Waterproof building material

A technology for waterproof building materials and distilled water, which is applied in the field of waterproof building materials and can solve the problems of inability to construct, poor adhesive properties of waterproof building materials, and poor adhesive properties.

Inactive Publication Date: 2014-09-24
SINOMA CHENGDU ENERGY TECH
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the waterproof building materials used in the construction industry have poor adhesive properties and cannot be constructed at freezing temperatures; construction in freezing temperature environments does not take measures to improve their adhesive properties, and tiles cannot be placed on the construction surface. Marble, granite and other decorative materials
At present, the waterproof building materials used in the construction industry have poor adhesive properties and cannot be constructed at freezing temperatures; constructions in freezing temperature environments do not adopt measures to improve their adhesive properties, and tiles and marble cannot be pasted on the construction surface , granite and other decorative materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] A waterproof building material, characterized in that it is composed of the following components: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, tar-free asphalt, triethanolamine, expanded perlite, silica, sodium silicate, alumina, and distilled water.

[0058] The said waterproof building material is characterized in that the material consists of the following parts by weight:

[0059] 20-40 parts of magnesium oxide;

[0060] 35-55 parts of quartz sand;

[0061] 15-20 parts of acrylic emulsion;

[0062] 20-55 parts of polyurethane;

[0063] 25-40 parts of tar-free pitch;

[0064] 30-45 parts of triethanolamine;

[0065] 20-35 parts of expanded perlite;

[0066] 5-15 parts of silicon oxide;

[0067] 25-35 parts of sodium silicate;

[0068] 25-35 parts of alumina;

[0069] 20-65 parts of distilled water.

Embodiment 2

[0071] A waterproof building material, characterized in that it is composed of the following components: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, tar-free asphalt, triethanolamine, expanded perlite, silica, sodium silicate, alumina, and distilled water.

[0072] The said waterproof building material is characterized in that the material consists of the following parts by weight:

[0073] 20-40 parts of magnesium oxide;

[0074] 35-55 parts of quartz sand;

[0075] 15-20 parts of acrylic emulsion;

[0076] 20-55 parts of polyurethane;

[0077] 25-40 parts of tar-free pitch;

[0078] 30-45 parts of triethanolamine;

[0079] 20-35 parts of expanded perlite;

[0080] 5-15 parts of silicon oxide;

[0081] 25-35 parts of sodium silicate;

[0082] 25-35 parts of alumina;

[0083] 20-65 parts of distilled water.

[0084] The said waterproof building material is characterized in that the material consists of the following parts by weight:

[0085] 20 parts of magnesium oxide;

[0086]...

Embodiment 3

[0097] A waterproof building material, characterized in that it is composed of the following components: magnesium oxide, quartz sand, acrylic emulsion, polyurethane, tar-free asphalt, triethanolamine, expanded perlite, silica, sodium silicate, alumina, and distilled water.

[0098] The said waterproof building material is characterized in that the material consists of the following parts by weight:

[0099] 20-40 parts of magnesium oxide;

[0100] 35-55 parts of quartz sand;

[0101] 15-20 parts of acrylic emulsion;

[0102] 20-55 parts of polyurethane;

[0103] 25-40 parts of tar-free pitch;

[0104] 30-45 parts of triethanolamine;

[0105] 20-35 parts of expanded perlite;

[0106] 5-15 parts of silicon oxide;

[0107] 25-35 parts of sodium silicate;

[0108] 25-35 parts of alumina;

[0109] 20-65 parts of distilled water.

[0110] The said waterproof building material is characterized in that the material consists of the following parts by weight:

[0111] 35 parts of magnesium oxide;

[0112]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the waterproof building material field, and more specifically relates to design and manufacture fields of a waterproof material, and especially relates to the waterproof building material. The waterproof building material is composed of magnesium oxide, quartz sand, an acrylic acid emulsion, polyurethane, tar-free pitch, triethanolamine, expanded perlite, silicon oxide, sodium silicate, alumina and distilled water.

Description

technical field [0001] The invention belongs to the field of waterproof building materials, in particular to the field of design and manufacture of waterproof materials, in particular to a waterproof building material. Background technique [0002] In the prior art, the enclosure structure of the building should prevent the infiltration of rainwater, snowwater and groundwater; it should prevent the erosion of moisture, steam and other harmful gases and liquids in the air; the separation structure should prevent the seepage of water supply and drainage . These anti-penetration, leakage and erosion materials are collectively referred to as waterproof materials. [0003] Building waterproofing is the measures taken from the building materials and structure to prevent water from penetrating certain parts of the building. Waterproofing is mostly used in roofs, underground buildings, underground parts of buildings, inner chambers and water storage structures that need to be wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26
Inventor 付伟峰窦涛
Owner SINOMA CHENGDU ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com