Manufacturing method for porous powder sintered body and preloading molded body for manufacturing sintered body

A technology of pre-compression molding and porous body, which is applied in the field of pre-compression molding, which can solve the problems of difficult control of material pore size, excessive material tortuosity factor, and influence on permeability, etc., and achieve superior corrosion resistance, good corrosion resistance, and excellent The effect of corrosion resistance

Active Publication Date: 2014-12-10
CHENGDU INTERMENT TECH
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the development process of new materials, in addition to the research on material composition, many problems in the process of sintering porosity are

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing method for porous powder sintered body and preloading molded body for manufacturing sintered body
  • Manufacturing method for porous powder sintered body and preloading molded body for manufacturing sintered body
  • Manufacturing method for porous powder sintered body and preloading molded body for manufacturing sintered body

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The preparation methods of the above-mentioned powder sintered Ni-based porous filter alloys of the present invention and the powder sintered Ni-based porous filter alloys obtained by these methods are specifically described below through four sets of experimental examples. Through these descriptions, those skilled in the art can clearly understand the outstanding features of the powder sintered Ni-based porous filter alloy of the present invention. The numbers of the experimental examples mentioned below are the same as the numbers corresponding to the "sample".

[0034]

[0035] See Table 1 for the raw material components and contents (in mass percent) of Experimental Examples 1 to 12 of the first group of experimental examples. Among them, the material use A refers to the prepared powder sintered porous filter alloy for liquid filtration; the material use B refers to the prepared powder sintered porous filter alloy used for gas filtration. In the experimental exam...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a manufacturing method for a porous powder sintered body and a preloading molded body for manufacturing the sintered body. According to the method, the aperture size of the porous powder sintered body can be controlled easily and effectively, and the breakage probability of the molded body during compression molding can be lowered. The method comprises the steps of material preparation, molding and sintering. During material preparation, according to basic raw material powder for manufacturing the porous body, first powder and second powder are used, wherein the first powder and the second powder are different in shape and size, compared with the second powder, the granularity of the first powder is smaller, the compactibility of the first powder during molding is better, and the first powder accounts for 10 percent-90 percent of the total mass of the basic raw material powder. The first powder has the characteristics of being better in compactibility and smaller in sintered aperture size, the second powder has the characteristic of being larger in sintered aperture size, in this way, after the first powder is fully mixed with the second powder, gaps formed in the second powder can be filled with the first powder, on one hand, the effect of controlling the aperture size of the sintered material is achieved, and on the other hand, the compactibility of the mixed powder is improved.

Description

technical field [0001] The invention relates to a method for preparing a powder sintered porous body and a pre-pressed molded body of the sintered body. Background technique [0002] The applicant's current research on powder sintered porous filter materials focuses on the expansion of material application fields, improvement of material performance, exploration of pore-forming mechanism and optimization of preparation process. In the expansion of the application field of sintered porous filter materials, it is boldly proposed to develop corresponding ones that can meet the requirements of chemical stability (such as corrosion resistance) in this application environment and have good filtration performance for some specific and relatively harsh application environments. new material. Its significance is that if this type of new material is successfully developed, it will be able to bring precision filtration technology into the corresponding field, thereby changing the trad...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/11
Inventor 高麟汪涛焦鹏鹤吴磊王韬
Owner CHENGDU INTERMENT TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap