Modified polyurethane grouting material and preparation method and application thereof

A grouting material, polyurethane technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of low strength of the consolidated body, complicated operation process, pollution of the environment, etc., and achieve high strength and penetration of the foamed consolidated body. Good performance and low cost

Active Publication Date: 2014-11-12
CHENGDU UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high cost, the pollution of some admixtures to the environment, the complicated operation process,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified polyurethane grouting material and preparation method and application thereof
  • Modified polyurethane grouting material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0015] The present invention provides a method for preparing a modified polyurethane grouting material, wherein the method includes the following steps:

[0016] Step 1: contact and mix diluent, isocyanate compound, water and Portland cement to obtain component A;

[0017] Contact and mix the polymerized alcohol, foam stabilizer and catalyst to obtain component B;

[0018] Step 2: Contact and mix component A and component B.

[0019] Among them, in step 1, the process of contact mixing to obtain component A can be carried out according to the following steps: firstly, the diluent is contacted and mixed with the isocyanate compound, and then the mixture 1 is contacted with water to obtain the mixture 2, and then the mixture 2 is mixed with silicon Component A is obtained by contacting with salt cement.

[0020] In step 1, the process of contacting and mixing to obtain component B can be carried out according to the following steps: firstly, the polymeric alcohol is contacted and mixed w...

Example Embodiment

[0050] Example 1-9

[0051] Examples 1-9 are used to illustrate the preparation method of the modified polyurethane grouting material provided by the present invention.

[0052] According to the content of the components listed in Table 2, the modified polyurethane grouting material was prepared.

[0053] In the mixing tank, first add the diluent, then add the isocyanate compound and mix well, then add water and mix well, finally add Portland cement and mix well under normal pressure to prepare component A.

[0054] In the mixing kettle, first add the polyalcohol, then add the foam stabilizer and stir evenly, and finally add the catalyst and stir and mix evenly to obtain component B.

[0055] Mix component A and component B uniformly to obtain a modified polyurethane grouting material.

[0056] Table 2

[0057]

[0058] In Examples 1-9, the specific selection of each component is as follows:

[0059] The selection of each component in Examples 1-5 is as follows: diluent (butyl acetate), is...

Example Embodiment

[0060] Example 6

[0061] The modified polyurethane grouting material was prepared according to the method of Example 1, except that the diluent was mixed with butyl acetate and dichloromethane in a weight ratio of 17:23.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method and application of a modified polyurethane grouting material. The preparation method comprises the following steps that firstly, diluents, isocyanate compounds, water and Portland cement make contact and are evenly mixed to obtain a component A, and polymeric alcohol, foam stabilizers and catalysts make contact and are evenly mixed to obtain a component B; secondly, the component A and the component B make contact and are evenly mixed. The preparation method and application of the modified polyurethane grouting material solve the problems of an existing pure polyurethane grouting material that the cost is high, induration strength is low, and an inorganic grouting material is long in setting time and slow in strength development, and the obtained material is low in cost, adjustable in setting time, high in foaming induration strength, good in permeability and environmentally friendly.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a modified polyurethane grouting material and its preparation method and application. Background technique [0002] The grouting material refers to pouring into the cracks and holes in the bottom layer, rocks or structures under a certain pressure to reduce extrusion leakage, improve the physical and mechanical properties of cracked rock mass, and increase the overall stability of the foundation of buildings and structures. Fluid materials that improve their impermeability, strength, and durability. There are many kinds of grouting materials, generally divided into inorganic grouting materials and organic grouting materials. [0003] Inorganic grouting materials are mainly cement slurry, cement mortar, superfine cement slurry, clay slurry, cement clay slurry, cement lime slurry, etc. Among them, cement slurry is currently the inorganic grouting material with the widest applica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L75/08C08K3/34C08G18/76C08G18/73C08G18/48C09K3/10C04B28/04C04B111/70
Inventor 叶长文陈礼仪王胜李之军袁进科霍宇翔袁学武韦猛
Owner CHENGDU UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap