professional hair salon to re-style and arrange before continuing to use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] 1. Composition formula of fiber curly hair styling adhesive (in parts by weight):

[0024] 15g of polyether modified amino silicone oil, can choose conventional polyether modified amino silicone oil, preferably by mass percentage 20-35% polyether modified dimethyl silicone oil, 1-5% thickener and 60%- 80% deionized water composition.

[0025] 15g of cationic amino silicon terpolymer, you can choose conventional polyether modified amino silicone oil, preferably composed of 60-80% by mass percentage of amino silicon cationic polyether (AB) n terpolymer, 20-40% deionized water .

[0026] 10g of epoxy-modified silicone oil, you can choose conventional epoxy-modified silicone oil, preferably epoxy-modified dimethyl silicone oil with a mass percentage of 30-40% epoxy value>0.03, 5-10% isomerized thirteen Alcohol ether emulsifier, 1-5% thickener and 60%-70% deionized water.

[0027] For 10 g of PVP-based copolymers, conventional PVP-based copolymers can be selected, prefera...

Embodiment 2

[0034] 1. The composition of fiber curly hair styling adhesive components (in parts by weight): 10g of polyether-modified amino silicone oil, 20g of cationic amino-silicon terpolymer, 10g of epoxy-modified silicone oil, and 15g of PVP Copolymer, 45g of deionized water.

[0035] 2. Preparation method:

[0036] Put 45g of deionized water into a beaker, and when heated to 70°C, add 10g of polyether-modified amino silicone oil and 20g of ternary copolymerized silicone, stir with a mixer until completely dispersed in water, then cool down to 40°C, After replenishing water, add 10g of epoxy silicone oil and 15g of PVP-based copolymer, and continue to stir for 60 minutes to obtain a uniform light white bluish emulsion. After adjusting the pH value to be weakly acidic, the finished product is obtained.

[0037] 3. Dipping method:

[0038] Take 1000 ml of pre-prepared hand finishing solution at 30°C, add 3 grams of the product prepared above and stir to make it fully dissolve to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fibrous curly hair fixing adhesion agent, a preparation method and a periwig prepared with the adhesion agent. The method comprises the steps as follows: deionized water is added in an emulsifying machine and heated to 60-70 DEG C; 10-20 parts by weight of polyether modified amino-silicone and 10-20 parts of positive ion amino silicon oil terpolymer are added and stirred to enable the components to sufficiently disperse into the deionized water; and the temperature is decreased to 30-40 DEG C, 5-15 parts of epoxy silicone oil and 5-10 parts of PVP (polyvinyl pyrrolidone) copolymer are added after deionized water is supplemented, stirring is continuously performed for 1-1.5 hours to obtain a uniform light and white emulsion suffused with blue light, and the PH value is regulated into faintly acid so as to obtain a finished product. The obtained adhesion agent can be used for preparing the periwig, a transparent and glossy continuous film is formed on the fiber surface, is flexible and is not sticky, and accordingly, a higher fixing capacity and durable curl retainability are further obtained with lower usage quantity.

Description

[technical field] [0001] The invention relates to the technical field of fiber finishing agents and methods, in particular to a fiber curly hair styling adhesive, a preparation method and a wig prepared therefrom. [Background technique] [0002] In the hair product industry, there are usually many kinds of special hair products with curls. In the post-processing of this product, a certain amount of additives with a setting and bonding effect need to be added to maintain the setting and bonding effect of the product curvature. And require sticky but not stiff, soft but not loose, durable to wear and clean, etc. effects. After finishing the fibers with the post-treatment impregnation solution added with the adhesive, a layer of high-elastic and transparent soft film can be formed on the surface of the fibers to endow the curly hair with a long-lasting shape, soft and smooth, not rough or stiff, and high-elastic Glossy, full of vitality, giving people a youthful and beautiful ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/647D06M15/643D06M15/65D06M15/356A41G3/00
Inventor 郑有全郑桂花吴学丙
Owner HENAN REBECCA HAIR PRODS TNC