A technology of antibacterial plastics and polyoxyethylene ether, which is applied in the field of antibacterial plastics, can solve the problems of heat resistance, antibacterial, and mildew resistance, which are not very ideal and need to be improved, and achieve the effect of strong heat resistance
Inactive Publication Date: 2015-01-14
常熟市帅红塑料制品厂
View PDF4 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] The current environment-friendly plastics are not very ideal in heat resistance, antibacterial and mildew resistance, and need to be improved
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0048] Antimicrobial plastics, consisting of the following components in parts by weight:
[0049] 55 parts polyvinyl chloride,
[0050] 1.2 parts of phenyl silicone oil,
[0051] 2.3 parts of aniline,
[0052] 1.2 parts of vinyltrimethoxysilane,
[0053] 4.5 parts calcium zinc salt,
[0054] 2.3 parts titanate,
[0055] 1.2 parts glyceryl monostearate,
[0056] 5.6 parts of methyl propylene glycol,
[0057] 1.2 parts of isomeric decanol ethoxylates.
Embodiment 2
[0059] Antimicrobial plastics, consisting of the following components in parts by weight:
[0060] 55 parts polyvinyl chloride,
[0061] 2 parts phenyl silicone oil,
[0062] 3 parts aniline,
[0063] 2 parts vinyltrimethoxysilane,
[0064] 5 parts calcium zinc salt,
[0065] 3 parts titanate,
[0066] 2 parts glyceryl monostearate,
[0067] 6 parts methyl propylene glycol,
[0068] 2 parts isomeric decanol ethoxylates.
Embodiment 3
[0070] Antimicrobial plastics, consisting of the following components in parts by weight:
[0071] 55 parts polyvinyl chloride,
[0072] 1 part phenyl silicone oil,
[0073] 2 parts aniline,
[0074] 1 part vinyltrimethoxysilane,
[0075] 4 parts calcium zinc salt,
[0076] 2 parts titanate,
[0077] 1 part glyceryl monostearate,
[0078] 5 parts methyl propylene glycol,
[0079] 1 part Isodecanol Ethoxylates.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an antibacterial plastic. The antibacterial plastic comprises the following components in parts by weight: 55 parts of polyvinyl chloride, 1-2 parts of phenyl silicone oil, 2-3 parts of phenylamine, 1-2 parts of vinyltrimethoxysilane, 4-5 parts of calcium zinc salt, 2-3 parts of titanate, 1-2 parts of glycerin monostearate, 5-6 parts of methyl propylene glycol and 1-2 parts of isomeric decanol polyoxyethylene ether. The antibacterial plastic disclosed by the invention has the advantages of strong heat resistance and antibacterial and antifungal effects.
Description
technical field [0001] The present invention relates to antibacterial plastics. Background technique [0002] The current environment-friendly plastics are not ideal in terms of heat resistance, antibacterial, and mildew resistance, and need to be improved. Contents of the invention [0003] The object of the present invention is to provide an antibacterial plastic with strong heat resistance and antibacterial and antifungal effects. [0004] In order to achieve the above object, the technical solution of the present invention is to design a kind of antibacterial plastic, which consists of the following components in parts by weight: [0005] 55 parts polyvinyl chloride, [0006] 1 to 2 parts of phenyl silicone oil, [0007] 2 to 3 parts of aniline, [0008] 1-2 parts of vinyltrimethoxysilane, [0009] 4 to 5 parts of calcium zinc salt, [0010] 2 to 3 parts titanate, [0011] 1 to 2 parts of glycerol monostearate, [0012] 5-6 parts of methyl propylene glycol, ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more 
Login to view more