Large-diameter polyvinyl alcohol monofilament and production method thereof

A polyvinyl alcohol and production method technology, applied in the direction of single-component synthetic polymer rayon, chemical post-treatment of synthetic polymer rayon filament, wet spinning method, etc., can solve the unsatisfactory strength and toughness of monofilament, which affects and other problems, to achieve the effect of improving strength and toughness, increasing strength, and sufficient crystallization

Active Publication Date: 2014-04-23
NANTONG NTEC MONOFILAMENT TECH CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the strength and toughness of the prepared monofilament are not satisfactory, which affects its application prospects in industry, textile and other fields.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Large-diameter polyvinyl alcohol monofilament and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2

[0021] 98% polyvinyl alcohol particles and 2% modified nano-TiO 2 According to the production method of Example 1, polyvinyl alcohol monofilaments were obtained. The diameter of the monofilaments was 2.8 m, the strength of the monofilaments was 6 cN / dtex, and the elongation of the monofilaments was 25%.

Embodiment 3

[0023] 97% polyvinyl alcohol particles and 3% modified nano-TiO 2 According to the production method of Example 1, polyvinyl alcohol monofilaments were obtained. The diameter of the monofilaments was 2.8 mm, the strength of the monofilaments was 6 cN / dtex, and the elongation of the monofilaments was 25%.

Embodiment 4

[0025] 99% polyvinyl alcohol particles and 1% modified nano-TiO 2 According to the production method of Example 1, polyvinyl alcohol monofilaments were obtained. The diameter of the monofilaments was 2.8 mm, the strength of the monofilaments was 5 cN / dtex, and the elongation of the monofilaments was 25%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a large-diameter polyvinyl alcohol monofilament and a production method thereof. The monofilament comprises 97-99.5 percent by weight of polyvinyl alcohol and 3-0.5 percent by weight of modified nanometer inorganic additives, wherein the monofilament is 0.5-5 millimeters in diameter, 3-6.7 cN / dtex in breaking strength and 15-35 percent in the elongation at break, and the strength and toughness of the product can be improved remarkably by adding the nanometer inorganic additives. The production method mainly comprises the treatment processes of polyvinyl alcohol dissolving, defoaming, wet spinning, stretching, winding and acetalation. Furthermore, a two-step method is adopted in a stretching procedure. In a first stretching step, the stretching rate is low. In a second stretching step, hot air stretching is adopted, and the stretching rate is high, so that the large-diameter polyvinyl alcohol monofilament can be crystallized fully, and the strength of the monofilament is enhanced.

Description

technical field [0001] The invention relates to a large-diameter polyvinyl alcohol monofilament and a production method thereof, belonging to the field of polymer fibers. Background technique [0002] Polyvinyl alcohol is reflected in the size of the molecular weight and the non-complete substitution of the carboxyl group in the alcoholysis, thus forming a variety of high viscosity, low viscosity, high degree of alcoholysis and low degree of alcoholysis. Since polyvinyl alcohol is a typical polyol, it is different from Carbohydrates and their similarities are miscible with water, and because they are polymers, the solution dissolved in water has a relatively high viscosity. Water-miscible polymer materials are extremely rare both in nature and in industrial synthesis. [0003] Polyvinyl alcohol is highly polymerized to form polyvinyl alcohol monofilament, which has good surface properties, is easy to bond firmly with other materials, and has good acid and alkali resistance,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/50D01F1/10D01F11/06D01D1/02D01D1/10D01D5/06D01D5/12
Inventor 马海燕
Owner NANTONG NTEC MONOFILAMENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com