Water absorbent for paper and preparation method thereof

A water-absorbing agent and paper technology, applied in the field of papermaking, can solve the problems of reduced paper strength, unable to absorb water effectively, reduce paper wet strength, etc., and achieve the effects of good compatibility, excellent liquid permeability and diffusion performance.

Active Publication Date: 2014-06-18
SUZHOU HENGKANG NEW MATERIALS
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Both toilet paper and facial tissue need to have good water absorption and good wet strength. The existing additives with good water absorption will reduce the wet strength of the paper, because the wet strength agent often increases the surface of the paper. Hydrophobicity is used to increase the wet strength of paper. Due to the introduction of hydrophobic groups, the water absorption efficiency of the water-absorbing agent is reduced, and it cannot effectively absorb water.
In order to solve these problems, some researchers solved the interaction between wet strength agent and water absorbing agent by adding surfactants, but these agents will reduce the strength of paper. Therefore, it is urgent to have good water absorption without the influence of wet strength agent water absorbing agent with reduced efficacy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] (1) Stir 30kg of sodium alginate, 10kg of polyacrylamide, 10kg of glycidol and 2 kg of sodium carbonate under vacuum conditions at 50°C and 700 rpm for 1 hour, then pass in nitrogen for cooling.

[0026] (2) Add sodium polyacrylate 30kg, hydroxyethyl cellulose 30kg, ethylene glycol monomethacrylate and polyethylene glycol monomethacrylate in a molar ratio of 1:2 to the product in step (1) 20kg of the resin copolymer and 10kg of pentaerythritol were ultrasonically dispersed to remove air bubbles to obtain a water-absorbing agent for paper.

[0027] The water absorption of the paper added with the water-absorbing agent for paper was 120% higher than that of the paper without the addition.

Embodiment 2

[0029] (1) Stir 25kg of sodium alginate, 5kg of polyacrylamide, 15kg of glycidol and 0.5kg of sodium carbonate under vacuum conditions at 70°C and 700 rpm for 1 hour, and then pass in nitrogen for cooling.

[0030] (2) Add sodium polyacrylate 50kg, hydroxyethyl cellulose 40kg, ethylene glycol monomethacrylate and polyethylene glycol monomethacrylate in a molar ratio of 1:2 to the product of step (1). 35kg of copolymer and 15kg of pentaerythritol were ultrasonically dispersed to remove air bubbles to obtain a water-absorbing agent for paper.

[0031] The water absorption of the paper added with the water-absorbing agent for paper was 114% higher than that of the paper without the addition.

Embodiment 3

[0033] (1) 20kg of sodium alginate, 8kg of polyacrylamide, 12kg of glycidyl alcohol and 1kg of sodium carbonate were stirred for 1 hour at 60°C and 700 rpm under vacuum conditions, and cooled by nitrogen gas.

[0034] (2) Add sodium polyacrylate 40kg, hydroxyethyl cellulose 50kg, ethylene glycol monomethacrylate and polyethylene glycol monomethacrylate in a molar ratio of 1:2 to the product of step (1). 30 kg of the copolymer and 12 kg of pentaerythritol were ultrasonically dispersed to remove air bubbles to obtain a water-absorbing agent for paper.

[0035] The water absorption of the paper added with the water-absorbing agent for paper was 132% higher than that of the paper without the addition.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a water absorbent for paper and a preparation method thereof. The water absorbent for paper is prepared from the following components in parts by weight: 30-50 parts of sodium polyacrylate, 20-30 parts of sodium alga acid, 30-50 parts of hydroxyethyl cellulose, 20-35 parts of resin copolymers, 5-10 parts of polyacrylamide, 10-15 parts of pentaerythritol, 10-15 parts of glycidol and 0.5-2 parts of sodium carbonate. The prepared water absorbent can be applied to the field of papermaking, and the paper prepared with the water absorbent can have a good synergistic effect with a cationic wet strength agent when having good hygroscopic property and a high water-retention rate. Thus, the dry strength and the wet strength of the paper can be enhanced.

Description

technical field [0001] The invention belongs to the technical field of papermaking, and in particular relates to a water-absorbing agent for paper and a preparation method thereof. Background technique [0002] Super absorbent material is a new type of functional polymer material developed in recent years, which can absorb hundreds or even thousands of times its own weight in water, and has a strong water retention capacity and can be used repeatedly. [0003] Both toilet paper and facial tissue need to have good water absorption and good wet strength. Existing additives with good water absorption will reduce the wet strength of paper, because wet strength agents often increase the paper surface Hydrophobicity is used to increase the wet strength of paper. Due to the introduction of hydrophobic groups, the water absorption efficiency of the water-absorbing agent is reduced, and water cannot be effectively absorbed. In order to solve these problems, some researchers solved t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H21/22D21H17/55D21H17/66D21H17/06D21H17/25D21H17/37
Inventor 邓强
Owner SUZHOU HENGKANG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products