Granite veneer stone and its production method

A production method and technology of veneer stone, applied in the field of artificial stone, can solve problems such as short color duration, unstable pattern of veneer stone, fading of paint, etc.

Active Publication Date: 2016-02-24
浙江泰基涂料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] When using natural stone for decoration, because the natural stone is heavy, it is very difficult to transport and construct, and the mining of natural stone is not conducive to the protection of ecology and the environment; The pattern is not stable, the hand feel is poor, and because the paint is exposed to the external environment, it is easy to cause the paint to fade after being exposed to the rain and the sun, and the color duration is too short

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Granite veneer stone and its production method
  • Granite veneer stone and its production method
  • Granite veneer stone and its production method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] The preparation steps of colorful granite paint:

[0046] (1) Preparation of GTS colloidal solution: slowly add GTS powder to deionized water, centrifuge and disperse at 1500r / min for 30 minutes to obtain a GTS colloidal solution, where the mass percentage of GTS powder is 93.5% and the mass percentage of deionized water is 6.5 %;

[0047] (2) Preparation of colorful base paint: 40% deionized water, 0.6% dispersant 120V, 0.1% wetting agent G-396, 0.2% defoamer G, which accounts for the mass percentage of the total colorful base paint -298, and 0.8% inorganic mineral gel were added to the dispersion tank and centrifuged at a speed of 300r / min for 1 min, and then 10% 4000 mesh kaolin and 0.7% cellulose HS-30000 were added in sequence, and the rotation speed was maintained to continue centrifugal dispersion. 5min, then add 0.2% AMP-95, and slowly increase the speed to 1000r / min during the feeding process, continue to disperse for 30min, and finally add 0.6% of the film-forming...

Embodiment 2

[0063] Table 7 shows the components and preparation steps and conditions of the color grain granite coating of Example 2.

[0064]

[0065] Table 8 shows the preparation steps and conditions of the granite veneer in Example 1.

[0066]

Embodiment 3

[0068] Table 9 shows the components and preparation steps and conditions of the color grain granite paint in Example 3.

[0069]

[0070] Table 10 shows the preparation steps and conditions of the granite veneer in Example 3.

[0071]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a granite veneer stone and a preparation method thereof. The granite veneer stone is characterized in that a protective layer is a nano fluorocarbon paint; a color grain granite coating consists of particles and a continuous phase emulsion; each particle consists of a GTS colloidal solution and a colorful base paint; the preparation method comprises the following steps: firstly coating a seal primer on a base material, then coating the color grain granite coating on the seal primer, then coating the nano fluorocarbon paint on the seal primer again, and drying to form a granite veneer stone finished product.

Description

Technical field [0001] The invention relates to the field of artificial stone, more specifically, it relates to a granite veneer stone and a manufacturing method thereof. Background technique [0002] At present, when granite decoration is applied to the building wall, natural granite stone is directly pasted on the surface of the building wall, or colorful paint is sprayed on the composite coil, and then the composite coil is pasted on the surface of the building. [0003] When natural stone is used for decoration, the heavy natural stone makes transportation and construction very difficult, and the mining of natural stone is not conducive to ecological and environmental protection; when colorful paint is sprayed on the composite coil, such a veneer stone The pattern is unstable and the hand feel is poor. Moreover, because the paint is exposed to the external environment, it is easy to cause the paint to fade and the color lasts too short. Summary of the invention [0004] In view...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/077B32B37/02C09D133/00C09D5/29
Inventor 周航帆
Owner 浙江泰基涂料有限公司