A kind of binder for casting and preparation method thereof

A binder and polyisocyanate technology, which is used in casting molding equipment, casting molds, manufacturing tools, etc., can solve the problems of core high temperature heat resistance time and high temperature compressive strength, and limit the binder. Effect of heat resistance time and high temperature heat resistance strength

Active Publication Date: 2016-12-07
JINAN SHENGQUAN GRP SHARE HLDG CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the core strength prepared by this casting core binder provided by the prior art is relatively high, the high-temperature heat-resistant time and high-temperature compressive strength of the core prepared by this binder are poor, which limits The application of this adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0048] In the present invention, based on the parts by weight of the benzyl ether phenolic resin, the parts by weight of the graphene is preferably 0.1 to 10 parts, more preferably 0.5 to 8 parts, most preferably 1 part ~ 6 parts, most preferably 2 ~ 4 parts. In the present invention, the raw material for preparing graphene is preferably biomass carbon source. In the present invention, the preparation method of described graphene preferably comprises the following steps:

[0049] 1), under the action of a catalyst, the biomass carbon source is subjected to catalytic treatment to obtain a first intermediate product, and the catalyst includes one or more of manganese chloride salts, iron compounds, cobalt compounds and nickel compounds Several;

[0050] 2) Under the condition of protective gas, the first intermediate product is heated from the first temperature to the second temperature and then kept warm to obtain the second intermediate product, the first temperature is 20°C...

Embodiment 1

[0089] At 90° C., hydrolyzing corncobs in sulfuric acid for 10 minutes to obtain lignocellulose, the mass of the sulfuric acid being 3% of the mass of the corncobs;

[0090] At 70°C, the lignocellulose was subjected to acidic sulfite treatment for 1 hour to obtain porous cellulose, the pH value in the acidic sulfite treatment process was 1, the acid was sulfuric acid, and sulfite It is magnesium sulfite, the quality of the sulfuric acid is 4% of the quality of the lignocellulose, and the liquid-solid ratio is 2:1.

[0091] The obtained porous cellulose is bleached with hydrogen peroxide, the mass of the hydrogen peroxide is 5% of the mass of the porous cellulose, the bleaching temperature of the hydrogen peroxide bleaching is 100° C., and the bleaching time is 5 hours.

[0092] Stir the porous cellulose and manganese chloride at 20°C for 2 hours for catalytic treatment, the mass ratio of the manganese chloride and porous cellulose is 0.01:1; Drying at a low temperature to obt...

Embodiment 2

[0096] At 180°C, hydrolyzing corncobs in nitric acid for 10 hours to obtain lignocellulose, the mass of the nitric acid being 20% ​​of the mass of the corncobs;

[0097] At 180°C, the lignocellulose was subjected to acidic sulfite treatment for 6 hours to obtain porous cellulose, the pH value during the acidic sulfite treatment process was 7, the acid was sulfuric acid, and sulfite It is sodium sulfite, the quality of the sulfuric acid is 30% of the quality of the lignocellulose, and the liquid-solid ratio is 20:1.

[0098] The porous cellulose is bleached with hydrogen peroxide, the mass of the hydrogen peroxide is 5% of the mass of the porous cellulose, the bleaching temperature of the hydrogen peroxide bleach is 100° C., and the bleaching time is 5 hours.

[0099] Stir the porous cellulose and ferric nitrate at 180°C for 10 hours for catalytic treatment, the mass ratio of ferric nitrate and porous cellulose is 2:1; dry the obtained catalytically treated product at 120°C , ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a casting binder, which is prepared by reacting benzyl ether phenolic resin, polyisocyanate, epoxy resin, acrylate, organic compound and graphene; the organic compound includes diacid glycol esters One or more of compounds, alcohol compounds and hydrocarbon compounds. The invention provides a method for preparing a casting binder, comprising: reacting benzyl ether phenolic resin, polyisocyanate, epoxy resin, acrylate, organic compounds and graphene to obtain a casting binder; The organic compounds include one or more of diacid diol ester compounds, alcohol compounds and hydrocarbon compounds. The casting mold or casting core prepared by the foundry binder provided by the invention has longer high-temperature heat-resistant time and higher high-temperature heat-resistant strength.

Description

technical field [0001] The invention relates to the technical field of binders, in particular to a casting binder and a preparation method thereof. Background technique [0002] In the foundry industry, the cold box method is usually used to prepare the core. The cold box method refers to the process of catalyzing the resin sand at room temperature with a gas or aerosol catalyst to achieve rapid solidification. The cold box method can be divided into amine method, SO 2 - Epoxy method, CO 2 Resin method and methyl formate method. Among them, SO 2 - The core sand prepared by the epoxy resin method can be used for a longer period of time, and solves production problems such as core box fouling and mold sticking, and is suitable for mass production. [0003] The Chinese patent with the application number 201010176020.6 discloses a binder for casting cores. Put 10 g of benzyl ether phenolic resin into the reactor, heat and stir, and dehydrate under vacuum (vacuum degree is 15...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22C1/22
Inventor 唐一林祝建勋许增彬
Owner JINAN SHENGQUAN GRP SHARE HLDG CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com