A formula for producing wood-plastic materials by recycling waste plastic resources and its preparation method
A waste plastic and wood-plastic technology, applied in the field of wood-plastic boards and their preparation, can solve problems such as poor surface wear resistance, increased process difficulty, and reduced application life, achieving excellent performance, high production efficiency, and easy operation.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0068] Weigh the raw materials according to the following weight ratio:
[0069] Recycled PVC resin powder: 100 copies;
[0070] Wood fiber powder: 60 parts;
[0071] Calcium filler: 60 parts;
[0072] Plasticizer: 6 parts;
[0073] Stabilizer: 6 parts;
[0074] PE wax: 0.9 parts;
[0075] Stearic acid: 1.2 parts;
[0076] Foaming regulator: 8 parts;
[0077] Foaming agent: 1.5 parts;
[0078] Dispersant: 0.2 parts.
[0079] Then use the following methods to prepare wood-plastic panels:
[0080] 1) Mix wood fiber powder and calcium filler at high speed for 30 minutes at 1200rpm;
[0081] 2) Add the above mixture to stearic acid, PE wax, and dispersant, heat it to 150°C, and mix it thoroughly with a stirring mixer;
[0082] 3) Add the recycled PVC resin powder to the plasticizer and stabilizer, heat to 150°C, use a stirring mixer to fully mix, and then enter the mixture prepared in step 2), and then add the foaming regulator and the foaming agent to fully mix, Cool to 70℃ and release;
[0083] 4)...
Embodiment 2
[0088] Weigh the raw materials according to the following weight ratio:
[0089] Recycled PVC resin powder: 100 copies;
[0090] Wood fiber powder: 40 parts;
[0091] Calcium filler: 90 parts;
[0092] Plasticizer: 6 parts;
[0093] Stabilizer: 6 parts;
[0094] PE wax: 1.3 parts;
[0095] Stearic acid: 0.8 parts;
[0096] Foaming regulator: 5 parts;
[0097] Foaming agent: 1.0 part;
[0098] Dispersant: 0.1 part.
[0099] Then use the following methods to prepare wood-plastic panels:
[0100] 1) Mix wood fiber powder and calcium filler at high speed for 40 minutes at a speed of 1200rpm;
[0101] 2) Add the above mixture to stearic acid, PE wax, and dispersant, heat it to 130°C, and mix it thoroughly with a stirring mixer;
[0102] 3) Add recycled PVC resin powder to plasticizers and stabilizers, heat to 130°C, use a stirring mixer to fully mix, and then enter the mixture prepared in step 2), and then add foaming regulator and foaming agent to fully mix, Cool down to 80℃ and release;
[0103] 4)...
Embodiment 3
[0108] Weigh the raw materials according to the following weight ratio:
[0109] Recycled PVC resin powder: 100 copies;
[0110] Wood fiber powder: 50 parts;
[0111] Calcium filler: 80 parts;
[0112] Plasticizer: 5 parts;
[0113] Stabilizer: 5 parts;
[0114] PE wax: 1.0 part;
[0115] Stearic acid: 1.0 part;
[0116] Foaming regulator: 6 parts;
[0117] Foaming agent: 1.2 parts;
[0118] Dispersant: 0.15 parts.
[0119] Then use the following methods to prepare wood-plastic panels:
[0120] 1) Mix the wood fiber powder and the calcium filler at a high speed for 50 minutes at a speed of 1000 rpm;
[0121] 2) Add the above mixture to stearic acid, PE wax, and dispersant, heat it to 140°C, and mix it thoroughly with a stirring mixer;
[0122] 3) Add recycled PVC resin powder to plasticizers and stabilizers, heat to 140°C, use a stirring mixer to fully mix, and then enter the mixture prepared in step 2), and then add foaming regulator and foaming agent to fully mix, Then cool to 70~80℃ and rele...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com