Paper-plastic edge banding with hot-melt adhesive and preparation process for paper-plastic edge banding

A preparation process, paper and plastic sealing technology, applied in furniture accessories, lamination devices, lamination auxiliary operations, etc. Indecent appearance and other problems, to avoid degumming, reduce production processes, and adapt to industrial production and use

Inactive Publication Date: 2014-12-17
DONGGUAN HUALI INDUSTRIES CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, whether it is manual edge banding or edge banding with an automatic edge banding machine, it is necessary to do some complicated preparations before pasting, such as heating and melting of hot melt adhesive, cleaning of edge banding strips, and whole materials; It works in two stages, which will consume more gluing materials, and the amount of gluing materials will not only be large but also uneven. Therefore, not only will overflow glue occur during edge sealing, but at the same time There will also be glue seams at the joint between the glue layer and the board surface, so that it is necessary to clean up the glue overflow after the event, and the glue seams that appear after the edge banding will also cause unsightly appearance of the finished product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Paper-plastic edge banding with hot-melt adhesive and preparation process for paper-plastic edge banding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The preparation process of the paper-plastic edge banding with hot melt adhesive of the present embodiment comprises the following preparation steps:

[0028] a. The base paper is impregnated with water-soluble melamine formaldehyde resin, and then dried at 180° C. to obtain a melamine paper composite material substrate;

[0029] b. printing a decorative layer on the upper surface of the melamine paper composite material substrate with ink;

[0030] c. Coat the protective layer on the upper surface of the decorative layer with UV light-curable paint, and the coating dry solid content of the UV light-curable paint protective layer is 5 g / m 2 , to obtain the paper-plastic edge banding primary product;

[0031] d. Start the heating device of the gluing unit of the gluing machine, heat the gluing unit at 140°C for 15 minutes, then put the finished paper-plastic edging into the gluing unit of the gluing machine for scraping and heating Melt glue, scrape ethylene-vinyl acet...

Embodiment 2

[0034] The preparation process of the paper-plastic edge banding with hot melt adhesive of the present embodiment comprises the following preparation steps:

[0035] a. The base paper is impregnated with water-soluble melamine formaldehyde resin, and then dried at 190° C. to obtain a melamine paper composite material substrate;

[0036] b. printing a decorative layer on the upper surface of the melamine paper composite material substrate with ink;

[0037] c. Coat the protective layer on the upper surface of the decorative layer with UV light-curable paint, and the coating dry solid content of the UV light-curable paint protective layer is 5.5 g / m 2 , to obtain the paper-plastic edge banding primary product;

[0038] d. Start the heating device of the gluing unit of the gluing machine for gluing, heat the gluing unit at 145°C for 18 minutes, then put the finished paper-plastic gluing into the gluing unit of the gluing machine for scraping and heating Melt glue, scrape thermo...

Embodiment 3

[0042] The preparation process of the paper-plastic edge banding with hot melt adhesive of the present embodiment comprises the following preparation steps:

[0043] a. The base paper is impregnated with water-soluble melamine formaldehyde resin, and then dried at 200° C. to obtain a melamine paper composite material substrate;

[0044] b. printing a decorative layer on the upper surface of the melamine paper composite material substrate with ink;

[0045] c. Coat the protective layer on the upper surface of the decorative layer with UV light-curable paint, and the coating dry solid content of the UV light-curable paint protective layer is 6 g / m2 , to obtain the paper-plastic edge banding primary product;

[0046] d. Start the heating device of the gluing unit of the gluing machine, heat the gluing unit at 150°C for 20 minutes, then put the finished paper-plastic edging into the gluing unit of the gluing machine for scraping and heating Melt glue, scrape polyamide hot melt ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of paper-plastic edge bandings with hot-melt adhesives, in particular to a paper-plastic edge banding with a hot-melt adhesive and a preparation process for the paper-plastic edge banding. The paper-plastic edge banding with the hot-melt adhesive sequentially comprises a protective layer, a decorative layer, a paper-plastic substrate layer and a hot-melt adhesive layer from top to bottom, wherein the lower surface of the paper-plastic substrate layer is blade-coated with the hot-melt adhesive layer. According to the paper-plastic edge banding with the hot-melt adhesive, the hot-melt adhesive layer is combined, the paper-plastic substrate layer is adhered to and seamlessly connected with the hot-melt adhesive layer in a molten state, and the adhesion force of the hot-melt adhesive layer with the paper-plastic substrate layer and a product to be banded is high, so that the phenomenon of degumming is avoided; in addition, when the paper-plastic edge banding is used, adhesive overflow, the formation of an adhesive line and preparation work during the sticking of a conventional edge banding can be avoided, the effects of reducing the using amount of the adhesive and avoiding adhesive overflow during sticking, the adhesive line and tedious preparation are achieved, and the quality of a product and the production efficiency are greatly improved; a preparation method is simple, easy, high in production efficiency and applicable to industrial production.

Description

technical field [0001] The invention relates to the technical field of plastic edge banding, in particular to a paper-plastic edge banding with hot melt adhesive and a preparation process thereof. Background technique [0002] Edge banding is a material for protecting, decorating and beautifying the section of furniture panels. Its main function is to seal the section of the panel so as to prevent the panel from being damaged by the environment and unfavorable factors during use. Unique color and texture design and other decorations make the applied furniture panel products more textured and three-dimensional. For edge banding products, gluing treatment is an important process that affects product quality. [0003] At present, in the furniture production process, the adhesive used for bonding the edge strip to the board is mainly hot melt adhesive. The traditional edge banding is co-extruded into one body. In the existing furniture edge banding process, there are two bondi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A47B95/04B32B37/12B32B38/18B32B38/16B32B37/06
Inventor 谢志昆吴锋盘茂森
Owner DONGGUAN HUALI INDUSTRIES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com