Wall coating and preparation method

A paint and wall technology, applied in the field of wall paint and preparation, can solve the problems of poor environmental performance, high production cost, easy mold on the wall, etc., and achieve the effect of low production cost, low cost and good covering effect

Active Publication Date: 2014-08-06
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are more than 10 million tons of volatile organic compounds (VOC) emitted into the atmosphere from paints in the world every year, which is one of the main sources of air pollution. At present, the existing wall paints are usually easy to use during use. The following problems occur: it contains certain harmful substances such as formaldehyde and volatile organic compounds, and usually emits an unpleasant smell for a long time, and the environmental performance is poor, which brings lasting harm to people's bodies. inconvenience to consumers
[0003] There are also some green paints on the market at present, but the production cost is high and cannot meet the huge market demand. Therefore, it is urgent to find a cheap, non-toxic, environmentally friendly and environmentally friendly paint that has antibacterial effects and does not have a negative impact on human health. wall paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wall coating and preparation method
  • Wall coating and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] It is characterized in that the coating is composed of the following parts by weight:

[0026] Weigh 15kg of bamboo pulp, 30kg of rice straw pulp, and 15kg of rag pulp, mix them evenly, break them with a beating machine, add 300kg of water, dilute them into the reactor, add 1.5kg of defoamer, and rotate at 700-900 rpm Stir for 15 minutes under the conditions of, then add 100kg of titanium dioxide, 230kg of pure acrylic emulsion, and stir for 20-30 minutes under the condition of rotation speed of 500-1200 rpm, and then sand to the material fineness below 50um; Put 35kg vegetable gum composition, 1.5kg defoamer, 4kg plant extract into the reactor, stir for 15-30 minutes at 400-800 revolutions per minute; finally adjust with 1.5kg high alkalinity complex alkali The PH value is 6-7, and it is qualified product after passing through 200 mesh sieve, and it is packaged and stored.

[0027] Preparation of vegetable gum composition: weigh 35 kg of couma gum and 35 kg of stone gum an...

Embodiment 2

[0030] Weigh 15kg of bamboo pulp, 30kg of rice straw pulp, and 15kg of rag pulp, mix them evenly, break them with a beating machine, add 300kg of water, dilute them into the reactor, add 1.5kg of defoamer, and rotate at 700-900 rpm Stir for 15 minutes under the condition of, then add 100kg of titanium dioxide, 230kg of polyvinyl acetate latex liquid, stir for 20-30 minutes under the condition of rotation speed of 500-1200 revolutions per minute, and then sand to the material fineness below 50um ; 35kg of vegetable gum composition, 1.5kg of defoamer, 4kg of plant extract into the reactor, stirring at 400-800 revolutions per minute for 15-30 minutes; finally 1.5kg of high alkalinity complex alkali Adjust the PH value to 6-7 and pass the 200-mesh sieve to be a qualified product, which is packaged and stored.

[0031] Preparation of vegetable gum composition: weigh 35 kg of couma gum and 35 kg of stone gum and mix the two to obtain the vegetable gum composition. Among them, couma gu...

Embodiment 3

[0034] Weigh 10kg of bamboo pulp, 20kg of rice straw pulp, and 10kg of rag pulp, mix them evenly, break them with a beating machine, add 200kg of water and dilute them into the reactor, add 1kg of defoamer, and rotate at 700-900 rpm. Stir for 15 minutes; then add 70kg of titanium dioxide, 180kg of pure acrylic emulsion, and stir for 20-30 minutes at a speed of 500-1200 revolutions per minute, and then sand to the material fineness below 50um; 30kg of plant Put the glue composition, 1kg defoamer, 2kg plant extract into the reaction kettle, stir for 15-30 minutes under the condition of 400-800 revolutions per minute; finally adjust the PH value to 6 with 1kg high alkalinity compound alkali -7. After passing through a 200-mesh sieve, it is a qualified product, which is packaged and stored.

[0035] Preparation of the vegetable gum composition: weigh 30 kg of couma gum and 30 kg of stone gum, and mix the two to obtain the vegetable gum composition. Among them, couma gum and stone fl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a wall coating. The coating comprises the following components by weight: 200-400 parts of water, 10-40 parts of pulp mixtures, 2-4 parts of foam killers, 50-150 parts of titanium dioxide, 100-350 parts of synthetic resin emulsion, 2-5 parts of acid-alkali modulation agents, 20-50 parts of vegetable gelatin compositions and 3-5 parts of plant extracts. According to the invention, the pulp mixtures are adopted, so that the cost is relatively low, and the technology is simple; the synthetic resin emulsion, the plant extracts and vegetable gelatin are cooperatively adopted for achieving the effects of mold prevention, desinsectization and sterilization, so that the wall coating has fresh smell; composite alkali with high alkalinity can be used for adjusting PH values, has the effects of emulsion breaking and coagulation improving, can form hydroxide precipitation with heavy metals to remove the heavy metals, and is good for health and environment protection; the coating is free from toxic substances of formaldehyde, benzene, ammonia and the like, and volatile toxic substances reach zero emission; the coating is an internal wall coating that is nontoxic, environment-friendly and low in manufacturing cost, has the antibacterial effect, and generates no adverse impacts on human health.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a wall coating and a preparation method. Background technique [0002] Coatings play an important role in the national economy and are indispensable in modern society. However, there are more than 10 million tons of volatile organic compounds (VOC) emitted into the atmosphere from paints in the world every year, which is one of the main sources of air pollution. At present, the existing wall paints are usually easy to use during use. The following problems occur: it contains certain harmful substances such as formaldehyde and volatile organic compounds, and usually emits an unpleasant smell for a long time, and the environmental performance is poor, which brings lasting harm to people's bodies. Consumers bring a lot of inconvenience. [0003] There are also some green paints on the market at present, but the production cost is high and cannot meet the huge market d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D131/04C09D5/14C09D7/12
Inventor 钱永兴
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap