Preparation technology for edge-sealing strip subjected to co-extrusion molding

A preparation process and co-extrusion molding technology, which is applied in the field of preparation of co-extrusion edge banding, can solve the problems of reducing production efficiency, increasing production processes, wasting hot melt adhesive, etc.

Inactive Publication Date: 2014-09-03
DONGGUAN HUALI INDUSTRIES CO LTD
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the existing edge banding is coated with hot melt adhesive, it is necessary to apply the treatment agent first, and then apply the hot melt adhesive. There is a gap between the base material layer of the edge banding and the hot melt adhesive, resulting in a layered structure. The phenomenon of wasting hot melt adhesive often occurs in the process, and it is necessary to change the color of hot melt adhesive when coating edge strips of different colors, which increases the production process and reduces production efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A preparation process for co-extruded edge banding, which comprises the following process steps:

[0045] A. Co-extrude the edge banding strip base material layer raw material and the hot melt adhesive layer raw material of the same color to have the edge banding strip with the base material layer and the hot melt adhesive layer, and the edge banding strip is seamlessly connected with the product to be edge banded; The raw material of the base material layer of the edge band is ABS, and the extrusion temperature of the raw material of the base material layer of the edge band is specifically: the temperature of the first zone of the barrel is 170°C, the temperature of the second zone of the barrel is 180°C, and the temperature of the third zone of the barrel is 170°C. The temperature of the hot melt adhesive layer is 195°C, the temperature of the mold area is 205°C; the extrusion temperature of the hot melt adhesive layer raw material is as follows: the temperature of the...

Embodiment 2

[0053] The difference between this embodiment and Example 1 is: A, co-extrude the edge banding strip with the base material layer and the hot melt adhesive layer with the edge banding strip base material layer raw material and the hot melt adhesive layer raw material of the same color; The raw material of the base material layer of the edge banding strip is ABS, and the extrusion temperature of the raw material material layer of the edge banding strip is specifically: the temperature of the first zone of the barrel is 173°C, the temperature of the second zone of the barrel is 183°C, and the temperature of the third zone of the barrel is The temperature is 198°C, and the temperature in the mold area is 210°C; the extrusion temperature of the hot melt adhesive layer raw material is as follows: the temperature in the first area of ​​the barrel is 68°C, the temperature in the second area of ​​the barrel is 72°C, and the temperature in the third area of ​​the barrel The temperature ...

Embodiment 3

[0058] The difference between this embodiment and embodiment 1 is: a preparation process of co-extruded edge banding, which includes the following process steps:

[0059] A. Co-extrude the edge banding strip base material layer raw material and hot melt adhesive layer raw material of the same color to have the edge banding strip with the base material layer and the hot melt adhesive layer; the raw material of the edge banding strip base material layer is ABS, and the edge banding The extrusion temperature of the raw material of the strip substrate layer is as follows: the temperature of the first zone of the barrel is 175°C, the temperature of the second zone of the barrel is 185°C, the temperature of the third zone of the barrel is 200°C, and the temperature of the mold zone is 220°C; The extrusion temperature of the raw material of the hot melt adhesive layer is as follows: the temperature of the first area of ​​the barrel is 70°C, the temperature of the second area of ​​the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of preparation of edge-sealing strips, and concretely relates to a preparation technology for an edge-sealing strip subjected to co-extrusion molding. The preparation technology comprises the following technological steps: step A, performing co-extrusion on a substrate-layer raw material and a hot-melt-adhesive-layer raw material possessing a same color, so as to prepare the edge-sealing strip possessing the substrate layer and the hot-melt-adhesive layer; B, cooling and curing the edge-sealing strip; and C, for usage, using hot wind or a hot gas or laser to melt the hot-melt-adhesive layer of the edge-sealing strip, so as to enable the face of the edge-sealing strip, which possesses the hot-melt-adhesive layer, to be adhered to a product to be subjected to edge sealing. The adhesive force of the hot-melt-adhesive layer is high, and degumming phenomenon is avoided. By employing hot wind or the hot gas or laser for melting the hot-melt-adhesive layer, edge sealing is performed. Seamless connection between the edge-sealing strip and a product to be subjected to edge sealing, such as medium density fiberboards, shaving boards, plywood and other artificial plates, is realized, and a hot melt adhesive is not needed for coating, so that a production process of coating a hot melt adhesive is saved, the product quality and the production efficiency are substantially improved, the production and application cost is reduced, and the preparation technology is relatively suitable for industrialized production.

Description

technical field [0001] The invention relates to the technical field of edge banding preparation, in particular to a preparation process of co-extruded edge banding. Background technique [0002] Edge banding is a material for protecting, decorating and beautifying the section of furniture panels. Its main function is to seal the section of the panel so as to prevent the panel from being damaged by the environment and unfavorable factors during use. Unique color and texture design and other decorations make the applied furniture panel products more textured and three-dimensional. [0003] At present, the edge banding strips used for edge banding in the furniture industry mainly include wood, paper, plastic and other materials. There are wooden strips and veneers for wooden edge banding. The edge banding is made of processed wooden materials. The advantage is that it is more convenient to glue and process, but the source of materials is limited, the cost is high, and the colo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C47/00B29C47/92C09J123/08C09J11/06C09J11/08B29C48/92B29C48/875
CPCB29C47/92B29C2947/92571B29C2947/92647B29C48/92C09J123/08B29C2948/92209B29C48/875B29C2948/92704B29C2948/92571B29C2948/92647B29C2948/92895
Inventor 谢志昆沈利达雷厚根
Owner DONGGUAN HUALI INDUSTRIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products