High-molecular automatic adhering and wrapping rubber powder for improving safety performance of automobile tire

A technology for safety performance and automobile tires, applied in the direction of non-polymer adhesive additives, adhesives, adhesive types, etc., can solve the problem of poor adhesion of polymer self-sealing hot-melt adhesive powder and adhesion on the inner wall surface of automobile wheels and tires Unreliable, polymer self-sealing hot melt adhesive powder layer falling off, etc., to speed up the chemical reaction speed, reduce the hardness, and improve the effect of being viscous

Inactive Publication Date: 2014-05-21
LUOYANG JUNTENG ENERGY TECH
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing polymer self-sealing hot-melt adhesive powder is difficult to meet this requirement, mostly due to the poor adhesion of the polymer self-sealing hot-melt adhesive powder and the unreliable adhesion to the inner wall surface of the automobile wheel tire, causing the polymer self-sealing hot-melt adhesive powder layer to fall off or off-edge defects, it is difficult to achieve the function and effect of the upgraded car tires without deflation
[0007] In order to solve the above-mentioned problems, relevant manufacturers and research institutes have worked hard to find a solution, but no suitable polymer self-sealing hot-melt adhesive powder has been found for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Components: thermoplastic elastomers, tackifiers, plasticizers, antioxidants, fillers, catalysts, curing agents; ratio: the ratio and components of polymer self-sealing hot melt adhesives (based on weight percentage) 45 % thermoplastic elastomer, 45% tackifier, 5% plasticizer, 1% antioxidant, 3% filler, 0.5% catalyst, 0.5% curing agent; actual amount: Weigh thermoplastic elastomer: SIS 300g, polyisocyanate Pentadiene rubber 150g; tackifier: aromatic modified terpene resin 300g, rosin coumarone resin 150g; plasticizer: diisobutyl phthalate (DIBP) 50g; antioxidant 1076 10g; filler: nano Calcium carbonate 30g; catalyst: N-methyldiethanolamine 5g; curing agent: curing agent 190 5g.

Embodiment 2

[0036] Components: thermoplastic elastomers, tackifiers, plasticizers, antioxidants, fillers, catalysts, curing agents; ratio: the ratio and components of polymer self-sealing hot melt adhesive (based on weight percentage) 50 % thermoplastic elastomer, 40% tackifier, 5% plasticizer, 1% antioxidant, 3% filler, 0.5% catalyst, 0.5% curing agent; actual amount: take thermoplastic elastomer: SIS 300g, polyisocyanate 200g of pentadiene rubber; tackifier: 300g of aromatic modified terpene resin, 100g of rosin coumarone resin; plasticizer: 50g of diisooctyl phthalate (DIOP); 10g of antioxidant 1010; filler: hydrogen Aluminum oxide 30g; catalyst: N-methyl-2-pyrrolidone 5g; curing agent: curing agent 190 5g.

Embodiment 3

[0038] Components: thermoplastic elastomers, tackifiers, plasticizers, antioxidants, fillers, catalysts, curing agents; ratio: the ratio and components of polymer self-sealing hot melt adhesives (based on weight percentage) 48 % thermoplastic elastomer, 42% tackifier, 4% plasticizer, 1% antioxidant, 4% filler, 0.5% catalyst, 0.5% curing agent; actual amount: take thermoplastic elastomer: SIS 300g, polyisocyanate 180g of pentadiene rubber; tackifier: aromatic modified terpene resin 300g, rosin coumarone resin 120g; plasticizer: diisobutyl phthalate (DIBP) 40g; antioxidant 1010 5g, antioxidant 10765g; Filler: 40g of nano-calcium carbonate; Catalyst: 5g of N-methyldiethanolamine; Curing agent: 190 5g of curing agent.

[0039] The synthesis sequence of the polymer automatic adhesive coating powder proposed by the present invention is: use material crushing equipment to crush the solid raw material of the polymer automatic adhesive coating powder into <150 mesh particles at the gla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to high-molecular automatic adhering and wrapping rubber powder for improving the safety performance of an automobile tire. The high-molecular automatic adhering and wrapping rubber powder comprises the following components in percentage by weight: 42-62 percent of a thermoplastic elastomer, 34-54 percent of a thickening agent, 3-8 percent of a plasticizer, 0.5-1.5 percent of an antioxidant, 0-15 percent of a filler, 0-1 percent of a catalyst and 0-3 percent of a curing agent. Through the technical scheme provided by the invention, a common automobile tire can be upgraded to be an automobile tire with temperature resistance, pressure resistance, bullet resistance, leakage resistance, explosion resistance and puncture resistance.

Description

technical field [0001] The invention relates to a polymer rubber powder, in particular to a polymer self-adhesive rubber powder for improving the safety performance of automobile tires. Background technique [0002] At present, there are two types of car wheels used in vehicles, one with inner tubes and the other without tubes. At present, almost all of the passenger vehicles use tubeless wheels. The country requires gradual promotion and use of heavy-duty vehicles. Tubeless car wheels. The tubeless car wheel has the advantages of good heat dissipation, softness, sealing, good riding comfort, and long intervals between inflation and use. , the high-pressure gas in the tire of the car tire will leak out or blow out at the punctured part; Blowout or two situations of rapid leakage, the risk of automobile accidents is high, and the probability of car crashes and fatalities is high. [0003] Since the main technology in the market in the eighties of last century was embodied ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J153/02C09J109/00C09J145/00C09J11/06C09J11/04
Inventor 周仁福周强
Owner LUOYANG JUNTENG ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com