Golf club head surface processing method

A golf club head and surface treatment technology, which is applied to golf balls, golf clubs, rackets, etc., can solve the problem that golf club heads cannot have both aesthetics, corrosion resistance and wear resistance, and achieves good appearance, The effect of reducing pollution and public nuisance and beautiful appearance

Inactive Publication Date: 2014-05-14
苏 基宏
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is: to improve the problems that existing technical means such as electroplating and plasma plating cannot make the golf club head have good appearance, good corrosion resistance and wear resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Golf club head surface processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] The technical means adopted by the present invention to achieve the predetermined invention objectives are further described below in conjunction with the drawings and preferred embodiments of the present invention.

[0038] Such as figure 1 As shown, it is a flow chart disclosing a preferred embodiment of the golf club head surface treatment method of the present invention, and the golf club head surface treatment method includes the following steps:

[0039] Provide a club head, the club head is made of carbon steel (such as low carbon steel, medium carbon steel, high carbon steel, etc.) or purposefully added other elements on the basis of carbon steel material Carbon steel such as carbon alloy steel is manufactured by casting, forging and other means, and the club head can be in the form of a wood club head or an iron club head;

[0040] The step of grinding the club head, which is applied to the club head by grinding means with a grinding machine, so as to modify t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a golf club head surface processing method which mainly includes conducting nitridation and two-stage oxidation on a club head formed by a carbon steel material, matching surface processing and washing steps such as grinding and sand blasting, and then conducting polishing, oil immersing and the like to enable the club head to have the even black surface appearance and achieve good corrosion resistance and abrasion resistance. The surface of the club head cannot be stripped and the like. The club head surface processing method achieves the effects of low pollution, low cost and the like and solves the problems of high pollution, high cost, coating film stripping and the like of the existing carbon steel club head adopting rust prevention technologies like a galvanized or plasma coating film.

Description

technical field [0001] The present invention relates to a manufacturing method of a golf club head, in particular to a club head surface treatment method for a molded club head in the golf club head manufacturing method. Background technique [0002] The existing golf club heads made of carbon steel, because carbon steel will rust, and in order to make the club head aesthetic, so the existing carbon steel golf club heads will use technical means such as electroplating or plasma plating For surface preparation. in: [0003] As far as the electroplating technology is concerned, it is to plate a layer of high-silver nickel (Ni) or chromium (Cr) coating on the surface of the carbon steel club head. The thickness of the nickel coating is about 20-25 μm, and the thickness of the chromium coating is about 3 to 8 μm. However, the surface treatment method of this electroplating method uses heavy metal chemicals, which has problems of environmental pollution and harm to the human b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A63B53/04A63B102/32
Inventor 苏基宏
Owner 苏 基宏
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap