Ceramic wine bottle colored glaze and glaze spraying method

A ceramic wine bottle and colored glaze technology, which is applied in the field of ceramics, can solve the problems of blistering on the glaze surface, cracks on the glaze surface, and low quality, and achieve good waterproof and moisture-proof performance, keep the glaze dry, and good water repellency Effect

Active Publication Date: 2014-07-16
ANHUI YICAI GLASSWARE
View PDF6 Cites 23 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glaze has been widely used in people's daily life because of its good smoothness, but the surface of the glaze in the prior art is prone t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] A method for glazing a hydrophobic ceramic wine bottle color glaze. The glaze is made of the following raw materials in parts by weight (kg): bauxite 10, dolomite 4, zinc sulfate 6, magnesium sulfate 3, cobalt acetate 4, CaO9, MgO 2, BaO3, silicon carbide 2, graphite 1, SnO 2 4. Sc 2 o 3 2. Adhesive 13, appropriate amount of water;

[0014] Include the following steps:

[0015] 1) Roasting and grinding: Roast bauxite and dolomite at 490-510°C for 4-5 hours, and then add them to the ball mill together with other remaining raw materials. The weight percentage of water is required to be controlled at 35%. -45%, at 53-58℃, ball mill for 12-15 hours until the glaze particle size is 20-40μm;

[0016] 2) Heating and aging: put the glaze slurry in the tank, heat it to 55-65°C and keep it warm, and store it for 30-36 hours;

[0017] 3) Glaze spray: Spray the glaze slurry on the body of the ceramic wine bottle at 65-70°C, the thickness of the first spray glaze is 0.1mm-0.2mm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glaze spraying method for water-repellent ceramic wine bottle colored glaze. The ceramic wine bottle colored glaze is characterized in that the glaze material is prepared from the following materials in parts by weight: 10-12 parts of bauxite, 3-4 parts of dolomite, 5-6 parts of zinc sulfate, 2-3 parts of magnesium sulfate, 3-4 parts of cobalt acetate, 9-12 parts of CaO, 2-3 parts of MgO, 3-4 parts of BaO, 2-3 parts of silicon carbide, 1-2 parts of graphite, 3-4 parts of SnO2, 1-2 parts of Sc2O3, 13-14 parts of binder and a proper amount of water. The ceramic wine bottle glaze disclosed by the invention is smooth and fine in glaze, extremely good in hand feeling, has very good hydrophobicity, can prevent water from gathering on the glaze, can keep the glaze dry, and therefore, the ceramic wine bottle colored glaze has very good waterproof and moisture-resistant performances.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a method for glazing a water-repellent ceramic wine bottle color glaze. Background technique [0002] Glaze has been widely used in people's daily life because of its good smoothness, but the surface of the glaze in the prior art is prone to cracks, the surface of the glaze is uneven, and it is easy to sag. Bubbles, deformation of ceramic wine bottles, etc., the quality is not high. There is an urgent need to improve the glaze formula and process, improve the quality of the glaze surface, and increase the authenticity rate of the glaze. Contents of the invention [0003] The object of the present invention is to provide a method for glazing the water-repellent ceramic wine bottle color glaze with good surface gloss. [0004] The present invention takes following technical scheme: [0005] A method for glazing a hydrophobic ceramic wine bottle color glaze, characterized in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B41/86
Inventor 潘涛张平
Owner ANHUI YICAI GLASSWARE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap