Anti-clogging and high-temperature-resisting polyvinyl butyral spray ink

A polyvinyl butyral, high temperature resistant technology, applied in the field of printing ink, to achieve the effect of efficient spraying, easy spraying, and not easy to block

Inactive Publication Date: 2014-12-24
FUYANG ANGU BOILER PRESSURE VESSEL MFG
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in order to improve the performance of the ink, it is necessary to start from improving the performance of these components, and at the same time improve the compatibility between the various raw materials to achieve the effect of synergistic promotion, thereby improving the common problems of ink accumulation, plate drop, and paste version, dirty version, backside sticky and other printing quality problems, in order to improve production efficiency and avoid waste of resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0010] The printing ink prepared in this example is made from the following raw materials by weight: 0.4 of zinc glycerol, 3 of polyoxyethylene lauryl ether, 0.1 of lithium acetate, 8 of magnesium ferrite pigment, 28 of dimethyl carbonate, 3 of phenyl salicylate , stearyl alcohol 2, dehydrated alcohol 12, polyvinyl butyral resin 32, auxiliary 1.2; wherein auxiliary is made of the following raw materials by weight: triethanolamine 0.1, alumina sol 4, ultrafine diatomaceous earth 1. Limonene 2, Absolute ethanol 5, Nano rare earth cerium sol 0.2, the preparation method is as follows: first, triethanolamine and limonene are fully stirred and dissolved in absolute ethanol, then ultra-fine diatomaceous earth is added, and after grinding and mixing for 30 minutes, the obtained The slurry is concentrated and dried, and the obtained powder is then mixed with alumina sol and nano-rare earth cerium sol, and it can be completely stirred and dispersed evenly.

[0011] The preparation metho...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of printing ink and particularly relates to anti-clogging and high-temperature-resisting polyvinyl butyral spray ink. The ink is prepared from the following raw materials in parts by weight: 0.2-0.5 part of glyzinc, 2-5 parts of lauryl alcohol polyoxyethylene, 0.1-0.2 part of lithium acetate, 6-8 parts of a magnesium ferrite pigment, 24-32 parts of dimethyl carbonate, 3-5 parts of phenyl salicylate, 2-3 parts of stearyl alcohol, 8-12 parts of absolute ethyl alcohol, 26-35 parts of polyvinyl butyral resin and 1-2 parts of auxiliaries. The ink takes the polyvinyl butyral resin as an adhering material, is good in softness and flexibility and good in transparency, can resist light and cold, and can be adhered to the surfaces of various kinds of materials well. The lithium acetate and the glyzinc can prevent the ink from crystallizing and improve the heat resistance of coatings, and the auxiliaries can improve the wettability of ink so as to enable the ink to be easily sprayed. The ink has the advantages of low toxicity, environmental friendliness, controllable viscosity and good liquidity, is prevented from color change and falling off in high-temperature environment, is moderate in drying speed, is not easily clogged, and is efficient in spraying.

Description

technical field [0001] The invention relates to the field of printing ink, in particular to an anti-blocking and high-temperature resistant polyvinyl butyral spraying ink. Background technique [0002] Ink is a kind of coloring material that is very commonly used in daily life. It is used as the carrier of text and patterns by printing. It is a kind of viscous colloidal fluid. It is widely used in various printing such as books, packaging and decoration, and architectural decoration. With the increase of social demand, the variety and output of inks have also expanded and increased accordingly. Improving the performance of inks and achieving an energy-saving and efficient production mode is always the inevitable direction of ink development in the future. [0003] The factors that affect the performance of the ink are mainly the properties of the components such as pigments, binders, fillers and additives. For example, pigments affect the durability and tinting strength of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/106C09D11/03
Inventor 傅贵轩陈子育赵志刚刘云飞付丽丽张涛刘长征葛哲骏
Owner FUYANG ANGU BOILER PRESSURE VESSEL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products