A kind of nizn soft magnetic ferrite and preparation method thereof

A technology of soft ferrite and soft ferrite, which is applied in the direction of magnetism of inorganic materials, to achieve the effects of reducing material stress, increasing anisotropy constant, and optimizing crystal structure

Active Publication Date: 2016-06-08
ZHAOQING CHAMPION FERRITE TECH
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a roller kiln for the common shortage of soft ferrite materials for SMD power inductors in the prior art that cannot simultaneously have high magnetic permeability, high BS, high strength and high thermal shock resistance. Preparation method of sintering and NiZn soft ferrite junction meeting the performance requirements of SMD power inductors

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nizn soft magnetic ferrite and preparation method thereof
  • A kind of nizn soft magnetic ferrite and preparation method thereof
  • A kind of nizn soft magnetic ferrite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] According to the invention figure 1 The shown sintering temperature curves embody the present invention, but the present invention is not limited to these examples.

[0023] (1) Primary batching: take the raw material by weighing the composition ratio described in Table 1, the secondary component Bi 2 o 3 It is also added at the time of batching.

[0024] (2) Primary ball milling: dry milling in a vibration ball mill for 60-120 minutes.

[0025] (3) Pre-burning: The powder after primary ball milling is pre-fired in a pusher kiln at a temperature of 940±20°C and a holding time of 120-180 minutes.

[0026] (4) Secondary ingredients: add the selected de-Bi according to the ratio of the auxiliary ingredients 2 o 3 Other trace modifying elements.

[0027] (5) Secondary ball milling: The powder after secondary batching is subjected to wet ball milling for 5-8 hours, and the particle size of the slurry is controlled at 1-1.5 μm.

[0028] (6) Spray-drying granulation: ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A NiZn soft magnetic ferrite and a preparation method thereof, the NiZn soft magnetic ferrite includes main components and auxiliary components. The main components are ferric oxide, nickelous oxide, zinc oxide, copper oxide, manganese carbonate, magnesium oxide; the secondary components include bismuth oxide, calcium carbonate, silicon dioxide, boron nitride, titanium boride, yttrium oxide ( rare earth oxides). The material obtained by the preparation method has high magnetic permeability, high BS, high strength and high thermal shock resistance, and meets the performance requirements of soft ferrite materials for SMD power inductors.

Description

technical field [0001] The invention belongs to the technical field of soft magnetic ferrite, and in particular relates to a nickel-zinc ferrite with high magnetic permeability, high Bs, high strength and high thermal shock resistance for SMD power inductors and a preparation method thereof. Background technique [0002] Soft magnetic materials are mainly manganese-zinc and nickel-zinc ferrite, which are important electronic functional materials. Due to the characteristics of high magnetic permeability, high resistivity, and high frequency of use, nickel-zinc ferrite is widely used in computers, communications, and consumer electronics. Nowadays, electronic products are developing in the direction of flat, thin and surface mount, and the size of soft magnetic components is getting smaller and smaller. At the same time, the manufacturing process of SMD power inductors has adopted automatic assembly line production, especially the spot welding process, which has a great impact...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01F1/34C04B35/26C04B35/622
Inventor 廖晓舟
Owner ZHAOQING CHAMPION FERRITE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com