Red ZrO2-coated gamma-Ce2S3 pigment and preparation method thereof

A -ce2s3, wrapping technology, applied in the field of wrapping γ-Ce2S3 red material and its preparation, can solve the problems of unseen pigments, etc., to broaden the application field, improve product quality, improve anti-oxidation performance and chemical stability Effect

Active Publication Date: 2014-08-20
JINGDEZHEN CERAMIC INSTITUTE
View PDF2 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, no preparation of ZrO 2 Encapsulated γ-Ce 2 S 3 coloring material report

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Red ZrO2-coated gamma-Ce2S3 pigment and preparation method thereof
  • Red ZrO2-coated gamma-Ce2S3 pigment and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The embodiment of the present invention adopts commercially available γ-Ce 2 S 3 , first pretreatment, that is, washing twice in deionized water and ethanol to remove possible impurities on the surface, then drying at 50 ° C, and then grinding the resulting powder in an agate mortar and sieving to obtain Pretreated Ce 2 S 3 colorant, and for the following ZrO 2 Encapsulated γ-Ce 2 S 3 Preparation of red material.

[0024] A kind of ZrO of the embodiment of the present invention 2 Encapsulated γ-Ce 2 S 3 The preparation method of red material, its step is as follows:

[0025] (1) Preparation of raw material solution

[0026] Pigment suspension: γ-Ce 2 S 3 Disperse the coloring material in 30mL deionized water, adjust its pH value to 8.0-13.0, and disperse it ultrasonically for 20 minutes to obtain a suspension; add the dispersant to the mixed solution of 10mL distilled water and 10mL ethanol and homogenize it, and then add it to the above suspension In the p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a red ZrO2-coated gamma-Ce2S3 pigment comprising a gamma-Ce2S3 chromogen core and a ZrO2 shell coated outside the chromogen core. In addition, the invention also discloses a preparation method of the red ZrO2-coated gamma-Ce2S3 pigment. According to the invention, the red ZrO2-coated gamma-Ce2S3 pigment is firstly prepared by using a homogeneous precipitation method, the breakthrough of a preparation technology of the red coated gamma-Ce2S3 pigment is realized, and the red ZrO2-coated gamma-Ce2S3 pigment is remarkably improved on oxidation resistance and chemical stability, favorable in dispersing performance, widened in application field and beneficial to popularization and development of a production technology.

Description

technical field [0001] The invention relates to the technical field of inorganic pigments, in particular to an encapsulated γ-Ce 2 S 3 Red material and preparation method thereof. Background technique [0002] Red has bright, bright, warm, noble, gorgeous and other qualities. Its connotations are rich and colorful, symbolizing life, joy, harvest, auspiciousness, wishful thinking and all good things. It is one of the favorite colors of all nations in the world. It plays a pivotal role in the production and application of decorative materials. Red pigments are usually divided into two categories: organic red pigments and inorganic red pigments. Organic red pigments have bright color and strong tinting power; however, their hiding power, thermal stability, light stability and ability to resist ultraviolet radiation are poor, so it is difficult to completely replace inorganic red pigments. However, the inorganic red pigments of the prior art mostly contain heavy metal elemen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09C1/00C09C3/04C09C3/06
Inventor 李月明刘顺国王竹梅沈宗洋谢志翔廖润华
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com