Lubricant for metal processing

A metal processing and lubricant technology, applied in the direction of lubricating composition, petroleum industry, etc., can solve the problems of reducing processing efficiency, high heat, and aggravating tool wear, so as to prolong the service life, effectively lubricate and cool, and prevent the blade from curling Effect

Inactive Publication Date: 2014-12-24
QINGDAO TORIX ELECTRONICS TECH
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existence of this friction phenomenon will generate a lot of heat and aggravate the wear of the tool and the deterioration of the surface accuracy of the workpiece, and will reduce the processing efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A lubricant for metal processing is made from the following raw materials in parts by weight:

[0011] 3 parts of polytetrafluoroethylene, 1 part of montmorillonite, 2 parts of dimethyl siloxane, 2 parts of melamine cyanuric acid complex, 2 parts of butyl octanol zinc salt, 3 parts of triethanolamine, sorbitan mono 3 parts of oleic acid ester, 1.5 parts of hydroxypropyl methacrylate, 2.2 parts of ceramic powder, 3 parts of zinc stearate, 3 parts of ethylene oxide.

Embodiment 2

[0013] A lubricant for metal processing is made from the following raw materials in parts by weight:

[0014] 8 parts of polytetrafluoroethylene, 3 parts of montmorillonite, 4 parts of dimethyl siloxane, 7 parts of melamine cyanuric acid complex, 6 parts of butyl octanol zinc salt, 5 parts of triethanolamine, sorbitan mono 7 parts of oleic acid ester, 6 parts of hydroxypropyl methacrylate, 4 parts of ceramic powder, 8 parts of zinc stearate, and 9 parts of ethylene oxide.

Embodiment 3

[0016] A lubricant for metal processing is made from the following raw materials in parts by weight:

[0017] 6 parts of polytetrafluoroethylene, 2 parts of montmorillonite, 3 parts of dimethyl siloxane, 4 parts of melamine cyanuric acid complex, 4 parts of butyl octanol zinc salt, 4 parts of triethanolamine, sorbitan mono 5 parts of oleic acid ester, 4.5 parts of hydroxypropyl methacrylate, 3 parts of ceramic powder, 5 parts of zinc stearate, and 6 parts of ethylene oxide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a lubricant for metal processing. The lubricant is prepared from the following raw materials in parts by weight: 3-8 parts of polytetrafluoroethylene, 1-3 parts of montmorillonite, 2-4 parts of dimethyl siloxane, 2-7 parts of melamine cyanurate complex, 2-6 parts of zinc butanol octanol sulfate, 3-5 parts of triethanolamine, 3-7 parts of sorbitan monooleate, 1.5-6 parts of hydroxypropyl methacrylate, 2.2-4 parts of ceramic powder, 3-8 parts of zinc stearate ester and 3-9 parts of epoxyethane. The lubricant disclosed by the invention has the beneficial effects of effectively lubricating and cooling cutters, preventing phenomena of turned cutter heads and the like and prolonging service lives of cutters.

Description

technical field [0001] The invention relates to a lubricant for metal processing. Background technique [0002] During the machining process, the metal surface is subjected to a large cutting force and has relative motion, which will generate large friction between the tool and the surface of the workpiece, and between the tool and the chips. The existence of this friction phenomenon will generate greater heat and aggravate the wear of the tool and the deterioration of the surface accuracy of the workpiece, and will reduce the processing efficiency. Metalworking fluids can greatly reduce this friction, extending tool life and improving the surface quality of machined parts. Generally speaking, the higher the mineral oil content in the metalworking fluid, the better the lubricating performance of the metalworking fluid, but with the development of metalworking fluid technology, semi-synthetic and fully synthetic metalworking fluids containing extreme pressure additives are a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M169/04C10N40/20
Inventor 刘宏法
Owner QINGDAO TORIX ELECTRONICS TECH