Epoxy resin-base paint for flexible or thin-paint solar cells and preparation method thereof

A technology of solar cells and epoxy resin, applied in the direction of epoxy resin coatings, coatings, etc., can solve the problem of low efficiency of solar cells

Inactive Publication Date: 2014-07-02
ZHONGYUAN ENGINEERING COLLEGE
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the optical resonance also causes the nanoparticles to absorb light, which means the solar cell will be less efficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) 8Kg glycidyl ether epoxy resin solution (solid content of epoxy resin is 10%) (Zhejiang Kaihua Chengxin Resin Co., Ltd.), viscosity regulator (N-methyl-2-pyrrolidone) 0.1Kg, 91.8995Kg N,N-dimethylformamide is mixed, processed in a high-speed emulsifier for 10-60 minutes, the rotation speed is 10000-100000 rpm, and processed into a uniformly mixed emulsion;

[0031] (2) Add 0.005Kg of acetone nano-aluminum powder in batches and traces continuously within 10-20 minutes under the same processing speed environment after the above mixed emulsion is processed;

[0032](3) The above emulsion is fully emulsified for 10-30 minutes after the nano-aluminum powder is completely added; (5) The above emulsion is filtered with a filter screen of 300 mesh or more to obtain an epoxy resin coating for flexible or thin film solar cells.

[0033] The coatings in this example were tested according to national standards QB / T2730.1-2005, QB / T2603-2007, GB / T13217.2-2009, GB / T 18724-2008 / IS...

Embodiment 2

[0035] (1) 9Kg glycidyl ester epoxy resin (solid content of epoxy resin is 5%) (Foshan Longxiang Resin Raw Material Co., Ltd.), viscosity modifier (N-methyl-2-pyrrolidone) 0.3Kg, with 10Kg ethanol, 20Kg acetone, and 60.6999Kg glycol ether acetate are prepared into a solution, processed in a high-speed emulsifier for 10-60 minutes at a speed of 10,000-100,000 rpm, and processed into a uniformly mixed emulsion;

[0036] (2) Add 0.0001Kg of acetone nano-aluminum powder in batches and continuously within 10-20 minutes under the same processing speed environment after the above mixed emulsion is processed;

[0037] (3) The above emulsion is fully emulsified for 10-30 minutes after the nano-aluminum powder is completely added; the above emulsion is filtered with a filter screen of more than 300 mesh to obtain an epoxy resin coating for flexible or thin-film solar cells.

Embodiment 3

[0039] (1) 10Kg glycidylamine epoxy resin (solid content of epoxy resin is 3%) (Foshan Longxiang Resin Raw Material Co., Ltd.), viscosity modifier (N-methyl-2-pyrrolidone) 0.8Kg, 25Kg Mix methyl ethyl ketone, 24.15Kg ethylene glycol ethyl ether, and 20Kg butyl acetate, process it in a high-speed emulsifier for 10-60 minutes at a speed of 10000-100000 rpm, and process it into a uniformly mixed emulsion;

[0040] (2) Add 0.05Kg of acetone nano-aluminum powder in batches and continuously within 10-20 minutes under the same processing speed after the processing of the above mixed emulsion is completed;

[0041] (3) The above emulsion is fully emulsified for 10-30 minutes after the nano-aluminum powder is completely added; the above emulsion is filtered with a filter screen of more than 300 mesh to obtain an epoxy resin coating for flexible or thin-film solar cells.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an epoxy resin-base paint for flexible or thin-film solar cells and a preparation method thereof. The paint is prepared from the following components in percentage by mass: 8-12% of epoxy resin solution (the solid content of epoxy resin is 1-10%), 0.0001-0.1% of nano aluminum powder, 0.1-1% of viscosity regulator and the balance of solvent. The product can be applied to the upper surface of the flexible or thin-film solar cell by a spray coating, silk screen printing, printing or any other technique to directly enhance the generating efficiency of the flexible or thin-film solar cell.

Description

technical field [0001] The invention relates to a coating for flexible or thin-film solar cells and a preparation method thereof. By using the coating to form a light-transmitting coating on the surface of the light-incident surface of the flexible or thin-film solar cell, the efficiency of the flexible or thin-film solar cell can be directly improved. Background technique [0002] All polymer compounds containing epoxy groups in the molecular structure are collectively referred to as epoxy resins. The cured epoxy resin has good physical and chemical properties, it has excellent bonding strength to the surface of metal and non-metal materials, good dielectric properties, small set shrinkage, good product dimensional stability, high hardness, It has good flexibility and is stable to alkalis and most solvents, so it is widely used in national defense and various sectors of the national economy for casting, impregnation, lamination, adhesives, coatings and other purposes. As f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
Inventor 张迎晨
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap