Emulsion adhesive

An adhesive and emulsion technology, which is applied in the direction of adhesive type, monocarboxylic acid ester copolymer adhesive, adhesive, etc. Long time, excellent adhesion, easy cleaning effect

Inactive Publication Date: 2014-05-21
SHAANXI TECHN INST OF DEFENSE IND
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, although the general development trend of adhesives is non-organic solvation, solvent-based adhesives cannot fully reach the level of solvent-based adhesives due to their excellent process and bonding performance, and solvent-based adhesives are still exist for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] 1. Preparation of liquid resin emulsion

[0022] Weigh 0.3KG of 264 stabilizer, 1KG of PVA24881KG, 60KG of liquid resin, 3KG of 908 emulsifier, and 35.7KG of water. Put 60KG of liquid resin into a closed cylinder, close the cylinder, start the agitator to stir at 60 rpm, turn on the heater, let the temperature of the liquid resin in the cylinder rise to 90°C gradually, and turn on the vacuum at the same time, in another pull Add 35.7KG of water, 3KG of 908 emulsifier and 1KG of PVA24881KG into the tank and heat up. When the temperature rises to 90°C, add water, emulsifier and stabilizer to the first tank in a short time, mix for 40 minutes, and turn on The high-speed disperser emulsifies at a speed of 1000-1500 rpm for 10-20 minutes.

[0023] 2. Preparation of acrylic mixed emulsion

[0024] Mix 75KG of acrylic emulsion, 7KG of EVA emulsion, and 18KG of vinegar-acrylic emulsion at room temperature, and use a disperser in a cylinder at 500-700 rpm to disperse for 10-20...

Embodiment 2

[0029] 1. Preparation of liquid resin emulsion

[0030] Weigh 0.3KG of 264 stabilizer, 1KG of PVA24881KG, 60KG of liquid resin, 3KG of 908 emulsifier, and 35.7KG of water. Put 60KG of liquid resin into a closed cylinder, close the cylinder, start the agitator to stir at 60 rpm, turn on the heater, let the temperature of the liquid resin in the cylinder rise to 90°C gradually, and turn on the vacuum at the same time, in another pull Add 35.7KG of water, 3KG of 908 emulsifier and 1KG of PVA24881KG into the tank and heat up. When the temperature rises to 90°C, add water, emulsifier and stabilizer to the first tank in a short time, mix for 40 minutes, and turn on The high-speed disperser emulsifies at a speed of 1000-1500 rpm for 10-20 minutes.

[0031] 2. Preparation of acrylic mixed emulsion

[0032] Mix 75KG of acrylic emulsion, 7KG of EVA emulsion, and 18KG of vinegar-acrylic emulsion at room temperature, and use a disperser in a cylinder at 500-700 rpm to disperse for 10-20...

Embodiment 3

[0037] The preparation steps are the same as in Example 1, the difference is that in the preparation of the acrylic mixed emulsion, 65KG of the acrylic emulsion, 5KG of the EVA emulsion, and 30KG of the vinegar-acrylic emulsion are mixed at room temperature, and the disperser is used in the tank under the condition of 500-700 revolutions , dispersed for 10 to 20 minutes and mixed evenly.

[0038] Bonding effect: Material destruction.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a nontoxic and tasteless emulsion adhesive for food packaging, which consists of the following raw materials in percentage by weight: 45-62% of acrylic acid mixed emulsion, 8-10% of rosin emulsion and 30-45% of liquid resin emulsion. The emulsion adhesive has the advantages of high adhesive strength and long opening time, and is suitable for the manual and flow line production of food packaging boxes; moreover, the emulsion adhesive is remarkably convenient to apply and easy to clean.

Description

technical field [0001] The invention relates to the field of food packaging, in particular to an emulsion adhesive used for food packaging outer boxes. Background technique [0002] At present, many food packaging boxes include materials that are in direct contact with food, and most of them use adhesives. Adhesive is an auxiliary material that can bond many materials together. There are many types of adhesives, and there are more packaging materials. For example, adhesive materials include solvent-based, semi-oily, water-soluble, and emulsion-based. The substrates to be bonded include paper, cardboard, plastic materials (OPP, PE, PP, PET, BOPP, PS), wood, aluminum foil, etc. Those skilled in the art choose different adhesives to bond different substrates, so as to realize the purpose of forming different materials into a whole. [0003] The rapid development of the adhesive industry has provided the society with many new types of glue. At the same time, the toxic raw mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J133/00C09J131/04C09J123/08C09J201/00C09J11/08C09J11/06
Inventor 张桂锋
Owner SHAANXI TECHN INST OF DEFENSE IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com