Preparation method of flocking titanium alloy plate

A titanium alloy and plate technology, which is applied in the field of preparation of flocked titanium alloy plates, achieves the effects of good thermal insulation effect, preventing water droplets from dripping, and long service life

Active Publication Date: 2016-08-17
NANJING UNIV OF AERONAUTICS & ASTRONAUTICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there is a lack of a preparation method for flocking titanium alloy sheets with good thermal insulation effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A preparation method of a flocked titanium alloy plate of the present invention comprises the following steps:

[0023] (1) Surface pretreatment: first, put the clean, unoiled titanium alloy plate with a thickness of 0.18mm and a width of 800mm into the surface treatment machine for surface pretreatment of coating the surface treatment agent. Treatment, the coated board surface treatment agent is RC300 passivator produced by Nippon Paint, the single-side coating speed of the board surface treatment agent is 20m / min, and the single-side coating amount of the board surface treatment agent is 1.0g / m 2 , the temperature of the surface treatment agent when coating is 25°C;

[0024] (2) Drying treatment: After the surface treatment agent is coated, the titanium alloy plate is placed in an oven for drying. The temperature of the oven is 65°C, and the drying time is 10s;

[0025] (3) Glass fiber mesh bonding procedure: After the titanium alloy plate is dried, it enters the gla...

Embodiment 2

[0032] A preparation method of a flocked titanium alloy plate of the present invention comprises the following steps:

[0033] (1) Surface pretreatment: first, put the clean, unoiled titanium alloy plate with a thickness of 0.6mm and a width of 1000mm into the surface treatment machine for surface pretreatment of coating the surface treatment agent. Treatment, the coated board surface treatment agent is RC300 passivator produced by Nippon Paint, the single-sided coating speed of the board surface treatment agent is 15m / min, and the single-sided coating amount of the board surface treatment agent is 0.8g / m 2 , the temperature of the surface treatment agent is 30°C when coating;

[0034] (2) Drying treatment: After the surface treatment agent is applied, the titanium alloy plate is put into a drying furnace for drying. The temperature of the oven is 62° C., and the drying time is 9 s.

[0035] (3) Glass fiber mesh bonding procedure: After the titanium alloy plate is dried, it e...

Embodiment 3

[0041] A preparation method of a flocked titanium alloy plate of the present invention comprises the following steps:

[0042] (1) Surface pretreatment: first, put the clean, unoiled titanium alloy plate with a thickness of 1.2mm and a width of 1250mm into the surface treatment machine for surface pretreatment of coating the surface treatment agent. Treatment, the coated board surface treatment agent is RC300 passivator produced by Nippon, the single-side coating speed of the board surface treatment agent is 22m / min, and the single-side coating amount of the board surface treatment agent is 0.7g / m 2 , the temperature of the board surface treatment agent is 20°C when coating,

[0043] (2) After the plate surface treatment agent is coated, the titanium alloy plate is put into an oven for drying. The temperature of the oven is 70° C., and the drying time is 8 s.

[0044](3) Glass fiber mesh bonding procedure: After the titanium alloy plate is dried, it enters the glass fiber mes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a flocked titanium alloy plate, which comprises the following steps: (1) plate surface pretreatment; (2) drying treatment; (3) glass fiber mesh cloth bonding procedure: (3) fluff Adhesive coating procedure; (5) electrostatic flocking; (6) drying procedure; (7) inspection and storage. The product produced by the method of the invention has weather resistance, corrosion resistance, long service life and good thermal insulation effect.

Description

technical field [0001] The invention relates to the field of building plate processing, in particular to a method for preparing a flocked titanium alloy plate. Background technique [0002] Titanium alloy has many excellent characteristics such as light weight, high strength, strong heat resistance and corrosion resistance. It is known as "the metal of the future" and is a new type of structural material with development prospects. The application of titanium alloy involves many fields, and the application in the aerospace field is the most prominent; [0003] With the rapid development of the national economy, the scale of economic construction and infrastructure construction is rapidly expanding, and buildings are developing in a multi-level and diversified direction. Modern decorative metal building materials, especially roof building materials, are rapidly developing towards lightweight. As the main emerging building materials, titanium alloys are gaining more and more...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D1/14B05D1/04E04D3/16E04D3/30
Inventor 姚正军袁明骆心怡吴小凤杨红勤林玉划
Owner NANJING UNIV OF AERONAUTICS & ASTRONAUTICS