Fireproof coating used for steel structure buildings, preparation method thereof and coating process

A technology for fire-resistant coatings and steel structures, applied in fire-resistant coatings, devices for coating liquids on surfaces, coatings, etc., can solve the problems of loss of mechanical strength, poor fire resistance of steel structures, easy heat conduction, etc., and achieve good protection and good performance The effect of fire performance

Active Publication Date: 2014-05-14
LIYANG TECH DEV CENT
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the fire resistance of the steel structure is very poor, and it is very easy to conduct heat. When its own temperature exceeds 540 degrees Celsius, its mechanical strength is almost completely lost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] The acrylic resin is selected as the main film-forming material, and the silicon-acrylic emulsion is used as the secondary film-forming material, taking advantage of the advantages of fast foaming of the acrylic resin and good strength of the carbonized layer of the silicon-acrylic emulsion.

[0012] Ammonium polyphosphate, dipentaerythritol, melamine and expanded graphite are selected as the carbon forming system.

[0013] The formula and preparation method of fireproof coating of the present invention are specifically as follows:

[0014] In terms of weight percentage: 35% film-forming material (base material), 48% carbon-forming system, 1% nano-magnesia powder (40-45nm), 15% deionized water, and 1% additive.

[0015] Preferably, expressed by weight percentage: 26% of acrylic resin, 9% of silicon acrylic emulsion, 24% of ammonium polyphosphate, 12% of dipentaerythritol, 6% of melamine, 6% of expanded graphite, 1% of nano-magnesium oxide powder, deionized 15% water, 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Fire resistanceaaaaaaaaaa
Login to View More

Abstract

The invention provides a fireproof coating used for steel structure buildings. The fireproof coating selects acrylic resin as a main film forming matter and silicone-acrylate emulsion as a secondary film forming matter. A formula of the fireproof coating comprises the following components by weight percent: 26% of acrylic resin, 9% of silicone-acrylate emulsion, 24% of ammonium polyphosphate, 12% of dipentaerythritol, 6% of melamine, 6% of expanded graphite, 1% of nanometer magnesia powder, 15% of deionized water and 1% of aids. The ultrathin steel structure fireproof coating has the advantages of high performance, strong adhesion, good weather resistance and the like. The invention also relates to a preparation method of the fireproof coating used for steel structure buildings and a process for coating steel structures.

Description

technical field [0001] The invention relates to a fireproof coating for steel structure buildings, and also relates to a manufacturing method of the fireproof coating for steel structure buildings and a process for coating steel structures. Background technique [0002] Steel structures have the advantages of light weight, high strength, convenient construction, good ductility and earthquake resistance, and are increasingly widely used in the construction industry, especially in super high-rise and long-span buildings. However, the fire resistance of the steel structure is very poor, and it is very easy to conduct heat. When its own temperature exceeds 540 degrees Celsius, its mechanical strength is almost completely lost. Many fire cases of steel structure buildings at home and abroad have proved that within 20 minutes after a fire breaks out, steel structure buildings will be burned and collapsed. Therefore, the fire protection problem of steel structure buildings has att...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D133/04C09D7/12C09D5/18B05D7/24B05D3/12
Inventor 梅欣
Owner LIYANG TECH DEV CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com