High-temperature-resistant powder coating with good gloss-retention performance and production method thereof

A powder coating, high temperature resistant technology, used in powder coatings, polyester coatings, coatings, etc., can solve problems such as large gloss changes, bubbles, and shedding

Inactive Publication Date: 2014-08-06
ZHANGJIAGANG JIANGNAN POWDER COATING
View PDF3 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the improvement of people's living standards, all kinds of household appliances involved in life are constantly being updated to meet the various requirements of consumers. Among them, the existence of ovens in every household is closely related to our lives. The ovens need Powder coatings have relatively high requirements, but most of the powder coatings used in ovens in the prior art have the following problems: 1) Poor high temperature resistance, frequent peeling off and bubbles after surface coating, and relatively large gloss changes, 2) The powder coatings used in ovens in the prior art all contain solvents, which cause great environmental pollution and certain potential safety hazards; therefore, a new technical solution is urgently needed to solve the above technical problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant powder coating with good gloss-retention performance and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A high-temperature-resistant powder coating with good gloss retention performance, which contains the following components in parts by mass,

[0048] 58 parts of polyester resin;

[0049] 4 parts of TGIC curing agent;

[0050] 0.2 parts of wax powder;

[0051] 0.3 parts of organic soil;

[0052] 1.5 parts of ammonium polyphosphate temperature-resistant additive;

[0053] 0.3 part of phosphite antioxidant;

[0054] Sand texture agent 0.1 part;

[0055] 0.6 parts of carbon black;

[0056] 20 parts of precipitated barium sulfate;

[0057] 2 parts of asbestos powder;

[0058] Wherein, the acid value of the polyester resin is 30;

[0059] The high temperature resistant auxiliary agent is ammonium polyphosphate temperature resistant auxiliary agent;

[0060] The antioxidant is a phosphite antioxidant.

Embodiment 2

[0062] A high-temperature-resistant powder coating with good gloss retention performance, which contains the following components in parts by mass,

[0063] 62 parts of polyester resin;

[0064] 5 parts of TGIC curing agent;

[0065] 0.5 parts of wax powder;

[0066] 1 part organic soil;

[0067] 2.5 parts of ammonium polyphosphate temperature-resistant additive;

[0068] 0.6 part of phosphite antioxidant;

[0069] Sand texture agent 0.3 parts;

[0070] 1.2 parts of carbon black;

[0071] 30 parts of precipitated barium sulfate;

[0072] 5 parts of asbestos powder;

[0073] Wherein, the acid value of the polyester resin is 35.

[0074] The high temperature resistant additive is ammonium polyphosphate temperature resistant additive

[0075] The antioxidant is a phosphite antioxidant.

Embodiment 3

[0077] A high-temperature-resistant powder coating with good gloss retention performance, which contains the following components in parts by mass,

[0078] 59 parts of polyester resin;

[0079] 4.5 parts of TGIC curing agent;

[0080] 0.3 parts of wax powder;

[0081] 0.5 parts of organic soil;

[0082] 2 parts of ammonium polyphosphate temperature-resistant additive;

[0083] 0.4 part of phosphite antioxidant;

[0084] Sand texture agent 0.19 parts;

[0085] 1 part carbon black;

[0086]28.11 parts of precipitated barium sulfate;

[0087] 4 parts of asbestos powder;

[0088] Wherein, the acid value of the polyester resin is 30-35.

[0089] The high temperature resistant additive is ammonium polyphosphate high temperature resistant additive

[0090] The antioxidant is a phosphite antioxidant.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high-temperature-resistant powder coating with good gloss-retention performance. The high-temperature-resistant powder coating is characterized by comprising the following constituents in mass percentage: 58-62 parts of polyester resin, 4-5 parts of TGIC (Triglycidyl Isocyanurate) curing agent, 0.2-0.5 part of wax powder, 0.3-1 part of organic soil, 1.5-2.5 parts of ammonium polyphosphate temperature resistant auxiliary, 0.3-0.6 part of phosphite ester antioxidant, 0.1-0.3 part of a sand ripple agent, 0.6-1.2 parts of carbon black, 20-30 parts of precipitated barium sulphate, and 2-5 parts of asbestos powder.

Description

technical field [0001] The invention relates to powder coatings, in particular to a high-temperature-resistant powder coating with good gloss retention and a production method thereof. Background technique [0002] With the improvement of people's living standards, all kinds of household appliances involved in life are constantly being updated to meet the various requirements of consumers. Among them, the existence of ovens in every household is closely related to our lives. The ovens need Powder coatings have relatively high requirements, but most of the powder coatings used in ovens in the prior art have the following problems: 1) Poor high temperature resistance, frequent peeling off and bubbles after surface coating, and relatively large gloss changes, 2) The powder coatings used in ovens in the prior art all contain solvents, which cause serious environmental pollution and certain potential safety hazards; therefore, a new technical solution is urgently needed to solve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D7/12C09D5/03B29C47/92B29B7/00B29C48/92
CPCB29B7/005B29B7/72C09K21/04C09D5/03C09D167/00C09D7/40B29C48/92B29C2948/92704B29C2948/92114B29C2948/9259C08K3/04C08K3/30C08K3/32C08L91/06
Inventor 邓福义李德
Owner ZHANGJIAGANG JIANGNAN POWDER COATING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com