B06-grade autoclaved sand aerated concrete block prepared by adding saponin air entraining agents

A saponin-type air-entraining agent and air-entraining concrete technology, applied in ceramic products, applications, household appliances, etc., can solve the problems of low slurry water-material mixing ratio, low qualified rate of block products, poor pouring stability, etc. The effect of sound absorption and sound insulation is good, the masonry strength utilization coefficient is large, and the production energy consumption is low.

Active Publication Date: 2014-11-05
FUZHOU UNIV
View PDF1 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in the production process of aerated concrete, there are generally low slurry-water-material mix ratios, poor pouring stability, and easy occurrence of slurry mold collapse and green body shrinkage. Block products generally have low pass rate, high bulk density, and low compressive strength. , Large and uneven pores, less pores, high thermal conductivity, short fire resistance limit, poor durability, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • B06-grade autoclaved sand aerated concrete block prepared by adding saponin air entraining agents
  • B06-grade autoclaved sand aerated concrete block prepared by adding saponin air entraining agents

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] According to the formula in Table 1, each raw material was quantitatively weighed, and 1354 kg of machine-made sand and weathered sand mixture, 48 kg of gypsum and 850 kg of surface water were first poured into the pouring pool, and stirred to form a mortar slurry, and then 293 kg of lime, Mix 251 kg of cement and the rest with water, stir for a certain time, and control the temperature of the slurry. When the temperature is ≥40°C, add water-soluble aluminum powder paste (1.43 kg in terms of aluminum) and air-entraining agent water (based on saponin 0.27 kg), stirring for a certain time to control the degree of expansion of the slurry, when the degree of expansion ≥ 36 cm, the inner volume of the slurry injection is 3.24 m 3 After the pouring is completed, the mold is moved to the static parking room for maintenance for a certain period of time. After the green body meets the solidification requirements, it is moved out of the static parking room. After cutting and formi...

Embodiment 2

[0042] According to the formula in Table 1, the raw materials were weighed quantitatively, and 1339 kg of river sand, 49 kg of gypsum and 850 kg of river water were first poured into the pouring pool, and stirred to form a mortar slurry, and then 273 kg of lime, 270 kg of cement and the remaining Mix water, stir for a certain time, and control the slurry temperature. When the temperature is ≥ 40°C, pour 1.41 kg of aluminum powder and air-entraining agent powder (0.25 kg in terms of saponin) directly, and stir for a certain time to control the expansion of the slurry degree, when the expansion degree is ≥36 cm, the inner volume of slurry injection is 3.24 m 3 After the pouring is completed, the mold is moved to the static parking room for maintenance for a certain period of time. After the green body meets the solidification requirements, it is moved out of the static parking room. After cutting and forming according to the product specifications, the mold is freed, and the gree...

Embodiment 3

[0045] According to the formula in Table 1, the raw materials were quantitatively weighed, and 1335 kg of sea sand, 50 kg of gypsum and 850 kg of seawater were first poured into the pouring pool, and stirred to form a mortar slurry, and then 251 kg of lime, 291 kg of cement and the remaining Mix water in a certain amount, stir for a certain time, control the temperature of the slurry, when the temperature is ≥40°C, add water-soluble aluminum powder paste (1.35 kg as aluminum), air-entraining agent powder (0.23 kg as saponin) and water 1.8 kg of the suspension formed, stirred for several times to control the degree of expansion of the slurry, when the degree of expansion ≥ 36 cm, the inner volume of the slurry injection is 3.24 m 3 After the pouring is completed, the mold is moved to the static parking room for maintenance for a certain period of time. After the green body meets the solidification requirements, it is moved out of the static parking room. After cutting and formin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a B06-grade autoclaved sand aerated concrete block prepared by adding saponin air entraining agents. The autoclaved aerated concrete block is prepared by using cement, lime and sand as main raw materials, doping gas generating agents, regulating agents and air entraining agents, and carrying out hydration reaction, mold forming by pouring, blank forming by procuring, forming by cutting, autoclaved curing and out-kettle processing. The dry density, compressive strength, mean pore diameter and percent of pass of the product are respectively less than 596kg / m<3>, more than 5.12MPa, less than 0.45mm and more than 97%. By adding a small quantity of saponin concrete air entraining agents, the ratio of water to material, unit aluminium powder gas evolution and pouring stability in the production process and the volume, strength and quality of the product can be obviously increased. The block is novel in conception, rich in raw materials, simple in process and low in cost, is convenient to implement and has greater generalization performance. The block is an environment-friendly and energy-saving wall material and can be applied to processing and construction of non-load-bearing walls, wallboards and roofing boards of buildings.

Description

technical field [0001] The invention relates to a B06 grade autoclaved sand aerated concrete block prepared by adding a saponin air-entraining agent, relates to green chemical preparation of aerated concrete, and belongs to the fields of novel environment-friendly fine chemical materials and green, environment-friendly and energy-saving building materials. Background technique [0002] The development of new wall materials is a strategic demand for promoting the sustainable and healthy development of my country's economic society and building an ecological country. Air-entrained concrete is a new type of green environmental protection and energy-saving material. It refers to the main raw materials of calcareous and siliceous materials, mixed with air-generating agents, and formed by hydration reaction, pouring molding, pre-curing cutting, autoclaving and other processes. The porous new wall material is a new type of environmental protection and energy-saving building materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/02C04B24/10
Inventor 陈剑锋陈浩李娜
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com